New solar cells with Ag/C60/MAPbI3/Cu2ZnSnSe4 (CZTSe)/Mo/FTO multilayered structures on glass substrates have been prepared and investigated in this study. The electron-transport layer, active photovoltaic layer, and hole-transport layer were made of C60, CH3NH3PbI3 (MAPbI3) perovskite, and CZTSe, respectively. The CZTSe hole-transport layers were deposited by magnetic sputtering, with the various thermal annealing temperatures at 300 °C, 400 °C, and 500 °C, and the film thickness was also varied at 50~300 nm The active photovoltaic MAPbI3 films were prepared using a two-step spin-coating method on the CZTSe hole-transport layers. It has been revealed that the crystalline structure and domain size of the MAPbI3 perovskite films could be substantially improved. Finally, n-type C60 was vacuum-evaporated to be the electronic transport layer. The 50 nm C60 thin film, in conjunction with 100 nm Ag electrode layer, provided adequate electron current transport in the multilayered structures. The solar cell current density-voltage characteristics were evaluated and compared with the thin-film microstructures. The photo-electronic power-conversion efficiency could be improved to 14.2% when the annealing temperature was 500 °C and the film thickness was 200 nm. The thin-film solar cell characteristics of open-circuit voltage, short-circuit current density, fill factor, series-resistance, and Pmax were found to be 1.07 V, 19.69 mA/cm2, 67.39%, 18.5 Ω and 1.42 mW, respectively.
RESUMO
This paper presents new photovoltaic solar cells with Cu2ZnSnSe4/CH3NH3PbI3(MAPbI3)/ZnS/IZO/Ag nanostructures on bi-layer Mo/FTO (fluorine-doped tin oxide) glasssubstrates. The hole-transporting layer, active absorber layer, electron-transporting layer, transparent-conductive oxide layer, and top electrode-metal contact layer, were made of Cu2ZnSnSe4, MAPbI3 perovskite, zincsulfide, indium-doped zinc oxide, and silver, respectively. The active absorber MAPbI3 perovskite film was deposited on Cu2ZnSnSe4 hole-transporting layer that has been annealed at different temperatures. TheseCu2ZnSnSe4 filmsexhibitedthe morphology with increased crystal grain sizesand reduced pinholes, following the increased annealing temperature. When the perovskitefilm thickness was designed at 700 nm, the Cu2ZnSnSe4 hole-transporting layer was 160 nm, and the IZO (indium-zinc oxide) at 100 nm, and annealed at 650 °C, the experimental results showed significant improvements in the solar cell characteristics. The open-circuit voltage was increased to 1.1 V, the short-circuit current was improved to 20.8 mA/cm2, and the device fill factor was elevated to 76.3%. In addition, the device power-conversion efficiency has been improved to 17.4%. The output power Pmax was as good as 1.74 mW and the device series-resistance was 17.1 Ω.