RESUMEN
The powder metallurgy method was used to manufacture three Ti-based alloys: Ti-15%Zr-2%Ta-4%Sn (Ti-Zr-Ta-4Sn), Ti-15%Zr-2%Ta-6%Sn (Ti-Zr-Ta-6Sn), and Ti-15%Zr-2%Ta-8%Sn (Ti-Zr-Ta-8Sn). Electrochemical measurements and surface analyses were used to determine the effect of Sn concentration on the corrosion of these alloys after exposure to a simulated body fluid (SBF) solution for 1 h and 72 h. It was found that the passivation of the alloy surface significantly increased when the Sn content increased from 4% to 6% and then to 8%, which led to a significant reduction in corrosion. The impedance spectra derived from the Nyquist graphs also explained how the addition of Sn significantly improved the alloys' polarization resistances. According to the change in the chronoamperometric current at an applied anodic potential over time, the increase in Sn content within the alloy significantly reduced the currents over time, indicating that the uniform and pitting corrosion were greatly decreased. The formation of an oxide layer (TiO2), which was demonstrated by the surface morphology of the alloys after exposure to SBF solution for 72 h and corrosion at 400 mV (Ag/AgCl) for 60 min, was supported by the profile analysis obtained by an X-ray spectroscopy analyzer. It was clear from all of the findings that the tested alloys have a remarkable improvement in resistance to corrosivity when the Sn content was increased to 8%.
RESUMEN
Very often, pure Ti and (α + ß) Ti-6Al-4V alloys have been used commercially for implant applications, but ensuring their chemical, mechanical, and biological biocompatibility is always a serious concern for sustaining the long-term efficacy of implants. Therefore, there has always been a great quest to explore new biomedical alloying systems that can offer substantial beneficial effects in tailoring a balance between the mechanical properties and biocompatibility of implantable medical devices. With a view to the mechanical performance, this study focused on designing a Ti-15Zr-2Ta-xSn (where x = 4, 6, 8) alloying system with high strength and low Young's modulus prepared by a powder metallurgy method. The experimental results showed that mechanical alloying, followed by spark plasma sintering, produced a fully consolidated (α + ß) Ti-Zr-Ta-Sn-based alloy with a fine grain size and a relative density greater than 99%. Nevertheless, the shape, size, and distribution of α-phase precipitations were found to be sensitive to Sn contents. The addition of Sn also increased the α/ß transus temperature of the alloy. For example, as the Sn content was increased from 4 wt.% to 8 wt.%, the ß grains transformed into diverse morphological characteristics, namely, a thin-grain-boundary α phase (αGB), lamellar α colonies, and acicular αs precipitates and very low residual porosity during subsequent cooling after the spark plasma sintering procedure, which is consistent with the relative density results. Among the prepared alloys, Ti-15Zr-2Ta-8Sn exhibited the highest hardness (s340 HV), compressive yield strength (~1056 MPa), and maximum compressive strength (~1470). The formation of intriguing precipitate-matrix interfaces (α/ß) acting as dislocation barriers is proposed to be the main reason for the high strength of the Ti-15Zr-2Ta-8Sn alloy. Finally, based on mechanical and structural properties, it is envisaged that our developed alloys will be promising for indwelling implant applications.
RESUMEN
Ti-15%Zr alloy and Ti-15%Zr-2%Ta alloy were fabricated to be used in biomedical applications. The corrosion of these two alloys after being immersed in simulated body fluid for 1 h and 72 h was investigated. Different electrochemical methods, including polarization, impedance, and chronoamperometric current with time at 400 mV were employed. Also, the surface morphology and the compositions of its formed film were reported by the use of scanning electron microscope and energy dispersive X-ray. Based on the collected results, the presence of 2%Ta in the Ti-Zr alloy passivated its corrosion by minimizing its corrosion rate. The polarization curves revealed that adding Ta within the alloy increases the corrosion resistance as was confirmed by the impedance spectroscopy and current time data. The change of current versus time proved that the addition of Ta reduces the absolute current even at high anodic potential, 400 mV. The results of both electrochemical and spectroscopic methods indicated that pitting corrosion does not occur for both Ti-Zr and Ti-Zr-Ta alloys, even after their immersion in SBF solutions for 72 h.