RESUMEN
Biopolymer-based composition with adding of conductive polymer poly-(3,4-ethylenedioxythiophene) polystyrenesulfonate (PEDOT PSS) was made by mixing of iota-carrageenan (CRG), polyvinyl alcohol (PVA) and PEDOT PSS followed by freezing/thawing cycles. The method is environmentally friendly and based on the formation of polymer matrix upon of mixing CRG, PVA and PEDOT PSS and formation of porous physical gel due to freezing/thawing cycles. It is necessary to mention that all components are well-known as biocompatible materials. The resulting material is stable in water and also has swelling capability both in distilled water and physiological solutions. Structure of material was characterized by means of X-ray diffraction, optical and electron microscopy. Electrophysical investigations also were performed. The conductivity of the gel immersed in distilled water is comparable with the dry gel value and close to 0.01 [S/cm].
RESUMEN
The effects of coagulant (FeCl3·6H2O), various flocculants based on polyacrylamide (PAA), polyethylenoxide (PEO) and flocculated biomass as ballast agent, dosage and sedimental time on flocculation efficiency of harvesting Chlorella vulgaris GKV1 cultivated in a laboratory were investigated. The results of this work indicated that the flocculation efficiency achieved about 90% after 5 min of sedimentation when adding of coagulant and flocculant mixture (FeCl3 50 mg/l+PEO based Sibfloc-718 7.5 mg/l) or flocculant with ballast agent (Sibfloc-718 7.5 mg/l+10% flocculated biomass). PAA and PEO showed good flocculation efficiency at dosage of 0.025 and 0.015 g/l, respectively without pH adjustment. Finally, the most suitable flocculation method was discussed in this paper.