Sulfur Free Crosslinking of EPDM Composites via Silane Grafting and Silica Incorporation.

This study aims at evaluating and developing an environmental-friendly and sulfur-free cured ethylene propylene diene monomer (EPDM) composites. Silane grafted EPDM (SiEPDM) composites incorporated with silica is prepared via a solvent-free, one-step reactive mixing process. The silane grafting and silica filler bonding are characterized using Fourier transform infrared spectroscopy and X-ray photoelectron spectroscopy. The mechanical properties of the developed composites are examined. The fracture morphology is observed using an environmental scanning electron microscopy. The rheology and thermomechanical properties are evaluated by using a rotational rheometer and dynamic mechanical analyzer. Notably, a robust bonding between silica and the grafted silane is established, yielding a crosslinking network within the composite structure. This phenomenon is substantiated by the observed gel efficiency and rheology behavior. Consequently, a pronounced augmentation of up to 75% in tensile strength and 29% in tear strength are observed in the optimized SiEPDM-silica composites, distinguishing them from their EPDM-silica counterparts. The introduction of paraffin oil contributes to enhanced processability; however, it is concomitant with a reduction in gel efficiency and associated mechanical properties. Furthermore, subsequent UV weathering test unveils that the SiEPDM-silica composites exhibit the highest levels of residual tensile strength and modulus, indicative of their exceptional UV stability.

Effects of erosion and abrasion on resin-matrix ceramic CAD/CAM materials: An in vitro investigation.

The aim of the study was to evaluate the effects of erosion and abrasion on resin-matrix ceramic CAD/CAM materials [CERASMART (GC); VITA ENAMIC (VITA Zahnfabrik); Lava Ultimate (3 M)] in comparison to feldspar ceramic (VITABLOCS Mark II, VITA Zahnfabrik) and resin composite materials (ceram.x universal, Dentsply Sirona). Daily brushing and acid exposure were simulated using a brushing apparatus and a solution of 0.5 vol% citric acid. Microhardness, surface roughness, and substance loss were measured at baseline and after simulation of 1 and 3 years of function. All materials showed a decrease in microhardness after 3 years and an increase in surface roughness (Ra) after 1 and 3 years. The Ra increase was statistically significantly lower for the resin-matrix ceramics than for feldspar ceramic and similar to composite material. After 3 years, only feldspar ceramic showed no significant substance loss. In conclusion, resin-matrix ceramics demonstrate reduced roughening compared to feldspar ceramics, potentially improving restoration longevity by preventing plaque buildup, but differences in abrasion resistance suggest the need for further material-specific research. Future research should aim to replicate clinical conditions closely and to transition to in vivo trials.

Influence of different immediate dentin sealing strategies on bond strength of indirect resin nanoceramic restorations.

In this study, we evaluated the effect of four different strategies for bonding a CAD/CAM resin nanoceramic restoration (Lava Ultimate, 3M) to the dentin surface using a universal adhesive (Scotch Bond Universal, 3M) and adhesive resin cement (RelyX Ultimate, 3M) on the shear bond strength (SBS) and failure mode. The strategies comprised: (i) immediate sealing, immediate bonding; (ii) immediate sealing, bonding after 2 weeks with provisional restoration; (iii) immediate sealing with flowable resin composite reinforcement and bonding after 2 weeks with provisional restoration; and (iv) no immediate sealing, and bonding after 2 weeks with provisional restoration. After bonding, all the specimens were thermocycled, shear tests were performed using a universal testing machine, and failure modes were determined using stereomicroscope and scanning electron microscopy. The highest mean SBS was recorded with immediate sealing, immediate bonding strategy. Most adhesive failures with exposed dentinal tubules were noted in specimens exposed to bonding after 2 weeks with no immediate sealing, which was associated with the lowest SBS. Mixed failures predominated in all immediate dentin sealing groups. Immediate sealing with universal adhesives improves SBS, particularly in the single-visit approach, which has shown significantly better performance, whereas the provisional phase has a negative effect.

Optical effects of graphene addition on adhesives for orthodontic lingual retainers.

