Surface Evaluation of Enamel Etched by Er,Cr:YSGG Laser for Orthodontic Purpose.

AIM: To compare the effect of erbium, chromium:yttrium-scandium-gallium-garnet (Er,Cr:YSGG) laser at different irradiation parameters and acid etching on the shear bond strength (SBS) of orthodontic brackets to enamel. MATERIALS AND METHODS: Forty bovine incisors were randomly distributed into groups (n = 10): GI: 37% phosphoric acid etching; GII: Er,Cr:YSGG laser etching 19.1 J/cm2; GIII: Er,Cr:YSGG, 29.3 J/cm2; and GIV: Er,Cr:YSGG, 42.4 J/cm2. After treatments, metallic brackets were bonded using Transbond XT adhesive system. After light curing, the samples were subjected to 500 thermal cycles, debonded with a universal testing machine, and the SBS values were recorded. After debonding, surface morphology was evaluated using scanning electron microscopy (SEM) and optical coherence tomography (OCT). The values of SBS testing were analyzed by one-way analysis of variance (ANOVA) and Tukey post hoc test, at 5% significance level. RESULTS: The mean SBS values of GI, GII, GIII, and GIV groups were 6.2 ± 1.7 MPa, 4.6 ± 2.5 MPa, 7.0 ± 2.2 MPa, and 8.0 ± 3.6 MPa, respectively. Laser irradiation promoted rough surfaces in all parameters used, and the OCT analysis revealed higher optical changes on lased groups when compared with phosphoric acid. CONCLUSION: Er,Cr:YSGG laser irradiation operated at 42.4 J/cm2 and 29.3 J/cm2 is a better alternative for etching enamel prior to the orthodontic treatment than the phosphoric acid. CLINICAL SIGNIFICANCE: Er,Cr:YSGG laser irradiation is better than the phosphoric acid for etching enamel prior to the orthodontic treatment because laser irradiation promotes similar SBSs and preventing demineralization around orthodontic brackets.

Variation on Molecular Structure, Crystallinity, and Optical Properties of Dentin Due to Nd:YAG Laser and Fluoride Aimed at Tooth Erosion Prevention.

This in vitro study evaluated the compositional, crystalline, and morphological effects promoted by Nd:YAG laser on root dentin, and verified the effects of laser and topical acidulated phosphate fluoride application (APF-gel) on dentin erosion. 180 bovine dentin slabs were randomized into 4 groups (n = 45): G1-untreated, G2-APF-gel (1.23% F-, 4 min), G3-Nd:YAG (1064 nm, 84.9 J/cm², 10 Hz), and G4-APF-gel application followed by Nd:YAG laser irradiation. The compositional, crystalline, and morphological effects promoted by treatments were investigated on five samples of each experimental group. The other samples were submitted to a 5-day, 10-day, or 15-day erosive and abrasive demineralization and remineralization cycling in order to create erosion lesions. The area and depth of lesions, as well as the optical attenuation coefficient, were assessed, and all data were statistically analysed (p < 0.05). Nd:YAG laser promoted the reduction of carbonate, the formation of tetracalcium phosphate, as well as the melting and recrystallization of the dentin surface. Laser significantly decreased the area and depth of erosion lesions and altered the optical attenuation coefficient when compared to untreated and APF-gel groups, but the association of APF-gel and laser did not promote an additional effect. Nd:YAG laser irradiation can be a promissory treatment to prevent dentin erosion and the abrasion process.