Synthesis of Network Biobased Aliphatic Polyesters Exhibiting Better Tensile Properties than the Linear Polymers by ADMET Polymerization in the Presence of Glycerol Tris(undec-10-enoate).

Development of biobased aliphatic polyesters with better mechanical (tensile) properties in film has attracted considerable attention. This report presents the synthesis of soluble network biobased aliphatic polyesters by acyclic diene metathesis (ADMET) polymerization of bis(undec-10-enyl)isosorbide diester [M1, dianhydro-D-glucityl bis(undec-10-enoate)] in the presence of a tri-arm crosslinker [CL, glycerol tris(undec-10-enoate)] using a ruthenium-carbene catalyst, and subsequent olefin hydrogenation using RhCl(PPh3)3. The resultant polymers, after hydrogenation (expressed as HCP1) and prepared in the presence of 1.0 mol% CL, showed better tensile properties than the linear polymer (HP1) with similar molecular weight [tensile strength (elongation at break): 20.8 MPa (282%) in HP1 vs. 35.4 MPa (572%) in HCP1]. It turned out that the polymer films prepared by the addition of CL during the polymerization (expressed as a 2-step approach) showed better tensile properties. The resultant polymer film also shows better tensile properties than the conventional polyolefins such as linear high density polyethylene, polypropylene, and low density polyethylene.

Synthesis of High Molecular Weight Biobased Aliphatic Polyesters Exhibiting Tensile Properties Beyond Polyethylene.

Synthesis of high molecular weight polyesters prepared by acyclic diene metathesis (ADMET) polymerization of bis(undec-10-enoate) with isosorbide (M1), isomannide (M2), and 1,3-propanediol (M3) and the subsequent hydrogenation have been achieved by using a molybdenum-alkylidene catalyst. The resultant polymers (P1) prepared by the ADMET polymerization of M1 (in toluene at 25 °C) possessed high Mn values (Mn = 44400-49400 g/mol), and no significant differences in the Mn values and the PDI (Mw/Mn) values were observed in the samples after the hydrogenation. Both the tensile strength and the elongation at break in the hydrogenated polymers from M1 (HP1) increased upon increasing the molar mass, and the sample with an Mn value of 48200 exhibited better tensile properties (tensile strength of 39.7 MPa, elongation at break of 436%) than conventional polyethylene, polypropylene, as well as polyester containing C18 alkyl chains. The tensile properties were affected by the diol segment employed, whereas HP2 showed a similar property to HP1.