The objective of this study was to determine the effects on the colour of adding increasing concentrations of graphene to orthodontic fixed retainer adhesives and to evaluate changes in optical transmission during light curing and the resultant degree of conversion. Two different types of adhesives commonly used for fixed retainers were investigated: A packable composite (Transbond) and a flowable composite (Transbond Supreme). Graphene was added to the adhesives in three different concentrations (0.01, 0.05, and 0.1 wt%). Adhesives without graphene addition were set as control groups. A Minolta colourimeter was used to measure the colour and translucency parameters. Irradiance transmitted during curing was quantified using MARC Light Collector. Fourier-transform infrared spectroscopy was used to record degree of conversion. Data were statistically analysed with the Student's t-test and one-way ANOVA with Tukey's tests (α = 0.05). The findings showed that incorporating graphene darkened the adhesive colour significantly and reduced translucency. As the graphene concentration reached 0.1 wt%, samples became opaque; yet, no adverse effect on degree of conversion was observed. The addition of graphene reduces optical transmission of lingual retainer adhesives; the effect increases with graphene concentration.

Chemical analysis of n-propyl gallate used as pre-treatment for resin-dentin bond strength: In vitro study.

This study aimed to evaluate the effect of n-propyl gallate as pre-treatment for resin-dentin bond strength. The dentin pre-treatments evaluated included propyl gallate of concentrations 0.1% (w/v), 1.0% (w/v), and 10.0% (w/v), as well as glutaraldehyde 5.0% (v/v), and distilled water as a control treatment. Dentin specimens were prepared for Fourier Transformed Infrared Spectroscopy (FT-IR) (n = 3/pre-treatment). Pre-treatments were actively applied to dentin blocks before performing the adhesive procedure to composite resin. Microtensile bond strength to dentin (µTBS) (n = 8/pre-treatment) was determined after 24 h and 6 months of storage. Data were submitted to a two-way ANOVA, followed by Tukey's post hoc test. As for FT-IR, propyl gallate 1%-treated specimens presented higher water, carbonate, collagen, and amide absorbance rates compared to other tested groups, while specimens pre-treated with glutaraldehyde and distilled water presented similar absorbance curves. Regarding µTBS, all concentrations of propyl gallate resulted in statistically significant higher bond strength values than distilled water at 24 h. After 6 months of storage, propyl gallate 0.1% was the only group that maintained µTBS over time. Propyl gallate 0.1% might be a suitable dentinal pre-treatment due to being able to present chemical bonds with demineralized dentin and providing resin-dentin bond stability after 6 months of storage.

Effects of alpha-tocopherol antioxidant on fracture strength and adhesion of endodontically treated teeth restored after dental bleaching.

This study evaluated the effect of different concentrations of alpha-tocopherol in gel form on fracture strength, hybrid layer formation, and microtensile bond strength of endodontically treated teeth bleached with 40% hydrogen peroxide (H2 O2 ). Sixty bovine incisors were randomized into one of six groups (n = 10 incisors per group) defined by the interventions carried out after endodontic treatment. In the control group, no additional intervention was carried out, while all teeth in the five intervention groups were bleached with 40% H2 O2 and subsequently treated with alpha-tocopherol at concentrations of 15% (15AT), 20% (20AT), or 25% (25AT), with 10% sodium ascorbate (10SA), or with nothing (40HP). Fracture strength was evaluated in a mechanical testing machine, hybrid layer formation was assessed using scanning electron microscopy, and bond strength was determined using microtensile bond-strength testing. Data were analyzed using Kruskal-Wallis and Dunn's tests. No statistically significant difference regarding fracture strength was observed among groups. Hybrid layer formation was greater in the 15AT group than in groups 40HP and 10SA. Teeth in groups 15AT, 20AT, and 25AT demonstrated higher bond strength than teeth in groups 40HP and 10SA. Alpha-tocopherol, preferably at 15%, effectively reverses the deleterious effects, of bleaching, on hybrid layer formation and bond strength to dentin.

Shear Bond Strength of Adhesives Placed following Selective Removal of Red-Fluorescing Carious Dentine in vitro.

