Universal adhesive: the effect of different simulated pulpal pressure fluids and bonding modes to dentin.

The aim of this study was to evaluate the effect of SPP with either fetal bovine serum (FBS) or deionized water (DW) on the bond strength (µTBS) of a Universal adhesive to dentin, in both etch-and-rinse (ER) and self-etch (SE) modes. The kinematic viscosity (cSt) of FBS and DW was measured at 25 °C ± 0.1 ºC. Seventy-two sound human molars were sectioned and randomly divided into three groups according to the SPP conditions: (1) Control (0 cm H2O), (2) SPP (15 cm H2O) with FBS, (3) SPP (15 cm H2O) with DW. Each group was subdivided (n = 10) based on the bonding modes: ER (37% phosphoric acid + ScothBond Universal Adhesive) or SE (ScothBond Universal Adhesive). Samples were then submitted to µTBS. Data were analyzed by Student's t test, two-way ANOVA and Tukey tests (p < 0.05). The cSt results showed that DW (23.59 ± 0.39) had significantly higher values than FBS (22.33 ± 0.06). With regard to SPP, the control group (36.1 MPa) had significantly higher values of µTBS when compared to the SPP using FBS (31.06 MPa) and SPP with DW (26.55 MPa). According to ANOVA, the bonding modes and the interaction of simulated pulpal pressure (SPP) did not statistically influence the results (p < 0.05). The presence of SPP reduced the bond strength of Universal adhesive to dentin. DW during SPP had significantly reduced bonding values when compared to FBS. Bonding strategies were not affected by SPP when evaluated in a short period of time (24 h).

A 2-year clinical evaluation of direct and semi-direct resin composite restorations in non-carious cervical lesions: a randomized clinical study.

OBJECTIVES: The purpose of this study was to evaluate the 2-year success of resin composite restorations in non-carious cervical lesions (NCCLs) using the direct or semi-direct techniques. MATERIALS AND METHODS: Thirty volunteers presenting with at least two NCCLs were included. Each participant received one restoration using the direct technique and the other using the semi-direct technique, totaling 60 restorations. Time for completing the treatment was computed. Assessments at baseline, 7 days, and 6, 12, and 24 months were performed using the modified United States Public Health Service criteria. Descriptive analysis was reported as a percentage of successful treatments. For inferential analysis, the Student t test was used to evaluate the differences between extension, depth, and time. The chi-square/Fisher tests were used to compare treatment success after each period (α = 0.05). The results were evaluated by using the Kaplan-Meier survival analysis. RESULTS: Differences were detected regarding mean ± standard deviation time, in which direct and semi-direct procedures were accomplished in 21.8 (± 14.5) and 35.3 (± 19.9) min, respectively. Of the 60 restorations placed, 7 failed in the direct group while 8 failed in the semi-direct group up to 2 years. No differences were detected between restorative protocols. The cumulative survival was 88.5% and 88.4% for the direct technique and semi-direct techniques after 24 months, respectively. CONCLUSION: The tested restorative protocols present similar results for NCCLs within the studied periods. CLINICAL RELEVANCE: The semi-direct technique exhibited clinical performance similar to direct technique for NCCL, demonstrating an alternative for restorations of these lesions.

Staining Beverages and Cigarette Smoke on Composite Resin and Human Tooth Fluorescence by Direct Spectrometry.

INTRODUCTION: This study evaluated the fluorescence intensity (FI) of different brands of composite resins (CRs) and compare those values with the FI of human tooth, under the action of cigarette smoke (CI), coffee (CA), and soft drink (CO), measured by direct spectrometry. MATERIALS AND METHODS: A total of 30 specimens of each brand (Filtek Z350, Esthet-X, Amelogen, Durafill) were made. Others 30 tooth specimens (3 mm/diameter) were obtained from human molars using a trephine bur. The specimens were randomly divided into three groups (n = 10), according to substances: CI, CA, CO. The FI was directly measured using an optic fiber associated with a spectrometer and was measured at baseline and after staining. Data were submitted to Kruskal-Wallis, Dunnett, and Dunn tests. RESULTS: Staining influenced FI mean values among CRs and between those with human tooth. Z showed the closest FI mean values of tooth after staining. CONCLUSION: Staining beverages and cigarette smoke negatively influenced on FI of CR and human tooth. CLINICAL SIGNIFICANCE: The study shows darkening treatments influenced on the fluorescent property of the dental tissues and restorative materials according to the direct spectrometry analysis.

