Antimicrobial efficiency against fish pathogens on the green synthesized silver nanoparticles.

Fish-borne pathogens such as A. hydrophila and F. aquidurense are the most resistant strains in pisciculture farming. Removing the aforementioned pathogens without antibiotics presents a formidable challenge. To overcome this problem, silver nanoparticles (AgNPs) are synthesized using silver nitrate, water medium, and as an AzadirachtaIndica leaf extract via the green synthesis route. X-ray diffraction (XRD) pattern results authenticate the synthesized material is the face-centered cubic structure of silver. The optical absorption edge of the synthesized product was found at the wavelength of 440 nm from the UV-visible spectra, which is confirmed to relate to the Surface Plasmon Resonance peaks of silver particles. In addition, the optical band gap value of the synthesized Ag sample is measured to be 2.81 eV from the obtained optical absorption spectra. EDX spectrum of the synthesized product also supports confirming the silver particle formation. The FT-IR spectra of the neem extract and silver nanoparticles showed their characteristic functional groups, respectively. The presence of bands between 1000 cm-1 to 500 cm-1 indicates to the formation of silver particles. Spherical particles appeared in the synthesized Ag using Scanning Electron Microscopy (SEM) and Transmission Electron Microscopy (TEM). The particle size of Ag NPs was measured as 40 nm and 62 ± 10 nm by TEM and Dynamic Light Scattering (DLS). The zeta potential was also measured as -12 mV showing the synthesized sample's stable nature. Using the DPPH assay, synthesized AgNPs were taken along with the various concentrations of ascorbic acid (20, 40, 60, 80, and 100 µg/mL) to examine the free radical scavenging activity (RSA). RSA value is higher (84 ± 2 %) for synthesized AgNPs at higher concentration (100 µg/mL) than 21 ± 2 % at low concentration (100 µg/mL). The antimicrobial efficacy of the AgNPs against A. hydrophila and F. aquidurense was performed through the agar diffusion method and its results showed the inhibitory zones of the F.aquidurense and A. hydrophila were measured as 25 ± 3 mm, and 28 ± 4 mm respectively. The synthesized Ag particles showed excellent antimicrobial and antioxidant properties confirmed by antimicrobial and DPPH experiments. It implies that the green synthesized silver nanoparticles could be a good alternative for antibiotics in aquaculture farms. The exposure of low concentrations of silver nanoparticles to zebrafish and brine shrimp does not affect the viability and morphology. The exposure of silver nanoparticles in the fisheries in optimized concentration and time could control the fish-borne pathogens without antibiotics.

Tuning the physiochemical properties of polycaprolactone-hydroxyapatite composite films by gamma irradiation for biomedical applications.

Physiochemical properties of polycaprolactone-hydroxyapatite (PCL-HAp) composites were investigated in the pristine and after irradiation of γ rays (25, 50, 75, and 100 kGy). PCL-HAp composites were synthesized by solvent evaporation and characterized using spectroscopic methods as well as biological assays. The surface roughness (RMS) of the irradiated composite film (at 75 kGy) was 80 times higher than that of the pristine. Irradiation tailors the contact angle of the films from 77° to 90° (at 100 kGy). A decrease in particle size (at 100 kGy) of HAp nanorods in PCL-HAp composites film was observed. The XRD peak of PCL was slightly shifted from 21.2° to 21.7° (at 100 kGy) with the decrease in crystallite size. The peak intensity of the PCL and HAp altered on irradiation that was confirmed by FTIR and Raman analysis. Further, the bandgap of the irradiated film was lowered by 13 % (at 25 kGy). The luminescence intensity decreased due to the non-radiative process induced by the irradiation defects. All the samples possess hemocompatibility percentage of <10 % as per ASTM standards. At 75 kGy, fibroblast cell proliferation was higher than the pristine and other doses. The gamma-irradiated PCL-HAp composite films are potential candidates for tissue engineering applications.