Red-fluorescing dentine indicates bacterial contamination [Caries Res 2002; 36: 315-319]. We investigated effect of removal of red fluorescent dentine caries on shear bond strength and fracture mode of 4 adhesive approaches. Sixty-five carious teeth and 50 noncarious controls were distributed into 4 groups: Clearfil™ self-etch (CSE), OptiBond™ FL total etch (OTE), Scotchbond™ Universal total etch (STE) and self-etch (SSE). Samples were excited at 405 nm and viewed through 530 nm filter. Carious samples were ground flat exposing strongly red-fluorescing (StrongRF) dentine, on which a composite cylinder was placed, using one of 4 adhesives. After 22 h in water, shear bond strength and fracture mode were analysed. StrongRF was removed; composite cylinders were placed on weakly red-fluorescing (WeakRF) dentine and tested as described above. Finally, red-fluorescing dentine was removed, and composite cylinders were placed on non-fluorescing (NonRF) dentine and tested. Composites were placed at 3 corresponding heights in controls. After 22 h in water, shear bond strength testing and fracture mode analysis were performed. Differences were tested using Mann-Whitney or Wilcoxon tests (p ≤0.05). Median (Q1, Q3) shear bond strength on StrongRF was SSE 14.4 (9.2, 18.2) MPa >CSE 10.2 (6.4, 17.3) MPa >STE 9.1 (6.9, 11.2) MPa >OTE 6.8 (4.0, 10.8) MPa. Shear bond strength increased statistically significantly for all adhesives on WeakRF: SSE 19.8 (13.6, 24.3) MPa >STE 19.5 (12.7, 23.1) MPa >CSE 17.5 (12.0, 22.5) MPa >OTE 15.8 (11.9, 20.9) MPa. Only STE 25.6 (22.4, 29.1) MPa and CSE 22.1 (17.6, 24.6) MPa were significantly different on NonRF compared to WeakRF. For controls tested at corresponding depths, superficial shear bond strength was OTE 18.7 (16.0, 22.1) MPa >STE 18.4 (12.0, 25.9) MPa >CSE 18.1 (12.7, 20.7) MPa >SSE 13.0 (9.6, 17.8) MPa. This was significantly higher compared to StrongRF except for SSE. Central shear bond strength was not significantly different to WeakRF, deep shear bond strength was significantly lower for SSE and CSE but higher for OTE compared to carious. Conclusion: StrongRF dentine should be removed for higher shear bond strength, but WeakRF dentine can often be preserved without compromising adhesive bond strength.

Blue Laser for Polymerization of Bulk Fill Composites: Influence on dentin bond strength and temperature rise during curing and co-curing method.

Blue diode lasers are alternative curing devices for dental composites. The aim of this study was to investigate the influence of blue diode laser polymerization on shear bond strength of bulk fill composites to human dentin and temperature rise during two types of polymerization. Composite cylinders of SDR Plus(SDR) and Ever X Flow(EX) were bonded to dentin slabs using Adhese Universal and curing devices blue diode laser (449 nm, 1.6 W) and Power Cure LED. For each material and curing device there were two polymerization approaches: 1)conventional: separate curing of adhesive; 2)co-curing: simultaneous adhesive and composite curing. Polymerization modes for each material in conventional and co-curing(c) approach were: blue laser 2000 mW/cm2 for 5 s (L5 and L5c); blue laser 1000 mW/cm2 for 10 s (L10 and L10c); Power Cure 2000 mW/cm2 for 5 s (LED5 and LED5c); Power Cure 1000 mW/cm2 for 10 s (LED10 and LED10c). Temeperature was measured using thermal vision camera. For SDR, the highest bond strength was 24.3 MPa in L10c, and the lowest 9.2 MPa in LED5c. EX exhibited the highest bond strength(21.3 MPa) in LED5, and the lowest in L5(7.7 MPa). The highest temperature rise for SDR was in L10 and L5 (7.3 and 7.2 °C), and the lowest in LED5(0.8 °C). For EX, the highest temperature rise was in L5 (13.0 °C), and the lowest in LED5 (0.7 °C). Temperature rise was higher during blue laser polymerization, especially at high intensity and with conventional curing. Preferable blue laser curing mode is co-curing at 1000mW/cm2 for 10 s.

Longevity of composite restorations in posterior teeth placed by dental students: a 12-year retrospective study.