Grander system: a new technology to reduce surface tension of adhesive systems in dentistry.

BACKGROUND: Reduced surface tension of liquids results in higher surface wetting ability and diffusivity by the substrate. OBJECTIVES: The objective of this study was to evaluate the influence of the Grander Technology in reducing the surface tension of adhesive systems. METHODS: Two adhesive systems (self-etch and total-etch) were modified by physical contact with the Grander system Flexible unit to revitalize water, for 48 h. Surface tension of adhesive systems and water in normal and grander-modified conditions was measured with a goniometer. RESULTS: The results showed a reduction of surface tension for all conditions grander-modified between 3-15%. CONCLUSIONS: Grander Technology was effective in reducing the surface tension of the Single Bond and Clearfil SE Bond adhesive systems. Clinical significance. Grander technology was employed to restructure the molecular structure of water-based adhesive systems, which can increase their wetness capacity and therefore ensure a greater diffusibility.

Inverted Layering Technique as a Biomimetic Procedure in a Multidisciplinary Resolution of Discolored Teeth: A Case Report.

The objective of this work is to report a restorative approach with composite resin applied in reverse in the aesthetic resolution of darkened anterior teeth. A 27-year-old female patient presented with the main complaint of dissatisfaction with the aesthetics of her smile due to dental darkening, a result of childhood trauma, without painful symptoms, pathological clinical signs or change in care. In the intraoral examination, a darkening of teeth 11 and 21 was observed, which radiographically showed thickening of the periodontal ligament, with disharmonious configuration of the marginal gingiva. From the clinical and radiographic characteristics, we opted for periodontal intervention for recovery and gingival levelling, followed by endodontic intervention and aesthetic restorative restoration. The restorative step was carried out sequentially by internal tooth bleaching, removal of dentin still pigmented after bleaching and enamel preservation. Soon after, it was restored in an alternative way and layered using a technique called reverse, using strips of polyethylene fiber over the dentin resin. The technique preserved the remaining enamel with the maintenance of the original remaining guides, proving to be a viable conservative alternative since of the diagnosis to the restorative conclusion in view of the longitudinal confirmation of the restorative efficacy after 1 year.

Longitudinal bond strength of a universal adhesive and chemical dentin characterization under different acid etching protocols.

OBJECTIVE: This study aimed to analyze the longitudinal bond strength of a universal adhesive and chemically characterize the dentin substrate under different acid etching protocols. METHODOLOGY: Dentin samples were etched with polyacrylic acid 25% (PAA) for 10 seconds (n=3) and phosphoric acid 32% (PA) for 15 seconds (n=3) and analyzed by Fourier transform infrared spectroscopy - attenuated total reflectance (FTIR-ATR) before and after treatment. For collagen degradation, samples (n=12) were divided into 3 groups: PAA, PA, and Deionized water (control), and analyzed by the quantity of solubilized type I collagen C-terminal cross-linked telopeptides and solubilized C-terminal peptide in relation to total protein concentration (ICTPtp and CTXtp) and by their ultimate tensile strength (UTS). For the adhesive interface analysis, dentin samples (n=72) were divided into 3 groups: PAA, PA, and Self-etch (SE), and subdivided into 2 groups: 24 h (baseline) and 1 year. The following tests were performed: microtensile bond strength (µTBS) (n=48), scanning electron microscopy (SEM) (n=12), and nanoleakage (n=12). RESULTS: The FTIR of PAA showed lower reduction of the peaks in the phosphate group when compared to PA. For ICTPtp, PA showed a significantly higher value. For CTXtp, PA and PAA groups failed to statically differ from each other. UTS was significantly lower for PA. For µTBS, storage time significantly affected bond strength. The results were unaffected by the etching protocol. For SEM, after 1 year, PA had little evidence of degradation in the upper third of the adhesive interface in comparison to the other groups. Nanoleakage showed no considerable silver impregnation after 1 year in the SE group. CONCLUSION: The use of PAA prior to a universal adhesive (when compared to PA) represents a less aggressive type of etching to dentin. However, self-etching still seems to be the best option for universal adhesive systems that have functional monomers in their composition.

