Highly sensitive triethylamine gas sensor by Pt-loaded p-n heterojunction Co3O4/WO3.

Triethylamine (TEA) exists widely in production and life and is extremely volatile, which seriously endangers human health. It is required to develop high-performance TEA sensors to protect human health. We fabricated Pt-Co3O4/WO3based on our previous work, and the performance was tested against volatile organic compounds. Compared with the previous work, its operating temperature was greatly reduced from 240 °C to 180 °C. The response value of Pt-Co3O4/WO3was increased from 1101 to 1532 for 10 ppm TEA with good selectivity. These results show a significant step toward practical use of the Pt-Co3O4/WO3sensor.

Ultrasensitive ppb-level trimethylamine gas sensor based on p-n heterojunction of Co3O4/WO3.

Trace poisonous and harmful gases in the air have been harming and affecting people's health for a long time. At present, effective and accurate detection of ppb-level harmful gas is still a bottleneck to be overcome. Herein, we report a ppb-level triethylamine (TEA) gas sensor based on p-n heterojunction of Co3O4/WO3, which is prepared with ZIF-67 as the precursor and provides Co3O4deposited tungsten oxide flower-like structure. Due to the introduction of Co3O4and the 3D flower-like structure of WO3, the Co3O4/WO3-2 gas sensor shows excellent gas sensing performance (1101 for 10 ppm at 240 °C), superb selectivity, good long-term stability and linear response for TEA concentration. Moreover, the experimental results indicate that the Co3O4/WO3-2 gas sensor also possesses a good response to 50 ppb TEA, in fact, the theoretical limit of detection is 0.6 ppb. Co3O4not only improves the efficiency of electron separation/transport, but also accelerates the oxidation rate of TEA. This method of synthesizing p-n heterojunction with ZIF as the precursor provides a new idea and method for the preparation of low detection limit gas sensors.

Nonstoichiometric Doping of La0.9FexSn1-xO3 Hollow Microspheres for an Ultrasensitive Formaldehyde Sensor.

Oxygen vacancies play an essential role in gas-sensitive materials, but the intrinsic oxides are poorly controlled and contain low oxygen vacancy concentrations. In this work, we prepared La0.9Fe1-xSnxO3 microspheres with high sensitivity and controllability by a simple hydrothermal method, and then, we demonstrated that it has many oxygen ion defects by X-ray photoelectron spectroscopy and electron paramagnetic resonance characterization. The gas sensor exhibited ultrahigh response, specific recognition of formaldehyde gas, and excellent moisture resistance. By comparing the composites with different doping ratios, it was found that the highest catalytic activity was reached when x = 0.75, and the response value of La0.9Fe0.75Sn0.25O3 hollow microspheres at 200 °C reached 73-10 ppm of formaldehyde, which is 188% higher than that of intrinsic LaFeO3 hollow microspheres. On the one hand, due to the absence of A-site La3+ and the replacement of B-site Fe3+ by Sn4+, a large number of oxygen vacancies are induced on the surface and in the interior of the materials; on the other hand, it is also related to the large specific surface area and gas channels caused by the particular structure.

Pd-SnO2/In2O3 with a Unique Structure for the Ultrasensitive Detection of Triethylamine near Room Temperature.

Triethylamine (TEA) is a serious threat to people's health, and it is still a challenge to detect TEA at ppb level near room temperature (RT). Herein, we developed a simple, low-cost, low-temperature, and ultra-sensitive TEA sensor based on Pd-SnO2/In2O3 composites. First, SnO2 nanoparticles were obtained by the pyrolysis of Sn-MOF@SnO2 precursor (MOF: metal organic framework), and Pd-SnO2/In2O3 composites were prepared by further compounding and doping. The results show that the Pd-SnO2/In2O3 sensor is highly sensitive to TEA gas at near RT (at 60 °C, the sensor response to 10 ppm TEA is 12,000, the response/recovery (res/rec) time is 51 s/493 s, and at 30 °C, the response value also reaches 1380, the res/rec time is 66 s/610 s), along with good selectivity, stability, and moisture resistance. Even at 10 °C operating temperature and 75% relative humidity (RH) in a low-temperature and high-humidity environment, it still maintains a high sensitivity of over 1000 to 10 ppm TEA, which shows great application potential in TEA detection. The reason for the enhanced performance of the 0.5%Pd-SnO2/In2O3 sensor can be attributed to a large number of adsorbed oxygens on the unique structure of the material, the good charge transfer ability of the n-n-type heterojunction between SnO2 and In2O3, the chemical sensitization and electronic sensitization of Pd nanoparticles, and the catalytic spillover effect. This work will provide a new approach for preparing sensors with good comprehensive properties, making full use of the advantages of the material structure-activity relationship.