Comparative Evaluation of Shear Bond Strength of Resin-modified Glass Ionomer Cement with ProRoot MTA and MTA Angelus.

AIM: The aim of the present study was to evaluate the shear bond strength of resin-modified glass ionomer cement with two different types of mineral trioxide aggregate at different time intervals. MATERIALS AND METHODS: A total of 80 cylindrical blocks were prepared using a self-cure acrylic resin with a central cavity of 4 mm internal diameter and 2 mm height. The prepared samples were randomly divided into two groups (n = 40 each) according to the type of MTA cements used (ProRoot MTA and MTA Angelus). Two groups were further sub-divided into four sub-groups of 10 samples each according to the different time intervals. ProRoot MTA and MTA Angelus were placed in the prepared cavity and a wet cotton pellet was placed over the filled cavity. A hollow plastic tube was placed over the MTA surface and resin-modified glass ionomer cement (RMGIC) was placed into the hollow plastic tube and light-cured (Spectrum 800, Dentsply Caulk Milford, DE, USA) according to the time intervals decided. After light curing the plastic tubes were removed carefully and the specimens were stored at 37°C and 100% humidity for 24 hours to encourage setting of MTA. The specimens were mounted in a universal testing machine (ADMET) and a crosshead speed of 0.5 mm/min was applied to each specimen by using a knife-edge blade until the bond between the MTA and RMGIC failed. The data were statistically analyzed using ANOVA, post hoc Tukey's t-test and Fisher's t-test and p-value ≤ 0.5 was considered significant. RESULTS: For both ProRoot MTA and MTA Angelus there was no statistically significant difference between 45 minutes and 24 hours (p-value ≥ 0.8). For ProRoot MTA, shear bond strength value at 10 minutes were significantly lower than 45 minutes and 24 hours group. However, for MTA Angelus, shear bond strength value at 10 minute was not significantly different from 45 minutes group (p-value ≥ 0.3). For both ProRoot MTA and MTA Angelus shear bond strength value at 0 minute were the least and were significantly lower than 10 minutes, 45 minutes, and 24 hours, respectively (p-value ≥ 0.000). CONCLUSION: Resin-modified glass ionomer cement can be layered over MTA Angelus after it is allowed to set for 10 minutes. However, ProRoot MTA should be allowed to set for at least 45 minutes before the placement of RMGIC to achieve better shear bond strength. CLINICAL SIGNIFICANCE: Due to the variety of types of mineral trioxide aggregate cements available in dentistry, it is justifiable to emphasize on different time intervals as it may affect the shear bond strength of restorative cements. Such information is pivotal for the clinicians while using mineral aggregate-based cements that receive forces from the condensation of restorative materials or occlusion, as the compressive strength may be affected due to different time intervals. How to cite this article: Tyagi N, Chaman C, Anand S, et al. Comparative Evaluation of Shear Bond Strength of Resin-modified Glass Ionomer Cement with ProRoot MTA and MTA Angelus. J Contemp Dent Pract 2024;25(1):35-40.

Apical Periodontitis - Is It Accountable for Cardiovascular Diseases?

The aim of this review was to assess the relationship between apical periodontitis and cardiovascular diseases and the predictive factors regarding this association. Cross sectional and observational studies have been included, which are mostly retrospective. A comprehensive search was performed in the Systematic Electronic Databases, PUBMED and MEDLINE from 1919 till September 2014. Articles were also hand searched. From 86 studies identified, all were read and 58 articles which were relevant were included in the text. Some articles were excluded because they were pertaining to periodontology and other systemic disorders. Some were solely animal studies and were thus excluded. Our results suggest an independent association between cardiovascular diseases and apical periodontitis. A causal relationship could not be established since weak parameters of risk have been assessed in the studies, population taken is difficult to compare and other confounding factors have not been ruled out. Only a more focused and better instituted scientific research can determine this association. Establishing a cause and effect relationship between apical periodontitis and cardiovascular diseases can affect the course of treatment of cardiovascular diseases. It is not only of interest from the scientific point of view but also from public health perspective.

The shear bond strength of MTA with three different types of adhesive systems: An in vitro study.

AIM: To evaluate the shear bond strength of MTA with three different types of adhesive systems- self-adhering flowable composite, etch and rinse adhesive system and self etch adhesive system. METHODOLOGY: MTA specimens (n = 60) were prepared using cylindrical acrylic blocks, having a central cavity with 4 mm diameter and 2 mm depth. MTA was mixed and placed in the prepared cavity, and was covered with a moist cotton pellet and temporary filling material. The specimens were divided into 3 groups which were further divided into 2 sub-groups (45 Minutes and 24 hours). After the application of bonding agents composite resin was placed over the MTA surface. The specimens were tested for shear bond strength and readings were statically analyzed. RESULT: After 24 hrs the mean value of etch and rinse group was significantly higher than self etch and the self adhering composite groups. Among the 45 minutes groups there were no significant difference. CONCLUSION: In single visit after 45 minutes self adhering flowable can be used successfully as a final restorative material in place of conventional flowable composite without using any alternative adhesive system over MTA.