RESUMO
The BIMEVOXes are among the best oxide ion conductors at low and intermediate temperatures. Their high conductivity is associated with local defect structure. In this work, the local structures of two BIMEVOX compositions, Bi2V0.9Ge0.1O5.45 and Bi2V0.95Sn0.05O5.475, are examined using total neutron and X-ray scattering methods, with both compositions exhibiting the ordered α-phase at 25 °C and the disordered γ-phase at 700 °C. While the diffraction data for the α-phase do not allow for the polar (C2) and nonpolar (C2/m) structures to be readily distinguished, measurements of dielectric permittivity suggest the α-phase is weakly ferroelectric in character, consistent with calculations of spontaneous polarization based on a combination of density functional calculations and machine learning methodology. Reverse Monte Carlo (RMC) analysis of total scattering data reveals Ge preferentially adopts tetrahedral geometry at both temperatures, while Sn is found to predominantly adopt octahedral coordination in the α-phase and tetrahedral coordination in the γ-phase. In all cases, V polyhedra are found to consist of tetrahedral, pentacoordinate, and octahedral geometries, as also predicted by the crystallographic analysis and confirmed by 51V solid state NMR spectroscopy. Although similar long-range structures are observed at room temperature, the oxide ion vacancy distributions were found to be quite different between the two studied compositions, with a nonrandom deficiency in vacancy pairs in the second-nearest shell along the ⟨100⟩ tetragonal direction for BIGEVOX10, compared with a long-distance (>8.0 Å) ordering of equatorial vacancies for BISNVOX05. This is attributed to the differences in the preferred coordination geometries of the substituent cations in the two systems. Impedance spectroscopy measurements reveal both compositions show high conductivity in the order of 10-1 S cm-1 at 600 °C.
RESUMO
Formamidinium lead triiodide (FAPbI3 ) is attractive for photovoltaic devices due to its optimal bandgap at around 1.45 eV and improved thermal stability compared with methylammonium-based perovskites. Crystallization of phase-pure α-FAPbI3 conventionally requires high-temperature thermal annealing at 150 °C whilst the obtained α-FAPbI3 is metastable at room temperature. Here, aerosol-assisted crystallization (AAC) is reported, which converts yellow δ-FAPbI3 into black α-FAPbI3 at only 100 °C using precursor solutions containing only lead iodide and formamidinium iodide with no chemical additives. The obtained α-FAPbI3 exhibits remarkably enhanced stability compared to the 150 °C annealed counterparts, in combination with improvements in film crystallinity and photoluminescence yield. Using X-ray diffraction, X-ray scattering, and density functional theory simulation, it is identified that relaxation of residual tensile strains, achieved through the lower annealing temperature and post-crystallization crystal growth during AAC, is the key factor that facilitates the formation of phase-stable α-FAPbI3 . This overcomes the strain-induced lattice expansion that is known to cause the metastability of α-FAPbI3 . Accordingly, pure FAPbI3 p-i-n solar cells are reported, facilitated by the low-temperature (≤100 °C) AAC processing, which demonstrates increases of both power conversion efficiency and operational stability compared to devices fabricated using 150 °C annealed films.
RESUMO
Grain size can have significant effects on the properties of electroceramics for dielectric, piezoelectric, and ferroelectric applications. Here, we systematically investigate the effect of grain size on the structure and properties of Mn-modified 0.67BiFeO3-0.33BaTiO3 ceramics, an important lead-free piezoelectric ceramic that exhibits both a high piezoelectric coefficient and a high Curie point. Ceramics with average grain sizes ranging from 0.46 to 6.85 µm were prepared using conventional and spark plasma sintering. It was found that the morphotropic phase boundary compositions are composed of two polar structures, rhombohedral and tetragonal, with DC poling inducing an increase in the fraction of the rhombohedral phase. All ceramics show relaxor behavior and their freezing temperature moves to higher temperatures with increasing grain size, although their Burns temperature is independent of grain size. In fine-grained ceramics, which show pronounced relaxor behavior, significant grain size dependency is seen in dielectric, piezoelectric, and ferroelectric properties, which is attributed to the presence of single ferroelectric domains and high concentrations of polar nanoregions. In coarse-grained ceramics, a critical grain size of 2.83 µm yields the highest dielectric permittivity at room temperature, with the piezoelectric coefficient plateauing at this grain size, which can be attributed to the contribution of both polar nanoregions and high domain wall density.
RESUMO
Mostra passo a passo como tratar sempre bem o cliente. Baseia-se em uma cuidadosa pesquisa sobre que comportamento e ações resultam em clientes sistematicamente contentes. Conta minuciosamente como tornar esse comportamento e essas ações parte da cultura de sua companhia ou de seu grupo de trabalho, para alcançar vantagem competitiva duradoura. Examina as diferenças entre as duas dimensões da excelência, qualidade de produto e qualidade de serviço, que as empresas precisam alcançar