RESUMO
BACKGROUND: In patients with coronary artery disease treated with permanent polymer-coated drug-eluting stents (DES), the persistent presence of a less biocompatible polymer might delay arterial healing. Thin strut polymer-free DES have the potential to improve clinical outcomes and reduce the duration of dual antiplatelet therapy (DAPT). The purpose of this first-in-human study was to assess the safety and effectiveness of a novel polymer-free DES in patients with de novo coronary lesions. The TIGERevolutioN® stent (CG Bio Co., Ltd., Seoul, Korea) consists of a cobalt chromium platform with a strut thickness of 70 µm and a surface treated with titanium dioxide onto which everolimus-eluting stent (EES) is applied abluminally (6 µg/mm of stent length) without utilization of a polymer. METHODS: A total of 20 patients were enrolled, with de novo coronary lesions (stable or unstable angina) and > 50% diameter stenosis in a vessel 2.25 to 4.00 mm in diameter and ≤ 40 mm in length for angiographic, optical coherence tomography (OCT), and clinical assessment at 8 months. All patients received DAPT after stent implantation. The primary endpoint was angiographic in-stent late lumen loss (LLL) at 8 months. RESULTS: Twenty patients with 20 lesions were treated with TIGERevolutioN®. At 8 months, in-stent LLL was 0.7 ± 0.4 mm. On OCT, percent area stenosis was 29.2 ± 9.4% and stent strut coverage was complete in all lesions. No adverse cardiovascular event occurred at 8 months. CONCLUSION: The new polymer-free EES was safe and effective with low LLL and excellent strut coverage at 8 months of follow-up. TRIAL REGISTRATION: Trial Registration: Clinical Research Information Service Identifier: KCT0005699.
Assuntos
Angiografia Coronária , Doença da Artéria Coronariana , Stents Farmacológicos , Everolimo , Titânio , Tomografia de Coerência Óptica , Humanos , Everolimo/uso terapêutico , Titânio/química , Masculino , Pessoa de Meia-Idade , Feminino , Idoso , Doença da Artéria Coronariana/terapia , Intervenção Coronária Percutânea , Polímeros/química , Resultado do Tratamento , Inibidores da Agregação Plaquetária/uso terapêuticoRESUMO
The purpose of this study was to evaluate the performance of biodegradable polymer sirolimus and ascorbic acid eluting stent systems with four commercially available drug-eluting stents (DES). We investigated the characterization of mechanical properties by dimension, foreshortening, recoil, radial force, crossing profile, folding shape, trackability, and dislodgement force. Additionally, we identify the safety and efficacy evaluation through registry experiments. Each foreshortening and recoil of D + Storm® DES is 1.3 and 3.70%, which has better performance than other products. A post-marketing clinical study to evaluate the performance and safety of D + Storm® DES is ongoing in real-world clinical settings. Two hundred one patients were enrolled in this study and have now completed follow-up for up to 1 month. No major adverse cardiovascular event (MACE) occurred in any subjects, confirming the safety of D + Storm® DES in the clinical setting. An additional approximately 100 subjects will be enrolled in the study and the final safety profile will be assessed in 300 patients. In conclusion, this study reported the objective evaluation of DES performance and compared the mechanical responses of four types of DES available in the market. There is little difference between the four cardiovascular stents in terms of mechanical features, and it can help choose the most suitable stent in a specific clinical situation if those features are understood. Graphical abstract.
