RESUMO
Proton-exchange membranes based on gamma-irradiated films of PVDF and radiation-grafted sulfonated polystyrene with an ion-exchange capacity of 1.8 meq/g and crosslinking degrees of 0 and 3% were synthesized. A solvent-free, environmentally friendly method of styrene grafting from its aqueous emulsion, with a styrene content of only 5 vol.% was used. Energy dispersive X-ray mapping analysis showed that the grafted sulfonated polystyrene is uniformly distributed throughout the membrane thickness. The obtained materials had a proton conductivity up to 132 mS/cm at 80 °C and a hydrogen permeability of up to 5.2 cm2/s at 30 °C, which significantly exceeded similar values for Nafion®-212 membranes. The resulting membranes exhibited a H2/O2 fuel cell peak power density of up to 0.4 W/cm2 at 65 °C. Accelerated stability tests showed that adding a crosslinking agent could significantly increase the stability of the membranes in the fuel cells. The thermal properties and crystallinity of the membranes were investigated through differential scanning calorimetry and X-ray powder diffraction methods. The conductivity, water uptake, and mechanical properties of the membranes (stress-strain curves) were also characterized.
RESUMO
Perfluorosulfonic acid Nafion membranes are widely used as an electrolyte in electrolysis processes and in fuel cells. Changing the preparation and pretreatment conditions of Nafion membranes allows for the optimization of their properties. In this work, a Nafion-NMP membrane with a higher conductivity than the commercial Nafion® 212 membrane (11.5 and 8.7 mSâcm-1 in contact with water at t = 30 °C) and a comparable hydrogen permeability was obtained by casting from a Nafion dispersion in N-methyl-2-pyrrolidone. Since the ion-exchange capacity and the water uptake of these membranes are similar, it can be assumed that the increase in conductivity is the result of optimizing the Nafion-NMP microstructure by improving the connectivity of the pores and channels system. This leads to a 27% increase in the capacity of the membrane electrode assembly with the Nafion-NMP membrane compared to the Nafion® 212 membrane. Thus, the method of obtaining a Nafion membrane has a great influence on its properties and performance of fuel cells based on them.
RESUMO
The development of novel materials with improved functional characteristics for supercapacitor electrodes is of current concern and calls for elaboration of innovative approaches. We report on an eco-friendly enzymatic synthesis of a composite based on poly(3,4-ethylenedioxythiophene) (PEDOT) and multi-walled carbon nanotubes (MWCNTs). The redox active compound, sodium 1,2-naphthoquinone-4-sulfonate (NQS), was used as a dopant for the backbone of the polymer. Oxidative polymerization of 3,4-ethylenedioxythiophene (EDOT) was catalyzed by a high redox potential laccase from the fungus Trametes hirsuta. Atmospheric oxygen served as an oxidant. A uniform thin layer of NQS-doped PEDOT formed on the surface of MWCNTs as a result of the enzymatic polymerization. The PEDOT-NQS/MWCNT composite showed a high specific capacitance of ca. 575 F g-1 at a potential scan rate of 5 mV s-1 and an excellent cycling stability within a potential window between -0.5 and 1.0 V, which makes it a promising electrode material for high-performance supercapacitors.