RESUMO
Fabrication of large area, multiscale microtextured surfaces engineered for antiadhesion properties remains a challenge. Compared to an elastic surface, viscoelastic solids show much higher surface stickiness, tack, and adhesion owing to the increased contact area and energy dissipation. Here, we show a simple, low cost, large-area and high throughput method with roll-to-roll compatibility to fabricate multiscale, rough microstructures resistant to adhesion in a viscoelastic layer by controlled tearing of viscous film. Even a high adhesive strength viscoelastic solid layer, such as partially cured PDMS, is made nonsticky simply by its controlled tearing. The torn surface shows a fracture induced, self-organized leaflike micropattern resistant to sticking. The topography and adhesion strength of these structures are readily tuned by changing the tearing speed and the film thickness. The microtexture displays a springlike recovery, low adhesive strength, and easy release properties even under the high applied loads.
RESUMO
Inspired by the detachment mechanics of natural adhesive pads, we studied the change in cavity shape during peel tests on a 10% cross-linked polydimethylsiloxane (PDMS) elastic microchannel filled with 1% cross-linked viscous PDMS liquid (patterned bilayer). During peeling, we explored cavity shape as a function of microchannel dimensions and correlated the dimensionless cavity shape factor (CSF) and characteristic stress decay length, K-1. The peel test on the liquid-filled elastic microchannel shows three distinct cavity-shape regimes, elliptical, circular, and binary, based on the values of CSF and K-1. Such cavity formation and shape regimes could be important for improving the design of pressure-sensitive adhesives.