RESUMEN
We present the fabrication and investigation of the properties of nanocomposite structures consisting of two-dimensional (2D) and three-dimensional (3D) metallic nano-objects self-organized on the surface and inside of organic molecular thin-film copper tetrafluorophthalocyanine (CuPcF4). Metallic atoms, deposited under ultrahigh vacuum (UHV) conditions onto the organic ultrathin film, diffuse along the surface and self-assemble into a system of 2D metallic overlayers. At the same time, the majority of the metal atoms diffuse into the organic matrix and self-organize into 3D nanoparticles (NPs) in a well-defined manner. The evolution of the morphology and electronic properties of such structures as a function of nominal metal content is studied under UHV conditions using transmission electron microscopy (TEM), high-resolution transmission electron microscopy (HR-TEM), and photoelectron spectroscopy (PES) techniques. Using HR-TEM, we have observed the periodicity of atomic planes of individual silver NPs. The steady formation of agglomerates from individual single nanocrystallites with intercrystallite boundaries is observed as well. PES reveals generally weak chemical interactions between silver and the organic matrix and n-doping of CuPcF4 at the initial stages of silver deposition, which is associated with charge transfer from the 2D wetting layer on the basis of core-level spectra shift analysis.
RESUMEN
In this paper we present a facile method for the synthesis of aminated graphene derivative through simultaneous reduction and amination of graphene oxide via two-step liquid phase treatment with hydrobromic acid and ammonia solution in mild conditions. The amination degree of the obtained aminated reduced graphene oxide is of about 4 at.%, whereas C/O ratio is up to 8.8 as determined by means of X-ray photoelectron spectroscopy. The chemical reactivity of the introduced amine groups is further verified by successful test covalent bonding of the obtained aminated graphene with 3-Chlorobenzoyl chloride. The morphological features and electronic properties, namely conductivity, valence band structure and work function are studied as well, illustrating the influence of amine groups on graphene structure and physical properties. Particularly, the increase of the electrical conductivity, reduction of the work function value and tendency to form wrinkled and corrugated graphene layers are observed in the aminated graphene derivative compared to the pristine reduced graphene oxide. As obtained aminated graphene could be used for photovoltaic, biosensing and catalysis application as well as a starting material for further chemical modifications.