RESUMO
The origin of limited plasticity in metallic glasses is elusive, with no apparent link to their atomic structure. We propose that the response of the glassy structure to applied stress, not the original structure itself, provides a gauge to predict the degree of plasticity. We carried out high-energy x-ray diffraction on various bulk metallic glasses (BMGs) under uniaxial compression within the elastic limit and evaluated the anisotropic pair distribution function. We show that the extent of local deviation from the affine (uniform) deformation in the elastic regime is strongly correlated with the plastic behavior of BMGs beyond yield, across chemical compositions and sample history. The results suggest that the propensity for collective local atomic rearrangements under stress promotes plasticity.
RESUMO
We studied the effect of crystallization on the embrittlement of bulk metallic glasses. Specifically, we measured fracture toughness for Zr(44)Ti(11)Cu(10)Ni(10)Be(25) and Pd(43)Cu(27)Ni(10)P(20) after annealing at various times to introduce controlled volume fraction of crystallization. We found that crystallization of up to â¼6% by volume does not measurably affect fracture toughness. When exceeding â¼6%, a dramatic drop in fracture toughness occurs; an additional 1% of crystallization reduces fracture toughness by 50%. Such a dramatic transition can be explained by the interaction among the crystals' stress fields in the amorphous matrix that becomes effective at â¼7% crystallinity. Our findings of a critical crystallization for embrittlement of metallic glasses help in designing tough metallic glasses and their composites, as well as defining processing protocols for the unique thermoplastic forming of metallic glasses to avoid embrittlement.
RESUMO
Angular symmetry in diffraction reflects rotational symmetry in the sample. We introduce the angular symmetry coefficient as a method to extract local symmetry information from electron nanodiffraction patterns of amorphous materials. Symmetry coefficients are the average of the angular autocorrelation function at the characteristic angles of a particular rotational symmetry. The symmetry coefficients avoid non-structural features arising from Fourier transformation and Friedel symmetry breakdown that affect the angular power spectrum approach to determining angular symmetries in amorphous nanodiffraction. Both methods require thin samples to avoid overlapping diffraction from clusters of atoms separated in the thickness of the sample, but symmetry coefficients are more forgiving. Electron nanodiffraction experiments on a Pd-based metallic glass sample demonstrate both potentially misleading information in angular power spectrum and the utility of symmetry coefficients.
RESUMO
The dynamics near the surface of glasses can be much faster than in the bulk. We studied the surface dynamics of a Pt-based metallic glass using electron correlation microscopy with sub-nanometer resolution. Our studies show an â¼20 K suppression of the glass transition temperature at the surface. The enhancement in surface dynamics is suppressed by coating the metallic glass with a thin layer of amorphous carbon. Parallel molecular dynamics simulations on Ni80P20 show a similar temperature suppression of the surface glass transition temperature and that the enhanced surface dynamics are arrested by a capping layer that chemically binds to the glass surface. Mobility in the near-surface region occurs via atomic caging and hopping, with a strong correlation between slow dynamics and high cage-breaking barriers and stringlike cooperative motion. Surface and bulk dynamics collapse together as a function of temperature rescaled by their respective glass transition temperatures.
RESUMO
The fracture toughness of glassy materials remains poorly understood. In large part, this is due to the disordered, intrinsically non-equilibrium nature of the glass structure, which challenges its theoretical description and experimental determination. We show that the notch fracture toughness of metallic glasses exhibits an abrupt toughening transition as a function of a well-controlled fictive temperature (Tf), which characterizes the average glass structure. The ordinary temperature, which has been previously associated with a ductile-to-brittle transition, is shown to play a secondary role. The observed transition is interpreted to result from a competition between the Tf-dependent plastic relaxation rate and an applied strain rate. Consequently, a similar toughening transition as a function of strain rate is predicted and demonstrated experimentally. The observed mechanical toughening transition bears strong similarities to the ordinary glass transition and explains the previously reported large scatter in fracture toughness data and ductile-to-brittle transitions.
RESUMO
We used pulsed laser beam welding method to join Pd43Cu27Ni10P20 (at.%) bulk metallic glass and characterized the properties of the joint. Fusion zone and heat-affected zone in the weld joint can be maintained completely amorphous as confirmed by X-ray diffraction and differential scanning calorimetry. No visible defects were observed in the weld joint. Nanoindentation and bend tests were carried out to determine the mechanical properties of the weld joint. Fusion zone and heat-affected zone exhibit very similar elastic moduli and hardness when compared to the base material, and the weld joint shows high ductility in bending which is accomplished through the operation of multiple shear bands. Our results reveal that pulsed laser beam welding under appropriate processing parameters provides a practical viable method to join bulk metallic glasses.