Synthesis of Ammonium-Based ILs with Different Lengths of Aliphatic Chains and Organic Halogen-Free Anions as Corrosion Inhibitors of API X52 Steel.

In the present work, synthesis and characterization of 15 ionic liquids (ILs) derived from quaternary ammonium and carboxylates were carried out in order to proceed to their evaluation as corrosion inhibitors (CIs) of API X52 steel in 0.5 M HCl. Potentiodynamic tests confirmed the inhibition efficiency (IE) as a function of the chemical configuration of the anion and cation. It was observed that the presence of two carboxylic groups in long linear aliphatic chains reduced the IE, whereas in shorter chains it was increased. Tafel-polarization results revealed the ILs as mixed-type CIs and that the IE was directly proportional to the CI concentration. The compounds with the best IE were 2-amine-benzoate of N,N,N-trimethyl-hexadecan-1-ammonium ([THDA+][-AA]), 3-carboxybut-3-enoate of N,N,N-trimethyl-hexadecan-1-ammonium ([THDA+][-AI]), and dodecanoate of N,N,N-trimethyl-hexadecan-1-ammonium ([THDA+][-AD]) within the 56-84% interval. Furthermore, it was found that the ILs obeyed the Langmuir adsorption isotherm model and inhibited the corrosion of steel through a physicochemical process. Finally, the surface analysis by scanning electron microscopy (SEM) confirmed less steel damage in the presence of CI due to the inhibitor-metal interaction.

Temperature Effect on the Corrosion Inhibition of Carbon Steel by Polymeric Ionic Liquids in Acid Medium.

In the present research work, the temperature effect on the corrosion inhibition process of API 5L X60 steel in 1 M H2SO4 by employing three vinylimidazolium poly(ionic liquid)s (PILs) was studied by means of electrochemical techniques, surface analysis and computational simulation. The results revealed that the maximal inhibition efficiency (75%) was achieved by Poly[VIMC4][Im] at 308 K and 175 ppm. The PILs showed Ecorr displacements with respect to the blank from -14 mV to -31 mV, which revealed the behavior of mixed-type corrosion inhibitors (CIs). The steel micrographs, in the presence and absence of PILs, showed less surface damage in the presence of PILs, thus confirming their inhibiting effect. The computational studies of the molecular orbitals and molecular electrostatic potential of the monomers suggested that the formation of a protecting film could be mainly due to the nitrogen and oxygen heteroatoms present in each structure.

Investigation of Sulfonium-Iodide-Based Ionic Liquids to Inhibit Corrosion of API 5L X52 Steel in Different Flow Regimes in Acid Medium.

The present work deals with the corrosion inhibition mechanism of API 5L X52 steel in 1 M H2SO4 employing the ionic liquid (IL) decyl(dimethyl)sulfonium iodide [DDMS+I-]. Such a mechanism was elicited by the polarization resistance (R p), potentiodynamic polarization (PDP), and electrochemical impedance spectroscopy (EIS) techniques, both in stationary and dynamic states. The electrochemical results indicated that the corrosion inhibition was controlled by a charge transfer process and that the IL behaved as a mixed-type corrosion inhibitor (CI) with anodic preference. The experimental results revealed maximal inhibition efficiency (IE) rates up to 93% at 150 ppm in the stationary state, whereas in turbulent flow, the IE fell to 65% due to the formation of microvortexes that promoted higher desorption of IL molecules from the surface. The Gibbs free energy of adsorption (ΔG°ads) value of -34.89 kJ mol-1, obtained through the Langmuir isotherm, indicated the formation of an IL monolayer on the metal surface by combining physisorption and chemisorption. The surface analysis techniques confirmed the presence of Fe x O y , FeOOH, and IL on the surface and showed that corrosion damage diminished in the presence of IL. Furthermore, the quantum chemistry calculations (DFT) indicated that the iodide anion hosted most of the highest occupied molecular orbital (HOMO), which eased its adsorption on the anodic sites, preventing the deposition of sulfate ions on the electrode surface.

Inhibition Mechanism of Some Vinylalkylimidazolium-Based Polymeric Ionic Liquids against Acid Corrosion of API 5L X60 Steel: Electrochemical and Surface Studies.

A corrosion inhibition mechanism of API 5L X60 steel exposed to 1.0 M H2SO4 was proposed from the evaluation of three vinylalkylimidazolium poly(ionic liquids) (PILs), employing electrochemical and surface analysis techniques. The synthesized PILs were classified as mixed-type inhibitors whose surface adsorption was promoted mainly by bromide and imidazolate ions, which along with vinylimidazolium cations exerted a resistive effect driven by a charge transfer process by means of a protective PIL film with maximal efficiency of 85% at 175 ppm; the steel surface displayed less surface damage due to the formation of metal-PIL complex compounds.