Effect of fluoride, chlorhexidine or Nd:YAG on the progression of root dentin demineralization after removal of the demineralized organic matrix.

OBJECTIVES: Quantification of collagen degradation is an important parameter to evaluate dentin caries for preventive aid.. Evaluate preventive methods against root collagen degradation by the hydroxyproline assay (HYP) and microradiography technique (MRT). METHODOLOGY: Five bovine root dentin blocks were obtained and subjected to an artificial demineralization process by acetate buffer (pH 5) to induce carious lesion formation. Samples were subjected to the following therapeutic treatments: 1) 0.12% chlorhexidine for 1 min, 2) 2% fluoride for 1 min, 3) Nd:YAG Laser (400 µm diameter optical fiber, 10 Hz frequency, 60 mJ/pulse energy, 48 J/cm2 energy density, in noncontact mode for 10 s), 4) deionized water (control) for 1 min, 5) MRT control group (without treatment and removal of collagen). Samples were exposed to degradation by a collagenase enzyme for five days. The enzyme solution was collected, by colorimetry in a spectrophotometer, from the collagen matrix for the hydroxyproline release analysis. The same samples were subjected to an additional two days of demineralization to induce the progression of mineral loss. Samples were analyzed by MRT for the visualization of their degraded areas (estimation of lesion depth and mineral loss). ANOVA was applied to compare hydroxyproline release rates. MRT data were subjected to the Kruskal-Wallis test, followed by the Dunn's test. Comparisons between the initial five-day and the subsequent two-day demineralization processes were performed by repeated t-test or Wilcoxon (p<0.05) measurements. RESULTS: The amount of HYP released from the dentin samples failed to show significant differences among the groups (p=0.09). Fluoride and chlorhexidine were able to interact with the samples, reducing the progression of dentin caries after removal of the demineralized organic matrix. CHX was the only treatment able to show significant lower lesion depth than the negative control. CONCLUSION: Chlorhexidine and fluoride were effective in reducing root caries progression.

How Water Content Can Influence the Chemomechanical Properties and Physical Degradation under Aging of Experimental Adhesives.

Objective: To evaluate the physicochemical (sorption (SOR), solubility (SOL), and degree of conversion (DC)) and mechanical (flexural strength (FS), modulus of elasticity (ME), and compressive strength (CS)) properties of adhesives with different water contents (D2O). Materials and Methods: An adhesive was formulated: 55 wt% BisGMA, 45 wt% HEMA, 0.5 wt% camphorquinone, 0.5 wt% EDMAB, and 1.0 wt% DPIHP. D2O was added into the adhesives (0 wt%, 10 wt%, and 16 wt%). DC was monitored through the FTIR. FS, ME, CS, SOR, and SOL were tested. The adhesive samples were aged in deionized water, ethanol, and acetone. Data were submitted to ANOVA and Tukey's tests (5%). Results: For DC, the 0 wt% group showed a significant reduction (68.09 ± 0.14A) compared with the 10 wt% (87.07 ± 0.81B) and 16 wt% groups (89.87 ± 0.24B); 10 wt% showed the highest FS (MPa) mean values (141.6 ± 6.71B) compared with the 0 wt% (109.4 ± 20.5A) and 16 wt% (107.8 ± 15.8A). For the CS (MPa) and ME (GPa), the 16 wt% showed the lowest mean values (98.8 ± 18.0B and 2.2 ± 0.3B, respectively) compared with the 10 wt% and 0 wt%. For the SOR, 16 wt% of water showed the highest mean values and the ethanol showed the lowest mean values of SOL regardless of water content. Conclusion: The amount of water content and the types of aging solvents significantly affect the adhesive properties.

Prevalence of chewing side preference in the deciduous, mixed and permanent dentitions.