OBJECTIVES: To evaluate the longevity of resin composite restorations placed in posterior teeth by dental students, using data from electronic records from 2008 to 2019. MATERIALS AND METHODS: Demographic (gender and age) and clinical variables (dental group, position in dental arch, and the number of restored surfaces) were evaluated. The 5-year follow-up was assessed according to the day the restoration was placed. Kaplan-Meier curves were generated to calculate the annual failure rate. Data were analyzed by Chi-Square, Kruskal-Wallis, and Mann-Whitney tests (α = 0.05). RESULTS: In total, 3.883 records relative to return periodicity were analyzed. The final sample consisted of 900 restorations from 479 patients. The majority were females, aged between 31 and 60. In total, 256 failures were reported (success rate = 78%), showing an annual failure rate of 2.05%. The main reasons for failures were restoration replacement (55.5%), endodontics (21.9%), prosthetics (14.5%) and extraction (8.2%). There was a higher risk of failure in restorations involving three or more surfaces (p = 0.000) and in patients over 60 years (p < 0.001). In females (p = 0.030), molars (p = 0.044), and maxillary teeth (p = 0.038) failed in a shorter time. CONCLUSIONS: Resin composite restorations placed in permanent posterior teeth by dental students had high survival rates. The main reason for failure was the replacement of restorations. The age group and the number of restored surfaces significantly affected the success of the restorations. CLINICAL RELEVANCE: The electronic health records over 12 years showed that 78% of the resin restorations in posterior teeth placed by dental students were successful for a minimum of five years.

Two-year clinical performance of dual- and light-cure bulk-fill resin composites in Class ӀӀ restorations: a randomized clinical trial.

OBJECTIVE: This study aimed to compare the clinical performance of dual- and light-cure bulk-fill resin composites (BFRCs) in Class ӀӀ restorations after 2 years. MATERIALS AND METHODS: A double-blinded, prospective, randomized clinical trial (RCT) was conducted following the CONSORT (Consolidated Standard of Reporting Trials) guidelines. Forty patients were enrolled in the study. Each patient received three compound Class ӀӀ restorations. One dual-cure (Fill-Up; Coltene Waledent AG) and two light-cure (QuiXfil; Dentsply, and Tetric N-Ceram Bulk Fill; Ivoclar Vivadent) BFRCs were used for 120 Class ӀӀ restorations. A universal adhesive (ONE COAT 7 UNIVERSAL; Coltene Waledent AG) was used with all restorations. Restorations were clinically evaluated after 1 week (baseline), 6 months, 12 months, 18 months, and finally after 24 months using the FDI World Dental Federation (FDI) criteria. The Kruskal-Wallis test was used for comparison between BFRCs groups at baseline and at each recall period, and the Wilcoxon signed-rank test was used for comparing different follow-up times of each BFRC to baseline. The level of significance was set at p < 0.05. RESULTS: All BFRCs restorations showed only minor changes and revealed no statistically significant differences between their clinical performance for all evaluated parameters at all recall periods; also, there was no statistically significant difference between all recall periods and baseline for all evaluated parameters. CONCLUSION: The two-year clinical performance of dual-cure BFRC was comparable to light-cure BFRCs in Class ӀӀ restorations. CLINICAL RELEVANCE: Dual- and light-cure BFRCs showed excellent clinical performance in Class ӀӀ restorations after a 2-year clinical follow-up.

Bonding performance and interfacial adaptation of modern bulk-fill restorative composites after aging in artificial saliva: an in vitro study.

