RESUMEN
Elastic and anelastic properties of ceramic samples of multiferroic perovskites with nominal compositions across the binary join PbZr0.53Ti0.47O3-PbFe0.5Ta0.5O3 (PZT-PFT) have been assembled to create a binary phase diagram and to address the role of strain relaxation associated with their phase transitions. Structural relationships are similar to those observed previously for PbZr0.53Ti0.47O3-PbFe0.5Nb0.5O3 (PZT-PFN), but the magnitude of the tetragonal shear strain associated with the ferroelectric order parameter appears to be much smaller. This leads to relaxor character for the development of ferroelectric properties in the end member PbFe0.5Ta0.5O3. As for PZT-PFN, there appear to be two discrete instabilities rather than simply a reorientation of the electric dipole in the transition sequence cubic-tetragonal-monoclinic, and the second transition has characteristics typical of an improper ferroelastic. At intermediate compositions, the ferroelastic microstructure has strain heterogeneities on a mesoscopic length scale and, probably, also on a microscopic scale. This results in a wide anelastic freezing interval for strain-related defects rather than the freezing of discrete twin walls that would occur in a conventional ferroelastic material. In PFT, however, the acoustic loss behaviour more nearly resembles that due to freezing of conventional ferroelastic twin walls. Precursor softening of the shear modulus in both PFT and PFN does not fit with a Vogel-Fulcher description, but in PFT there is a temperature interval where the softening conforms to a power law suggestive of the role of fluctuations of the order parameter with dispersion along one branch of the Brillouin zone. Magnetic ordering appears to be coupled only weakly with a volume strain and not with shear strain but, as with multiferroic PZT-PFN perovskites, takes place within crystals which have significant strain heterogeneities on different length scales.
RESUMEN
Resonant Ultrasound Spectroscopy has been used to characterize elastic and anelastic anomalies in a polycrystalline sample of multiferroic Pb(Fe(0.5)Nb(0.5))O(3) (PFN). Elastic softening begins at ~550 K, which is close to the Burns temperature marking the development of dynamical polar nanoregions. A small increase in acoustic loss at ~425 K coincides with the value of T(*) reported for polar nanoregions starting to acquire a static or quasi-static component. Softening of the shear modulus by ~30-35% through ~395-320 K, together with a peak in acoustic loss, is due to classical strain/order parameter coupling through the cubic â tetragonal â monoclinic transition sequence of ferroelectric/ferroelastic transitions. A plateau of high acoustic loss below ~320 K is due to the mobility under stress of a ferroelastic microstructure but, instead of the typical effects of freezing of twin wall motion at some low temperature, there is a steady decrease in loss and increase in elastic stiffness below ~85 K. This is attributed to freezing of a succession of strain-coupled defects with a range of relaxation times and is consistent with a report in the literature that PFN develops a tweed microstructure over a wide temperature interval. No overt anomaly was observed near the expected Néel point, ~145 K, consistent with weak/absent spin/lattice coupling but heat capacity measurements showed that the antiferromagnetic transition is actually smeared out or suppressed. Instead, the sample is weakly ferromagnetic up to ~560 K, though it has not been possible to exclude definitively the possibility that this could be due to some magnetic impurity. Overall, evidence from the RUS data is of a permeating influence of static and dynamic strain relaxation effects which are attributed to local strain heterogeneity on a mesoscopic length scale. These, in turn, must have a role in determining the magnetic properties and multiferroic character of PFN.