AIM: This study evaluated the prevalence of the chewing side preference (CSP) in the deciduous, mixed and permanent dentitions. MATERIALS AND METHODS: Three-hundred subjects were divided in three groups (n = 100): Group 1 - children with deciduous dentition; group 2-children with mixed dentition; group 3 - subjects with permanent dentition. The CSP was determined using a direct method (visual observation) developed by McDonnell et al. (2004). Descriptive statistic was used to observe the prevalence of CSP. The Pearson's Chi-square was used to investigate signicant associations between gender, presence of CSP and preferred side (right/left). RESULTS AND CONCLUSION: Eighty-seven percent of group 1 had a CSP. Eighty-two percent of group 2 had a CSP. Seventy-six percent of group 3 had a CSP. There was no statistically significant association between presence of CSP and gender in all groups. There was no statistically significant association between preferred side (right/left) and gender in all groups. CLINICAL SIGNIFICANCE: There is a higher prevalence of subjects in deciduous, mixed and permanent dentition that presented chewing side preference. The early diagnosis of the presence of chewing side preference can prevent the unilateral chewing pattern with prophylactic therapy applied to the first teeth (deciduous).

Assessment of color fidelity of several composite resins compared to their Vita Classical shade registration.

This study compared the color fidelity of different composite resins with their registration in the Vita Classical Shade Guide. Using a prefabricated Teflon mold, 120 specimens were divided into four groups (n = 30), according to the resin tested. Three subgroups (n = 10) were prepared for each resin group; these subgroups tested enamel shade, dentin shade, and enamel and dentin shade. Three measurements were performed to verify whether the tooth shade matched that of the Vita Classical Shade Guide. The color was evaluated and the shade variations were calculated. The data were submitted to a three-way ANOVA test (time, color match, and composite type), followed by Tukey's test. It was concluded that all composite resins showed color differences in relation to the Vita Classical Shade Guide.

Polyphenol-enriched extract of Arrabidaea chica used as a dentin pretreatment or incorporated into a total-etching adhesive system: Effects on bonding stability and physical characterization.

The aim of this paper was to evaluate the physical properties and the long-term bond strength of a 2.5% polyphenol-enriched extract of Arrabidaea chica (AC) incorporated into both the phosphoric acid and the primer of a three-step total-etch adhesive, or into an aqueous solution as a dentin pretreatment. Fifty dentin surfaces received the treatments (n = 10): CON (control) - application of the three-step adhesive system (Adper Scotchbond Multipurpose, 3M ESPE); WAT - distilled water used as a pretreatment after dentin etching and before application of the adhesive system; ACPA - AC incorporated into the phosphoric acid; ACW - dentin pre-treatment with AC incorporated into an aqueous solution after etching; ACP - AC incorporated into the primer. Microtensile bond strength tests were performed after 24 h, 6 and 12 months of storage. Slices from the resin-dentin interface were obtained for scanning electron microscopy analysis of the hybrid layer. Degree of conversion of AC incorporated into the primer was evaluated. The particle size, polydispersity index and zeta potential of all the solutions prepared by incorporating AC (phosphoric acid, primer and distilled water) were measured by dynamic light scattering, which brought about changes after incorporation. Degree of conversion of the primer was not affected after incorporating AC. ACP showed lower microtensile bond strength values than the other groups. Bond strength decreased after 6 months of storage, stabilizing at the 12-month evaluation. Therefore, use of AC incorporated into the primer led to lower bond strength values, since AC modified the physical properties (particle size, polydispersity index and zeta potential) of the primer, but did not change the degree of conversion. Application of AC as a dentin pretreatment did not affect bond strength or the micromorphological characteristics of the hybrid layer.

Mechanical-physicochemical properties and biocompatibility of catechin-incorporated adhesive resins.

OBJECTIVES: Several anti-proteolytic dentin therapies are being exhaustively studied in an attempt to reduce dentin bond degradation and improve clinical performance and longevity of adhesive restorations. This study assessed the effect of epigallocatechin-3-gallate (EGCG) on long-term bond strength when incorporated into adhesives. MATERIAL AND METHODS: Adhesive systems were formulated with EGCG concentrations of 0 wt%: (no EGCG; control); 0.5 wt% EGCG; 1.0 wt% EGCG, and 1.5 wt% EGCG. Flexural strength (FS), modulus of elasticity (ME), modulus of resilience (MR), compressive strength (CS), degree of conversion (DC), polymerization shrinkage (PS), percentage of water sorption (%WS), percentage of water solubility (%WL) and cytotoxicity properties were tested. Dentin microtensile bond strength (µTBS) was evaluated after 24 h and again after 6 months of water storage. The adhesive interface was analyzed using scanning electron microscopy (SEM). RESULTS: No significant differences were found among the groups in terms of FS, ME, MR, CS and PS. EGCG-doped adhesives increased the DC relative to the control group. EGCG concentrations of 1.0 wt% and 0.5 wt% decreased the WS of adhesives. WL decreased in all cases in which EGCG was added to adhesives, regardless of the concentration. EGCG concentrations of 1.0 wt% and 0.5 wt% reduced cytotoxicity. EGCG concentrations of 1.0 wt% and 0.5 wt% preserved µTBS after 6 months of storage, while 1.5 wt% EGCG significantly decreased µTBS. SEM: the integrity of the hybrid layer was maintained in the 0.5 wt% and 1.0 wt% EGCG groups. CONCLUSION: EGCG concentrations of 1.0 wt% and 0.5 wt% showed better biological and mechanical performance, preserved bond strength and adhesive interface, and reduced cytotoxicity.