OBJECTIVES: This study aimed at comparing the microtensile bond strength (MTBS) and interfacial adaptation of a modern self-curing and a light-curing restorative bulk-fill composite to a conventional composite applied with the layering technique. METHODS: Forty-eight occlusal cavities were divided in three main groups (16/group) based on tested materials: (i) STELA, bulk-fill self-curing restorative (STELA, SDI Ltd.); (ii) 3 M-BULK, bulk-fill composite (Filtek One Bulk-Fill, 3 M Oral Care); and (iii) 3 M-CTR, a conventional composite (Filtek Supreme XTE, 3 M Oral Care). These were used in combination with their adhesives in self-etch (SE) or etch-and-rinse (ER) mode. Specimens stored in artificial saliva (24 h or 12 months) were evaluated for MTBS and fractography. The interfacial analysis was performed through confocal microscopy. ANOVA and Fisher's LSD post hoc tests were performed with a level of significance of 5%. RESULTS: All the tested materials applied in ER mode presented (24 h) greater bond strength than in SE mode. Although all materials showed a significant drop in the bond strength after prolonged storage, STELA showed the highest bonding performance and interfaces with few gaps. 3 M-BULK had the lowest bond strength and an interface with several voids and gaps. CONCLUSIONS: All materials were affected by interface degradation and bonding reduction over prolonged aging. However, their use in combination with adhesives applied in ER mode may offer greater immediate bonding performance. CLINICAL RELEVANCE: The use of restorative light-curing bulk-fill composites may generate gaps at the bonding interface and voids. STELA may represent a suitable alternative to avoid such issues.

Sixty-month comperative evaluation of a glass hybrid restorative and a composite resin in non-carious cervical lesions of bruxist individuals.

OBJECTIVE: To compare the clinical performance of a glass hybrid (GH) restorative and a nano-ceramic composite resin (CR) in the restoration of non-carious cervical lesions (NCCLs) of bruxist individuals in a 60-month randomized clinical trial. MATERIALS AND METHODS: Twenty-five bruxist candidates having NCCLs were recruited in this clinical study. The depth, height (cervico-incisal), width (mesio-distal), internal angles of the NCCLs, degree of tooth wear (TWI) and gingival index (GI) were measured. One hundred-and-forty-eight NCCLs were restored either with a GH restorative (Equia Forte Fil) or a CR (Ceram.X One Universal). Modified USPHS criteria was used to evaluate restorations after 1 week and 12, 24, 36 and 60 months. Pearson's Chi-Square, Fisher's Exact and Cochran Q tests were run for analysis. Survival rates of the restorations were compared with Kaplan-Meier analysis (p < 0.05). RESULTS: After 60 months, 97 restorations in 15 patients were examined. The recall rate was 60.0%. Retention rates were 73.5% for CR and 66.7% for GH. A total of 29 restorations were lost (13CR (26.5%), 16GH (33.3%)). There was not a significant difference between tested restoratives in retention (p = 0.464), marginal adaptation (p = 0.856) and marginal discoloration (p = 0.273). There was no relationship between internal angle, depth, height or width and retention of the GH or CR restorations (p > 0.05). The increase in retention loss and marginal discoloration of both restorations over time were significant (p < 0.001). Sensitivity or secondary caries were not detected after 60 months. CONCLUSION: GH and nano-ceramic CR showed similar clinical performances in NCCLs after 60 months in patients with bruxism. CLINICAL SIGNIFICANCE: After 60 months, CR and GH materials showed clinically acceptable performances in restoration of NCCLs in patients with bruxism.

Effect of fiber-reinforced direct restorative materials on the fracture resistance of endodontically treated mandibular molars restored with a conservative endodontic cavity design.

OBJECTIVE: This study aimed to evaluate the fracture strength of teeth restored using fiber-reinforced direct restorative materials after endodontic treatment with a conservative mesio-occlusal access cavity design. MATERIALS AND METHODS: A total of 100 extracted intact mandibular first molars were selected and distributed into a positive control group where teeth left intact and the following four test groups comprised of teeth with conservative mesio-occlusal access cavities that had undergone root canal treatment (n = 20/group): access cavity without restoration (negative control), bulk-fill resin composite with horizontal glass fiber post reinforcement, fiber-reinforced composite with bulk-fill resin and bulk-fill resin composite. Following thermocycling (10,000 cycles), fracture resistance was measured using a universal testing machine. Statistical analyses (one-way analysis of variance and the Tamhane test) were performed, and statistical significance was set at p < 0.05. RESULTS: Groups with minimally invasive access cavities had lower fracture strength than intact teeth, regardless of the restoration material (p < 0.05). Fiber-reinforced composite groups demonstrated higher fracture strength than bulk-fill resin composite alone (p < 0.05). Fracture types varied among groups, with restorable fractures predominant in the fiber-reinforced composite groups. CONCLUSION: This study suggests that using fiber-reinforced composite materials, especially in combination with bulk-fill resin composites, can effectively enhance the fracture strength of endodontically treated teeth with conservative access cavities. However, using only bulk-fill resin composite is not recommended based on the fracture strength results. CLINICAL SIGNIFICANCE: When teeth that undergo endodontic treatment are restored using a conservative access cavity design and fiber-reinforced composite materials, especially in combination with bulk-fill resin composites, the fracture strength of the teeth can be effectively increased.

