Development of a novel biosensor based on a conducting polymer.

A new type of amperometric cholesterol biosensor was fabricated to improve the biosensor characteristics such as sensitivity and reliability. For this purpose, a novel immobilization matrix 2-(4-fluorophenyl)-4,7-di(thiophene-2-yl)-1H-benzo[d]imidazole (BIPF) was electrochemically deposited on a graphite electrode and used as a matrix for the immobilization of cholesterol oxidase (ChOx). Due to strong π-π stacking of aromatic groups in the structures of polymer backbone and enzyme molecule, one can easily achieve a sensitive and reliable biosensor without using any membrane or covalent bond formation between the enzyme molecules and polymer surface. Moreover, through pendant fluorine group of the polymer, H-bond formation between with enzyme molecules and polymer was generated. Cholesterol was used as the substrate and amperometric response was measured in correlation with cholesterol amount, at -0.7 V vs. Ag/AgCl in phosphate buffer (pH 7.0). Consequently, optimum conditions for this constructed biosensor were determined. K(M)app, I(max), LOD and sensitivity values were investigated and calculated as 4.0 nM, 2.27 µA, 0.404 µM and 1.47 mA/mM cm(2), respectively. A novel and accurate cholesterol biosensor was developed for the determination of total cholesterol in food samples.

Development of an efficient immobilization matrix based on a conducting polymer and functionalized multiwall carbon nanotubes: synthesis and its application to ethanol biosensors.

Material modification is one of the hot topics recently. Hereby a novel functional monomer, 2-(4-nitrophenyl)-4,7-di(thiophen-2-yl)-1H-benzo[d]imidazole (BIPN), was synthesized for matrix generation through electrochemical polymerization. Its conducting polymer was successfully used for the biolayer construction in the biosensor preparation. The electrochemical and morphological properties were improved by the introduction of carboxylic acid functionalized multiwall carbon nanotubes (f-MWCNTs). Carboxylic acid functionalization of MWCNTs was carried out via acid treatment. The electrode surface was modified with the polymer and f-MWCNTs during electropolymerization to achieve a perfect immobilization matrix for alcohol oxidase. In order to prepare a new alcohol biosensor, alcohol oxidase (AOx) was immobilized onto the modified electrode. The modified electrode was characterized by scanning electron microscopy (SEM), X-ray photoelectron microscopy (XPS) and Fourier transform infrared (FTIR) spectroscopy techniques. Electrochemical responses of the enzyme electrodes were monitored at -0.7 V vs. Ag reference electrode by monitoring oxygen consumption in the presence of ethanol. Kinetic parameters, operational and storage stabilities were investigated. K, Imax, LOD and sensitivity were calculated as 16.946 mM, 3.31 µA, 0.806 mM and 476 µA mM-1 cm-2, respectively. Finally, this biosensor was applied to estimate the alcohol content in various beverages successfully.

A novel and effective surface design: conducting polymer/ß-cyclodextrin host-guest system for cholesterol biosensor.

The combination of supramolecules and conducting polymers (CPs) has gained much attention for the development of new immobilization matrices for biomolecules. Herein, an amperometric biosensor based on a novel conducting polymer, poly(2-(2-octyldodecyl)-4,7-di(selenoph-2-yl)-2H-benzo[d][1,2,3]triazole)) (PSBTz) and ß-cyclodextrin (ß-CD) for the detection of cholesterol, was constructed. The PSBTz film with ß-CD was deposited on a graphite electrode by electropolymerization technique to achieve a suitable matrix for enzyme immobilization. Moreover, to justify the immobilization, alkyl chain containing conducting polymer (PSBTz) was designed, synthesized and electrochemically polymerized on the transducer surface. Alkyl chains in the structure of SBTz and hydroxyl groups of ß-CD contributed to effective immobilization while protecting the suitable orientation of the biomolecule. Cholesterol oxidase (ChOx) was covalently immobilized onto the modified surface using N,N'-carbonyldiimidazole (CDI) as the cross-linking agent. After successful immobilization, amperometric biosensor responses were recorded at −0.7 V vs Ag/AgCl in phosphate buffer (pH 7.0). The apparent Michaelis-Menten constant (KM(app)), maximum current (Imax), limit of detection (LOD), and sensitivity values were determined: 28.9 µM, 12.1 µA, 0.005 µM, and 5.77 µA/µM cm(2), respectively. The fabricated biosensor was characterized using scanning electron microscopy (SEM) and cyclic voltammetry (CV) techniques. Finally, the prepared biosensor was successfully applied for the determination of cholesterol in blood samples.