Longitudinal bond strength of a universal adhesive and chemical dentin characterization under different acid etching protocols

Abstract Objective This study aimed to analyze the longitudinal bond strength of a universal adhesive and chemically characterize the dentin substrate under different acid etching protocols. Methodology Dentin samples were etched with polyacrylic acid 25% (PAA) for 10 seconds (n=3) and phosphoric acid 32% (PA) for 15 seconds (n=3) and analyzed by Fourier transform infrared spectroscopy - attenuated total reflectance (FTIR-ATR) before and after treatment. For collagen degradation, samples (n=12) were divided into 3 groups: PAA, PA, and Deionized water (control), and analyzed by the quantity of solubilized type I collagen C-terminal cross-linked telopeptides and solubilized C-terminal peptide in relation to total protein concentration (ICTPtp and CTXtp) and by their ultimate tensile strength (UTS). For the adhesive interface analysis, dentin samples (n=72) were divided into 3 groups: PAA, PA, and Self-etch (SE), and subdivided into 2 groups: 24 h (baseline) and 1 year. The following tests were performed: microtensile bond strength (μTBS) (n=48), scanning electron microscopy (SEM) (n=12), and nanoleakage (n=12). Results The FTIR of PAA showed lower reduction of the peaks in the phosphate group when compared to PA. For ICTPtp, PA showed a significantly higher value. For CTXtp, PA and PAA groups failed to statically differ from each other. UTS was significantly lower for PA. For μTBS, storage time significantly affected bond strength. The results were unaffected by the etching protocol. For SEM, after 1 year, PA had little evidence of degradation in the upper third of the adhesive interface in comparison to the other groups. Nanoleakage showed no considerable silver impregnation after 1 year in the SE group. Conclusion The use of PAA prior to a universal adhesive (when compared to PA) represents a less aggressive type of etching to dentin. However, self-etching still seems to be the best option for universal adhesive systems that have functional monomers in their composition.

Scientific writing with artificial intelligence: key considerations and alerts / Escrita científica com inteligência artificial: principais considerações e alertas

A integração de geradores de texto de inteligência artificial (IA) em relatórios científicos exige uma avaliação cuidadosa de considerações éticas específicas. Embora essas tecnologias de IA ofereçam suporte à geração de texto, abordar as implicações éticas é fundamental. Este editorial destaca a necessidade de uma abordagem ponderada e responsável, enfatizando o estabelecimento de diretrizes e melhores práticas por parte de pesquisadores e comunidades científicas. Esforços colaborativos entre desenvolvedores de IA, pesquisadores e comitês éticos podem garantir a integração perfeita das tecnologias de IA, ao mesmo tempo em que mantêm a integridade, qualidade e padrões éticos da divulgação científica. Este texto oferece um resumo abrangente considerações-chave ao se utilizar geradores de texto de inteligência artificial em relatórios científicos (AU)

The integration of artificial intelligence (AI) text generators in scientific reports demands careful evaluation of specific ethical considerations. While these AI technologies offer text generation support, addressing the ethical implications is vital. This editorial highlights the need for a thoughtful and responsible approach, emphasizing the establishment of guidelines and best practices by researchers and scientific communities. Collaborative efforts between AI developers, researchers, and ethical committees can ensure the seamless integration of AI technologies while upholding the integrity, quality, and ethical standards of scientific reporting. This text comprehensively summarizes the key considerations to be followed when utilizing artificial intelligence text generators in scientific reports.(AU)