In-vitro evaluation of fracture resistance of teeth restored with different high-viscosity glass ionomer restorative materials and bulk-fill composite resins.

OBJECTIVES: This study aimed to evaluate the effect of restorations made with a glass-hybrid restorative system (GHRS), a high-viscosity glass ionomer restorative material (HVGIC), a high-viscosity bulk-fill composite resin (HVB), a flowable bulk-fill composite resin (FB), and a nanohybrid composite resin (NH), which are commonly preferred in clinical applications on the fracture resistance of teeth in-vitro. MATERIALS AND METHODS: One hundred intact human premolar teeth were included in the study. The teeth were randomly divided into ten groups (n = 10). No treatment was applied to the teeth in Control group. Class II cavities were prepared on the mesial surfaces of the remaining ninety teeth in other groups. For restoration of the teeth, a GHRS, a HVGIC, a HVB, a FB, and a NH were used. Additionally, in four groups, teeth were restored using NH, GHRS, and HVGIC with open and closed-sandwich techniques. After 24 h, fracture resistance testing was performed. One-way ANOVA and Tukey HDS tests were used for statistical analysis of the data. RESULTS: The fracture resistance values of Control group were statistically significantly higher than those of GHRS, HVGIC, FB, NH, HVGIC-CS, GHRS-OS, and HVGIC-OS groups(p < 0.05). There was no statistically significant difference observed between the fracture resistance values of Control, HVB, and GHRS-CS groups (p > 0.05). CONCLUSION: It can be concluded that the use of HVB and the application of GHRS with a closed-sandwich technique may have a positive effect on the fracture resistance of teeth in the restoration of wide Class II cavities. CLINICAL RELEVANCE: The use of high-viscosity bulk-fill composite resin and the application of glass-hybrid restorative system with the closed-sandwich technique in the restoration of teeth with wide Class II cavities could increase the fracture resistance of the teeth.

Marginal integrity of prototype bioactive glass-doped resin composites in class II cavities.

OBJECTIVES: This in vitro study examined the marginal integrity of experimental composite materials doped with bioactive glass (BG). MATERIALS AND METHODS: Class-II MOD cavities were prepared and restored with one of the following composite materials: a commercial composite material as a reference (Filtek Supreme XTE), an experimental composite doped with BG 45S5 (C-20), and an experimental composite doped with a fluoride-containing BG (F-20). Six experimental groups (n = 8) were used, as each of the three composites was applied with (+) or without (-) a universal adhesive (Adper Scotchbond Multipurpose). All specimens were subjected to thermocycling (10,000 x, 5-55 °C) and then additionally stored in artificial saliva for eight weeks. Scanning electron micrographs of the mesial and the distal box were taken at three time points (initial, after thermocycling, and after eight weeks of storage in artificial saliva). The margins were classified as "continuous" and "non-continuous" and the percentage of continuous margins (PCM) was statistically analyzed (α = 0.05). RESULTS: In most experimental groups, thermocycling led to a significant decrease in PCM, while the additional 8-week aging had no significant effect. F-20 + performed significantly better (p = 0.005) after 8 weeks storage in artificial saliva than the reference material with adhesive, while no statistically significant differences were observed at the other two time points. C-20 + exhibited significantly better PCM than the reference material with adhesive after thermocycling (p = 0.026) and after 8 weeks (p = 0.003). CONCLUSIONS: Overall, the experimental composites with BG showed at least as good marginal adaptation as the commercial reference, with an indication of possible re-sealing of marginal gaps. CLINICAL RELEVANCE: Maintaining or improving the marginal integrity of composite restorations is important to prevent microleakage and its likely consequences such as pulp irritation and secondary caries.

