Hydrogen Production by Steam Reforming of Ethanol and Dry Reforming of Methane with CO2 on Ni/Vermiculite: Stability Improvement via Acid or Base Treatment of the Support.

In this study, vermiculite was explored as a support material for nickel catalysts in two key processes in syngas production: dry reforming of methane with CO2 and steam reforming of ethanol. The vermiculite underwent acid or base treatment, followed by the preparation of Ni catalysts through incipient wetness impregnation. Characterization was conducted using various techniques, including X-ray diffraction (XRD), SEM-EDS, FTIR, and temperature-programmed reduction (H2-TPR). TG-TD analyses were performed to assess the formation of carbon deposits on spent catalysts. The Ni-based catalysts were used in reaction tests without a reduction pre-treatment. Initially, raw vermiculite-supported nickel showed limited catalytic activity in the dry reforming of methane. After acid (Ni/VTA) or base (Ni/VTB) treatment, vermiculite proved to be an effective support for nickel catalysts that displayed outstanding performance, achieving high methane conversion and hydrogen yield. The acidic treatment improved the reduction of nickel species and reduced carbon deposition, outperforming the Ni over alkali treated support. The prepared catalysts were also evaluated in ethanol steam reforming under various conditions including temperature, water/ethanol ratio, and space velocity, with acid-treated catalysts confirming the best performance.

ZrP2O7 as a Cathodic Material in Single-Chamber MFC for Bioenergy Production.

The present work is the first investigation of the electrocatalytic performances of ZrP2O7 as a cathode in a single-chamber Microbial Fuel Cell (MFC) for the conversion of chemical energy from wastewater to bioelectricity. This catalyst was prepared by a coprecipitation method, then characterized by X-ray diffraction analysis (XRD), Fourier transform infrared spectroscopy (FTIR), scanning electron microscopy (SEM), energy dispersive X-ray analysis (EDX), ultraviolet-visible-near-infrared spectrophotometry (UV-Vis-NIR), and cyclic voltammetry analyses. The acid-basic characteristics of the surface were probed by using 2-butanol decomposition. The conversion of 2-butanol occurs essentially through the dehydrating reaction, indicating the predominantly acidic character of the solid. The electrochemical test shows that the studied cathode material is electroactive. In addition, the ZrP2O7 in the MFC configuration exhibited high performance in terms of bioelectricity generation, giving a maximum output power density of around 449 mW m-2; moreover, it was active for wastewater treatment, reducing the chemical oxygen demand (COD) charge to 50% after three days of reaction.