Impact of photoinitiator quality on chemical-mechanical properties of dental adhesives under different light intensities / Impacto da qualidade de fotoiniciadores nas propriedades químico mecânicas de adesivos dentais sob diferentes intensidades de luz

Objective: Evaluate the mechanical properties of experimental adhesive models with different photoinitiators (PI) polymerized by LED units of different power densities. Material and Methods: Three groups of adhesive models based on HEMA/BisGMA (45/55) were prepared in association with different PI combinations: G2 (control) ­ 2 PI: 0.5% CQ, 0.5% EDMAB; G3 - 3 PI: 0.5% CQ; 0.5% DMAEMA, 0.5% DPIHP; G4 - 4 PI: 0.5% CQ; 0.5% EDMAB; 0.5% DMAEMA; 0.5% DPIHP. The three formulations were polymerized at two different LED power densities: 550 mW/cm2 and 1200 mW/cm2. The degree of conversion (DC) of adhesive monomers was monitored in situ through the FTIR for 600 s. Specimens were prepared for each formulation for analysis mong adhesive systems (G2

Objetivo: Avaliar as propriedades mecânicas de modelos adesivos experimentais com diferentes fotoiniciadores (PI) polimerizados por unidades de LED de diferentes densidades de energia. Material e Métodos: Três grupos de modelos adesivos baseados em HEMA/BisGMA (45/55) foram preparados em associação com diferentes combinações de PI: G2 (controle) ­ 2 PI: 0,5% CQ, 0,5% EDMAB; G3 - 3PI: 0,5% CQ; 0,5% DMAEMA, 0,5% DPIHP; G4 - 4 PI: 0,5% CQ; 0,5% EDMAB; 0,5% DMAEMA; 0,5% DPIHP. As três formulações foram polimerizadas em duas densidades de potência de LED: 550 mW/cm2 e 1200 mW/cm2. O grau de conversão (DC) dos monômeros adesivos foi monitorado in situ através do FTIR durante 600 s. Amostras foram preparadas para cada formulação para análise de resistência à flexão (FS), módulo de elasticidade (ME), sorção (SOR) e solubilidade (SOL). Os dados foram submetidos aos testes ANOVA 2-fatores e Tukey (5%). Resultados: DC: houve diferença significativa entre os sistemas adesivos (G2

Effect of fluoride, chlorhexidine or Nd:YAG on the progression of root dentin demineralization after removal of the demineralized organic matrix

Abstract Quantification of collagen degradation is an important parameter to evaluate dentin caries for preventive aid. Objectives: Evaluate preventive methods against root collagen degradation by the hydroxyproline assay (HYP) and microradiography technique (MRT). Methodology: Five bovine root dentin blocks were obtained and subjected to an artificial demineralization process by acetate buffer (pH 5) to induce carious lesion formation. Samples were subjected to the following therapeutic treatments: 1) 0.12% chlorhexidine for 1 min, 2) 2% fluoride for 1 min, 3) Nd:YAG Laser (400 μm diameter optical fiber, 10 Hz frequency, 60 mJ/pulse energy, 48 J/cm2 energy density, in noncontact mode for 10 s), 4) deionized water (control) for 1 min, 5) MRT control group (without treatment and removal of collagen). Samples were exposed to degradation by a collagenase enzyme for five days. The enzyme solution was collected, by colorimetry in a spectrophotometer, from the collagen matrix for the hydroxyproline release analysis. The same samples were subjected to an additional two days of demineralization to induce the progression of mineral loss. Samples were analyzed by MRT for the visualization of their degraded areas (estimation of lesion depth and mineral loss). ANOVA was applied to compare hydroxyproline release rates. MRT data were subjected to the Kruskal-Wallis test, followed by the Dunn's test. Comparisons between the initial five-day and the subsequent two-day demineralization processes were performed by repeated t-test or Wilcoxon (p<0.05) measurements. Results: The amount of HYP released from the dentin samples failed to show significant differences among the groups (p=0.09). Fluoride and chlorhexidine were able to interact with the samples, reducing the progression of dentin caries after removal of the demineralized organic matrix. CHX was the only treatment able to show significant lower lesion depth than the negative control. Conclusion: Chlorhexidine and fluoride were effective in reducing root caries progression.

Zn-doped etch-and-rinse model dentin adhesives: Dentin bond integrity, biocompatibility, and properties.