Fracture resistance of CAD/CAM endocrowns made from different materials in maxillary premolar interproximal defects.

OBJECTIVES: This in vitro study aims to compare the fracture resistance of three CAD/CAM materials used in endocrown restoration of interproximal defects in maxillary premolars. MATERIALS AND METHODS: 45 maxillary premolars extracted as part of orthodontic treatment were included. Following standardized root canal treatment, all teeth were prepared into Mesial-Occlusal (MO) cavity types. The samples were then randomly divided into three groups: LD [repaired with lithium disilicate glass ceramics (IPS e.max CAD)], VE [treated with polymer-infiltrated ceramics (Vita Enamic)], and LU [repaired with resin-based nanoceramics (Lava Ultimate)]. Axial static loading was applied using a universal testing machine at 1 mm/min until fracture, and fracture resistance and failure modes were recorded. RESULTS: Regarding Fracture Resistance Values (FRVs), the LD group exhibited significantly higher values than the other two groups, VE (P = 0.028) and LU (P = 0.005), which showed no significant difference (P = 0.778). On the other hand, regarding failure modes, the LD group had a higher prevalence of irreparable fractures compared to the other two groups, VE (P < 0.001) and LU (P < 0.001), which showed no significant difference. CONCLUSIONS: Although lithium disilicate glass ceramics exhibited higher FRVs, they had a lower repair probability. In contrast, polymer-infiltrated ceramics and resin-based nanoceramics contributed to tooth structure preservation. CLINICAL RELEVANCE: For maxillary premolars with interproximal defects following root canal treatment, resin ceramic composites are recommended for restoration to enhance abutment teeth protection.

Clinical performance of a glass-hybrid system in comparison with a resin composite in two-surface class II restorations: a 5-year randomised multi-centre study.

OBJECTIVE: To evaluate the 5-year clinical performance of a glass hybrid restorative system and a nano-hybrid resin composite in moderate to large two-surface class II cavities. MATERIALS AND METHODS: This study was carried out by dental schools in Zagreb, Croatia; Izmir, Turkey; Belgrade, Serbia; and Milan, Italy. A total of 180 patients requiring two class-II two-surface restorations in the molars of the same jaw were recruited. The teeth were randomly restored with either a nano-hybrid resin composite (Tetric EvoCeram, Ivoclar Vivadent) or a glass-hybrid material (EQUIA Forte, GC). During the 5-year follow-up, two calibrated evaluators at each centre scored the restorations annually using the FDI-2 scoring system. The survival rates were calculated using the Kaplan-Meier method and compared using non-parametric matched pair tests (p < 0.05). RESULTS: There were no statistically significant differences between the overall survival and success rates of the two types of restorations (p>0.05). The success rates (FDI-2 scores 1-3) for EQUIA Forte were 81.9% (average annual failure rate: 3.9%) and 90.7% for Tetric EvoCeram (average annual failure rate: 1.9%). The survival rates (FDI-2 scores 1-4) for EQUIA Forte and Tetric EvoCeram were 94.5% and 94.4%, respectively, with an average annual failure rate of 1.1%. CONCLUSIONS: In terms of success and survival rates, both the glass-hybrid restorative system and the nano-hybrid resin composite have been shown to perform satisfactorily. CLINICAL RELEVANCE: The results of this study indicate that EQUIA Forte can be one of the therapeutic options for moderate to large two-surface class II restorations of posterior teeth.

Two-year evaluation of a nano-hybrid and a bulk-fill resin composite: a randomized, double-blind split-mouth clinical study.

