Hybrid molecules based on fullerene C60 and dithienylethene and its perfluorinated analog not inferior in the efficiency of phototransformations to the initial photochromic compounds were synthesized for the first time. The resulting pyrrolidinofullerenes containing photochromic moieties were used to fabricate organic field-effect transistors (OFETs) with output and transfer characteristics ten times exceeding similar characteristics of devices based on staring dithienylethenes. It was found that OFETs based on hybrid molecules with dithienylethenes are four times less efficient than devices based on hybrid molecules with perfluorinated analogs.
RESUMEN
The optoelectronic properties of a new poly(2-ethyl-3-methylindole) (MPIn) are discussed in this paper. The absorption and photoluminescence spectra were studied. The electronic spectrum of MPIn showed a single absorption maximum at 269 nm that is characteristic of the entire series of polyindoles. The fluorescence spectra show that the emission peaks of the test sample are centered around 520 nm. The photoconductivity of thin film samples of MPIn polyindole was studied by measuring the current-voltage characteristics under ultraviolet radiation with a wavelength of 350 nm. Samples of phototransistors were obtained, where thin films of MPIn polyindole were used as a transport layer, and their characteristics were measured and analyzed. The value of the quantum efficiency and the values of the mobility of charge carriers in thin polyindole films were estimated.