Effect of double-layer application on the early enamel bond strength of universal adhesives.

OBJECTIVES: The present study aimed to investigate the changes in the enamel bond strengths of universal adhesives in the early phase of specimen creation and evaluate the effect of double-layer application on enamel bond effectiveness using different etching modes. METHOD: Four universal adhesives, namely Clearfil Universal Bond Quick, G-Premio Bond, Scotchbond Universal, and Tokuyama Universal Bond, were used. Clearfil SE Bond two-step self-etch adhesive system was used as a comparison. Fifteen specimens per group were used for determining the shear bond strength (SBS) to bovine enamel in the etch-and-rinse or self-etch mode. The adhesive was applied to specimens in accordance with the manufacturers' instructions (single-layer application), or the adhesive was applied twice (double-layer application). The bonded specimens were stored in distilled water at 37 °C for 5 min or 1, 6, 12, or 24 h before SBS testing. The flexural properties of the resin composite Clearfil AP-X were measured for the same storage periods. RESULTS: All universal adhesives exhibited increased SBS values with prolonged storage periods regardless of the application technique or etching mode used. Double-layer application was associated with higher SBS values than single-layer application for most universal adhesives over the same storage period. CONCLUSION: Phosphoric acid pre-etching and double-layer application of universal adhesives resulted in increased enamel bond strength in the early phase of specimen bonding. CLINICAL RELEVANCE: Care should be taken when using universal adhesives in the self-etch mode for enamel bonding because the enamel adhesion is sensitive to the duration after filling.

Early Phase Enamel Bond Performance of a Two-step Adhesive Containing a Primer Derived from a Universal Adhesive.

PURPOSE: To investigate the changes in the enamel bond performance of a two-step adhesive containing a primer derived from a universal adhesive in the early phase before 24 h and compare them to those of other adhesives. The Knoop hardness number (KHN) of the cured adhesive layers and resin composite was measured. MATERIALS AND METHODS: A new two-step adhesive using universal adhesive technology, G2-Bond Universal, was tested. Two conventional two-step adhesives, Clearfil SE Bond 2 and OptiBond eXTRa, and an established universal adhesive, Scotchbond Universal Plus Adhesive, were used as comparison materials. Twelve specimens per group were used to measure the shear bond strength (SBS) to bovine enamel in different etching modes. The bonded specimens were stored in distilled water at 37°C for 5 min or 1, 6, 12, or 24 h before SBS testing. The KHN of the adhesive layer and resin composite was determined after the same storage periods as for SBS testing. RESULTS: All adhesives exhibited increased SBS with prolonged storage periods, irrespective of the etching mode. The KHN of the adhesive layer and resin composite increased over time. CONCLUSIONS: There were strong positive correlations between the SBS and KHN of the adhesive layer and resin composite. Phosphoric acid pre-etching of enamel effectively increases enamel bond performance. The two-step adhesive G2-Bond Universal demonstrated significantly higher bond strength in the early phase than the other adhesives in self-etch mode.