OBJECTIVES: The aim of this study was to compare the 2-year clinical performance of a bulk-fill composite resin and a nano-hybrid-filled composite resin in 6-12-year-old children in a split-mouth design. MATERIALS AND METHODS: This randomized, split-mouth, and double-blind study was conducted on 89 patients aged 6-12 years with caries on bilateral mandibular first molars. In a split-mouth design, restorations of mandibular permanent molars were completed with nano-hybrid organically modified ceramic (ORMOCER)-based bulk-fill composite resin Admira Fusion x-tra (Voco GmbH, Cuxhaven, Germany) and nano-hybrid composite Grandio (Voco, Cuxhaven, Germany). Futurabond U single dose (Voco, Cuxhaven, Germany) was used with selective enamel etching. The clinical success of the restorations was evaluated using USPHS and FDI criteria at 6, 12, and 24-month follow-up controls. RESULTS: In the 2-year follow-up, all restorations were clinically acceptable. Grandio was significantly worse than Admira Fusion x-tra in terms of surface luster and superficial change (p < 0.05). Surface staining and color match scores increased in Admira Fusion x-tra compared with Grandio significantly (p < 0.05). CONCLUSIONS: Although both materials showed acceptable clinical performance over 2 years, a significant difference was observed between the surface luster, surface staining, marginal adaptation, and staining of the nano-hybrid composite placed with the incremental technique and the bulk-fill ORMOCER-based composite resin. CLINICAL RELEVANCE: As an alternative to nano-hybrid composite resins, using bulk-fill restorative materials, which can be indicated in the proper case, may contribute to shortening treatment procedures and increasing patient and physician comfort, leading to clinical success.

Repair of monolithic zirconia restorations with different direct resin composites: effect on the fatigue bonding and mechanical performance.

OBJECTIVE: The study aims to evaluate the shear bond and flexural strength fatigue behavior of yttrium-stabilized zirconia (4YSZ) repaired using different resin composites. MATERIALS AND METHODS: Cylindric specimens of 4YSZ were obtained for the bond strength (Ø = 6 mm, 1.5 mm of thickness) and biaxial flexural strength (Ø = 15 mm, 1 mm of thickness) fatigue tests and divided into 3 groups according to the repair resin composite: EVO (nanohybrid), BULK (bulk-fill), and FLOW (flowable). The zirconia surface was air-abraded with alumina particles, a 10-methacryloyloxydecyl dihydrogen phosphate (10-MDP) primer was applied, and the resin composite was build-up over the zirconia. Fatigue shear bond strength and flexural fatigue strength tests were performed (n = 15). One-way ANOVA and Tukey post hoc tests were carried out for both outcomes, besides scanning electron microscopy and finite element analysis. RESULTS: The repair material affected the fatigue shear bond strength of zirconia ceramic. The BULK group (18.9 MPa) depicted higher bond strength values than FLOW (14.8 MPa) (p = 0.04), while EVO (18.0 MPa) showed similar results to both groups. No effect was observed for the mechanical behavior (p = 0.53). The stress distribution was similar for all groups. CONCLUSION: The repair of yttrium-stabilized zirconia (4YSZ) ceramics with bulk-fill resin composites was the best option for high fatigue bond strength. However, the fatigue mechanical performance was similar regardless of the applied repair material. CLINICAL RELEVANCE: The repair of yttrium-stabilized zirconia (4YSZ) monolithic restorations may be performed with nanohybrid and bulk-fill resin composites in order to promote longevity in the treatment.

Mechanical properties of ion-releasing restorative materials.

PURPOSE: To evaluate and compare the laboratory compressive strength (CS), flexural strength (FS), and diametral tensile strength (DTS) of Cention Forte and three bulk fill restorative materials. METHODS: A total of 168 specimens were prepared following the manufacturers' instructions and standards for testing CS, FS, and DTS. Mechanical properties of Cention Forte (LC-Cent) were compared to three commercial bulk-fill materials for posterior restorations: Fuji IX Extra (Fuji), Tetric PowerFill (TPF), and Equia Forte HT (Equia). The tests were performed 24 hours after storage in distilled water on a universal testing machine at a crosshead speed of 0.75 mm/minute. Strength values (MPa) were calculated and statistically analyzed by one-way ANOVA and Tukey's post hoc test (P< 0.05). RESULTS: Analysis showed significant differences between tested materials for CS, FS, and DTS (P= 0.0001). LC-Cent showed the highest mean value for FS (112.8 MPa) with a significant difference compared to Fuji and Equia. DTS (49.2 MPa) of LC-Cent was significantly higher than all tested materials. TPF showed the highest mean value (180 MPa) for CS but without significant difference compared to LC-Cent. CLINICAL SIGNIFICANCE: Ion-releasing material Cention Forte, according to obtained results, may serve as a viable alternative for posterior restorations compared to conventional bulk-fill restorative materials.