OBJECTIVE: This study assessed a 6 month resin/dentin bond's durability and cytotoxic effect of Zn-doped model dentin adhesives. The mechanical and physicochemical properties were also tested. METHODS: A model etch-and-rinse single-bottle adhesive was formulated (55wt.% Bis-GMA, 45wt.% HEMA, 0.5wt.% CQ, 0.5wt.% DMAEMA) and Zinc methacrylate (Zn-Mt) or ZnO nanoparticles (ZnOn) were added to the model's adhesive, resulting in three groups: Group Control (control model adhesive); Group Zn-Mt (1wt.% Zn-Mt incorporated to adhesive) and Group ZnOn (1wt.% ZnOn incorporated to adhesive). The microtensile bond strength (mTBS) was assessed after 24h or 6 months in water storage. Mechanical properties (diametral tensile strength/DTS, flexural strength/FS, flexural modulus/FM, resilience modulus/RM, and compressive strength/CS) and physicochemical properties (polymerization shrinkage/PS, contact angle/CA, water sorption/WS, and water solubility/WS) were also tested. Cytotoxicity was evaluated with SRB biochemical assay. RESULTS: No significant difference in the DTS, FS, FM, CS, CA, WS, and WS were found when 1% of ZnOn or Zn-Mt was added to the model dentin adhesive. Group Zn-Mt decreased the RM of adhesive. Groups Zn-Mt and ZnOn decreased the PS of adhesives. Group ZnOn reduced the cytotoxicity of adhesive. Group ZnOn preserved mTBS after 6 months storage without degradation areas as seen by SEM analysis. SIGNIFICANCE: The 1wt.% ZnOn may preserve the integrity of the hybrid layer and may reduce cytotoxicity and polymerization shrinkage of model dentin adhesive. The addition of Zn-Mt to the adhesive had no beneficial effects.

Amalgam allergy and Burning Mouth Syndrom: treatment and 25 years recall / Alergia ao amálgama e Síndrome da ardência bucal: tratamento e 25 anos de proservação

Background: Burning mouth syndrome (BMS) is a non-neuropathic chronic orofacial pain condition, characterized by the presence of burning/warm sensation without specific mucosal lesions. Objective: The aim of the present clinical case report is to describe the positive outcome of dental treatment of a patient with BMS and followed up for 25 years. Data Treatment: This report describes the case of a 50-year-old black woman sought treatment for burning, and persistent swelling of tong (24h/day) occurring over years. Clinical evaluation of the oral environment revealed the tongue with cracking, darkened points areas, surrounded by whitish areas. Twelve teeth presented extensive amalgam restorations. Patch testing revealed a very strong hypersensitivity to Amalgam. All amalgam restorations were substituted by composite resin restorations. Results and Conclusion: Burning sensation disappeared completely after these restorations had been changed. After 25-year follow-up period, it was observed that burning sensation has never been felt anymore. Clinical Significance: Burning mouth syndrome is a chronic orofacial pain, usually without specific mucosal lesions. The etiology is complex and multifactorial and the treatment should be made specifically for each pacient. (AU)

Introdução: A síndrome de ardência bucal (SAB) é uma condição de dor orofacial crônica não neuropática, caracterizada pela presença de sensação de queimação/calor sem lesões específicas da mucosa. Objetivo: Oobjetivo do presente relato de caso clínico é descrever a evolução positiva do tratamento odontológico de uma paciente com SAB e o retorno após 25 anos. Tratamento dos Dados: Este relato descreve o caso de uma mulher negra de 50 anos que buscou tratamento por queimadura e edema persistente da língua (24h/dia) ocorrendo ao longo dos anos. A avaliação clínica da cavidade bucal revelou a língua com áreas fissuradas e áreas com pontos escurecidos circundadas por áreas esbranquiçadas. Doze dentes apresentavam restaurações extensas de amálgama de prata. O teste de contato revelou hipersensibilidade muito forte ao amálgama de prata. Todas as restaurações de amálgama de prata foram substituidas por restaurações de resina composta. Resultados e Conclusão: A sensação de queimação desapareceu completamente após a substituição das restaurações. Após um periodo de 25 anos, observou-se que a sensação de queimação nunca foi mais relatada. Significado Clínico: a síndrome da ardência bucal é uma dor orofacial crônica, geralmente sem lesões específicas da mucosa. A etiologia é complexa e multifatorial e o tratamento deve ser feito especificamente para cada paciente.(AU)