Assuntos
Doença da Artéria Coronariana , Stents Farmacológicos , Humanos , Sirolimo , Ácido Ascórbico , Resultado do Tratamento , Polímeros , Implantes Absorvíveis , Desenho de PróteseRESUMO
BACKGROUND: A drug-eluting stent (DES) is a highly beneficial medical device used to widen or unblock narrowed blood vessels. However, the drugs released by the implantation of DES may hinder the re-endothelialization process, increasing the risk of late thrombosis. We have developed a tacrolimus-eluting stent (TES) that as acts as a potent antiproliferative and immunosuppressive agent, enhancing endothelial regeneration. In addition, we assessed the safety and efficacy of TES through both in vitro and in vivo tests. METHODS: Tacrolimus and Poly(lactic-co-glycolic acid) (PLGA) were applied to the metal stent using electrospinning equipment. The surface morphology of the stent was examined before and after coating using a scanning electron microscope (SEM) and energy dispersive X-rays (EDX). The drug release test was conducted through high-performance liquid chromatography (HPLC). Cell proliferation and migration assays were performed using smooth muscle cells (SMC). The stent was then inserted into the porcine coronary artery and monitored for a duration of 4 weeks. RESULTS: SEM analysis confirmed that the coating surface was uniform. Furthermore, EDX analysis showed that the surface was coated with both polymer and drug components. The HPCL analysis of TCL at a wavelength of 215 nm revealed that the drug was continuously released over a period of 4 weeks. Smooth muscle cell migration was significantly decreased in the tacrolimus group (54.1% ± 11.90%) compared to the non-treated group (90.1% ± 4.86%). In animal experiments, the stenosis rate was significantly reduced in the TES group (29.6% ± 7.93%) compared to the bare metal stent group (41.3% ± 10.18%). Additionally, the fibrin score was found to be lower in the TES group compared to the group treated with a sirolimus-eluting stent (SES). CONCLUSION: Similar to SES, TES reduces neointimal proliferation in a porcine coronary artery model, specifically decreasing the fibrins score. Therefore, tacrolimus could be considered a promising drug for reducing restenosis and thrombosis.
Assuntos
Proliferação de Células , Vasos Coronários , Stents Farmacológicos , Tacrolimo , Animais , Tacrolimo/farmacologia , Vasos Coronários/efeitos dos fármacos , Suínos , Proliferação de Células/efeitos dos fármacos , Copolímero de Ácido Poliláctico e Ácido Poliglicólico/química , Miócitos de Músculo Liso/efeitos dos fármacos , Miócitos de Músculo Liso/citologia , Movimento Celular/efeitos dos fármacosRESUMO
BACKGROUND: Current polymer-based drug-eluting stents (DESs) have fundamental issues about inflammation and delayed re-endothelializaton of the vessel wall. Substance-P (SP), which plays an important role in inflammation and endothelial cells, has not yet been applied to coronary stents. Therefore, this study compares poly lactic-co-glycolic acid (PLGA)-based everolimus-eluting stents (PLGA-EESs) versus 2-methacryloyloxyethyl phosphorylcholine (MPC)-based SP-eluting stents (MPC-SPs) in in-vitro and in-vivo models. METHODS: The morphology of the stent surface and peptide/drug release kinetics from stents were evaluated. The in-vitro proliferative effect of SP released from MPC-SP is evaluated using human umbilical vein endothelial cell. Finally, the safety and efficacy of the stent are evaluated after inserting it into a pig's coronary artery. RESULTS: Similar to PLGA-EES, MPC-SP had a uniform surface morphology with very thin coating layer thickness (2.074 µm). MPC-SP showed sustained drug release of SP for over 2 weeks. Endothelial cell proliferation was significantly increased in groups treated with SP (n = 3) compared with the control (n = 3) and those with everolimus (n = 3) (SP: 118.9 ± 7.61% vs. everolimus: 64.3 ± 12.37% vs. the control: 100 ± 6.64%, p < 0.05). In the animal study, the percent stenosis was higher in MPC-SP group (n = 7) compared to PLGA-EES group (n = 7) (MPC-SP: 28.6 ± 10.7% vs. PLGA-EES: 16.7 ± 6.3%, p < 0.05). MPC-SP group showed, however, lower inflammation (MPC-SP: 0.3 ± 0.26 vs. PLGA-EES: 1.2 ± 0.48, p < 0.05) and fibrin deposition (MPC-SP: 1.0 ± 0.73 vs. PLGA-EES: 1.5 ± 0.59, p < 0.05) around the stent strut. MPC-SP showed more increased expression of cluster of differentiation 31, suggesting enhanced re-endothelialization. CONCLUSION: Compared to PLGA-EES, MPC-SP demonstrated more decreased inflammation of the vascular wall and enhanced re-endothelialization and stent coverage. Hence, MPC-SP has the potential therapeutic benefits for the treatment of coronary artery disease by solving limitations of currently available DESs.