RESUMEN
The ability of bottlebrush block copolymers (BBCPs) to self-assemble into ordered large periodic structures could greatly expand the scope of photonic and membrane technologies. In this paper, we describe a two-step synthesis of poly(l-lactide)-b-polystyrene (PLLA-b-PS) BBCPs and their rapid thin-film self-assembly. PLLA chains were grown from exo-5-norbornene-2-methanol via ring-opening polymerization (ROP) of l-lactide to produce norbornene-terminated PLLA. Norbonene-terminated PS was prepared using anionic polymerization followed by a termination reaction with exo-5-norbornene-2-carbonyl chloride. PLLA-b-PS BBCPs were prepared from these two norbornenyl macromonomers by a one-pot sequential ring opening metathesis polymerization (ROMP). PLLA-b-PS BBCPs thin-films exhibited cylindrical and lamellar morphologies depending on the relative block volume fractions, with domain sizes of 46-58 nm and periodicities of 70-102 nm. Additionally, nanoporous templates were produced by the selective etching of PLLA blocks from ordered structures. The findings described in this work provide further insight into the controlled synthesis of BBCPs leading to various possible morphologies for applications requiring large periodicities. Moreover, the rapid thin film patterning strategy demonstrated (>5 min) highlights the advantages of using PLLA-b-PS BBCP materials beyond their linear BCP analogues in terms of both dimensions achievable and reduced processing time.
Asunto(s)
Nanoestructuras/química , Poliestirenos/síntesis química , Rastreo Diferencial de Calorimetría , Norbornanos/química , Polimerizacion , Poliestirenos/química , Solventes/química , Espectrometría de Masa por Láser de Matriz Asistida de Ionización Desorción , TermogravimetríaRESUMEN
Diblock brush terpolymers (DBTs) with different fluorinated methacrylate-based block segments are synthesized through sequential ring-opening metathesis polymerizations and are used to prepare polymer thin films with predictable film thicknesses. These DBTs exhibit preferable substrate vertical alignments within the films, induced by the relatively lower surface energy of the fluorinated structural components, together with the overall cylindrical morphology of the brush architecture.