Full digital workflow in fixed adhesive dental prosthesis: Description of a clinical technique / Fluxo de trabalho digital completo em prótese fixa adesiva: descrição de uma técnica clínica

Digital dentistry has gained space in several dental specialties. It is possible to achieve excellent results with the digital workflow, which combines the efficiency of the restorative material with a greater marginal adaptation. This study aimed to report a clinical case through the digital workflow, with a faster and clinically acceptable prosthetic resolution. In this clinical case report, digital workflow allowed a faster and clinically acceptable prosthetic resolution. A 45-year-old female patient reported cementation failure of the prosthetic crown on tooth 14. As it was a vital tooth, the tooth received a total crown preparation. In the same clinical session, the patient's mouth was scanned then a capture software obtained a virtual model. After, the design software planned a digital "diagnostic wax-up", so a leucitic ceramic was chosen for the rehabilitation. The ceramic block was milled and receive stain and glaze, dispensing the prosthesis laboratory. Then, the adhesive cementation was performed with a dual-polymerized resin cement. The final crown had ideal adaptation, with no need for interproximal and occlusal adjustments, with an excellent marginal fit. Within the limitations of this study, this case report showed that the digital workflow allowed a favorable result in a shorter working time, which brought back function and aesthetics, without the need for interproximal and occlusal adjustments. (AU)

A odontologia digital vem ganhando espaço em diversas especialidades odontológicas. Com o fluxo de trabalho digital, é possível alcançar excelentes resultados na reabilitação protética, combinando a eficiência do material restaurador com a adaptação marginal proporcionada pela odontologia digital. O objetivo desse estudo foi relatar um caso clínico através do fluxo de trabalho digital, com uma resolução protética mais rápida e clinicamente aceitável. Paciente do sexo feminino, 45 anos, relatou falha de cimentação da coroa protética do dente 26. Por ser um dente vital, o dente recebeu um preparo de coroa total e os dentes foram escaneados e um software de captura obteve um modelo virtual. Posteriormente, o software de projeto planejou um "enceramento diagnóstico" digital, sendo escolhida uma cerâmica leucítica para a reabilitação. O bloco cerâmico foi fresado e recebeu acabamento, maquiagem e glaze pelo próprio dentista, dispensando um técnico laboratorial de prótese dentária. Em seguida, foi realizada cimentação adesiva definitiva. Este relato de caso mostra que, dentro das limitações desse estudo, o fluxo digital permite um resultado favorável em um menor tempo de trabalho, devolvendo a função e estética, sem necessidade de ajustes interproximais e oclusais (AU)

Marginal leakage in class V cavities pretreated with different laser energy densities.

The purpose of the present study was to evaluate in vitro the degree of marginal leakage in Class V cavities involving the cementoenamel junction. Cavities were 4 mm wide and 2 mm deep. The specimens received dentin pretreatment (37% phosphoric acid) followed by the Single Bond (3M) adhesive system application. The 40 specimens were then divided into four groups: Group 1 (control); Group 2 (Nd:YAG laser at 120 mJ/pulse, frequency of 10 Hz, power of 1.2 W); Group 3 (Nd:YAG laser at 140 mJ/pulse, frequency of 10 Hz, power of 1.4 W); Group 4 (Nd:YAG laser at 160 mJ/pulse, frequency of 10 Hz, power of 1.6 W). The cavities were restored with Z100 composite resin (3M) and light cured at 300-600 mW/cm2 light intensity. Specimens were thermocycled to 500 cycles from 2-50 degrees C. After that, they were dried and sealed with nail varnish, respecting 1 mm around the restorations, and immersed in 0.5% methylene blue solution for 4 h. After this period, the teeth were rinsed, dried, sectioned, and analyzed in a stereoscopic loupe. The highest leakage scores were considered for each specimen. The results were statistically analyzed by the analysis of variance (ANOVA) - Kruskal-Wallis test to the 5% level. For both the enamel and cementum, there was a decrease in marginal leakage with the application of laser energy; no significant differences were observed for Groups 2, 3, and 4. The results also showed a smaller tendency to marginal leakage on the cementum than on the enamel.