Hydrogen Production by Steam Reforming of Ethanol and Dry Reforming of Methane with CO2 on Ni/Vermiculite: Stability Improvement via Acid or Base Treatment of the Support.

In this study, vermiculite was explored as a support material for nickel catalysts in two key processes in syngas production: dry reforming of methane with CO2 and steam reforming of ethanol. The vermiculite underwent acid or base treatment, followed by the preparation of Ni catalysts through incipient wetness impregnation. Characterization was conducted using various techniques, including X-ray diffraction (XRD), SEM-EDS, FTIR, and temperature-programmed reduction (H2-TPR). TG-TD analyses were performed to assess the formation of carbon deposits on spent catalysts. The Ni-based catalysts were used in reaction tests without a reduction pre-treatment. Initially, raw vermiculite-supported nickel showed limited catalytic activity in the dry reforming of methane. After acid (Ni/VTA) or base (Ni/VTB) treatment, vermiculite proved to be an effective support for nickel catalysts that displayed outstanding performance, achieving high methane conversion and hydrogen yield. The acidic treatment improved the reduction of nickel species and reduced carbon deposition, outperforming the Ni over alkali treated support. The prepared catalysts were also evaluated in ethanol steam reforming under various conditions including temperature, water/ethanol ratio, and space velocity, with acid-treated catalysts confirming the best performance.

BaTiO3 Functional Perovskite as Photocathode in Microbial Fuel Cells for Energy Production and Wastewater Treatment.

Microbial fuel cells (MFCs) provide new opportunities for the sustainable production of energy, converting organic matter into electricity through microorganisms. Moreover, MFCs play an important role in remediation of environmental pollutants from wastewater with power generation. This work focuses on the evaluation of ferroelectric perovskite materials as a new class of non-precious photocatalysts for MFC cathode construction. Nanoparticles of BaTiO3 (BT) were prepared and tested in a microbial fuel cell (MFC) as photocathode catalytic components. The catalyst phases were synthesized, identified and characterized by XRD, SEM, UV-Vis absorption spectroscopy, P-E hysteresis and dielectric measurements. The maximum absorption of BT nanoparticles was recorded at 285 nm and the energy gap (Eg) was estimated to be 3.77 eV. Photocatalytic performance of cathodes coated with BaTiO3 was measured in a dark environment and then in the presence of a UV-visible (UV-Vis) light source, using a mixture of dairy industry and domestic wastewater as a feedstock for the MFCs. The performance of the BT cathodic component is strongly dependent on the presence of UV-Vis irradiation. The BT-based cathode functioning under UV-visible light improves the maximum power densities and the open circuit voltage (OCV) of the MFC system. The values increased from 64 mW m-2 to 498 mW m-2 and from 280 mV to 387 mV, respectively, showing that the presence of light effectively improved the photocatalytic activity of this ceramic. Furthermore, the MFCs operating under optimal conditions were able to reduce the chemical oxygen demand load in wastewater by 90% (initial COD = 2500 mg L-1).

ZrP2O7 as a Cathodic Material in Single-Chamber MFC for Bioenergy Production.

The present work is the first investigation of the electrocatalytic performances of ZrP2O7 as a cathode in a single-chamber Microbial Fuel Cell (MFC) for the conversion of chemical energy from wastewater to bioelectricity. This catalyst was prepared by a coprecipitation method, then characterized by X-ray diffraction analysis (XRD), Fourier transform infrared spectroscopy (FTIR), scanning electron microscopy (SEM), energy dispersive X-ray analysis (EDX), ultraviolet-visible-near-infrared spectrophotometry (UV-Vis-NIR), and cyclic voltammetry analyses. The acid-basic characteristics of the surface were probed by using 2-butanol decomposition. The conversion of 2-butanol occurs essentially through the dehydrating reaction, indicating the predominantly acidic character of the solid. The electrochemical test shows that the studied cathode material is electroactive. In addition, the ZrP2O7 in the MFC configuration exhibited high performance in terms of bioelectricity generation, giving a maximum output power density of around 449 mW m-2; moreover, it was active for wastewater treatment, reducing the chemical oxygen demand (COD) charge to 50% after three days of reaction.