RESUMO
In this study, we address the catalytic performance of variously sized Pt nanoparticles (NPs) (from 1.7 to 2.9 nm) supported on magnéli phase titanium oxide (MPTO, Ti4O7) along with commercial solid type carbon (VXC-72R) for oxygen reduction reaction (ORR). Key idea is to utilize a robust and electrically conductive MPTO as a support material so that we employed it to improve the catalytic activity and durability through the strong metal-support interaction (SMSI). Furthermore, we increase the specific surface area of MPTO up to 61.6 m2 g-1 to enhance the SMSI effect between Pt NP and MPTO. After the deposition of a range of Pt NPs on the support materials, we investigate the ORR activity and durability using a rotating disk electrode (RDE) technique in acid media. As a result of accelerated stress test (AST) for 30k cycles, regardless of the Pt particle size, we confirmed that Pt/MPTO samples show a lower electrochemical surface area (ECSA) loss (<20%) than that of Pt/C (~40%). That is explained by the increased dissolution potential and binding energy of Pt on MPTO against to carbon, which is supported by the density functional theory (DFT) calculations. Based on these results, we found that conductive metal oxides could be an alternative as a support material for the long-term fuel cell operation.
RESUMO
Supportless Pt catalysts have several advantages over conventional carbon-supported Pt catalysts in that they are not susceptible to carbon corrosion. However, the need for high Pt loadings in membrane electrode assemblies (MEAs) to achieve state-of-the-art fuel cell performance has limited their application in proton exchange membrane fuel cells. Herein, we report a new approach to the design of a supportless Pt catalyst in terms of catalyst layer architecture, which is crucial for fuel cell performance as it affects water management and oxygen transport in the catalyst layers. Large Pt hollow spheres (PtHSs) 100 nm in size were designed and prepared using a carbon template method. Despite their large size, the unique structure of the PtHSs, which are composed of a thin-layered shell of Pt nanoparticles (ca. 7 nm thick), exhibited a high surface area comparable to that of commercial Pt black (PtB). The PtHS structure also exhibited twice the durability of PtB after 2000 potential cycles (0-1.3 V, 50 mV/s). A MEA fabricated with PtHSs showed significant improvement in fuel cell performance compared to PtB-based MEAs at high current densities (>800 mA/cm2). This was mainly due to the 2.7 times lower mass transport resistance in the PtHS-based catalyst layers compared to that in PtB, owing to the formation of macropores between the PtHSs and high porosity (90%) in the PtHS catalyst layers. The present study demonstrates a successful example of catalyst design in terms of catalyst layer architecture, which may be applied to a real fuel cell system.
RESUMO
Magnéli phase titanium oxides (MPTOs), possess high electrical conductivity and chemical stability, are promising support materials for the development of novel electrocatalyst in polymer electrolyte fuel cells (PEFCs). Despite MPTO's extremely low specific surface area (1 m2/g or less), high Pt loading (40 wt%) and excellent Pt particle-size distribution were obtained by the modified borohydride method. The reasons were discussed and compared with polyol method. Membrane electrode assembly (MEA) performance of those Pt/MPTO catalysts were found to be 169.7 and 366.2 mA/cm2 at 0.7 V for H2/air and H2/O2, respectively. The accelerated stress tests (ASTs) showed superior durability of the Pt/MPTO catalyst as a cathode electrode. After 10,000 cycles of high-voltage cycling test from 0.9 V and 1.3 V RHE, no significant performance degradation of the Pt/MPTO electrode was observed comparing with Pt/C. Thus, MPTOs can be considered as a good substitute of carbon supports in fuel cells.