High-strength gypsum binder with improved water-resistance coefficient derived from industrial wastes.

The article presents the possibility of increasing the water resistance of gypsum binders (GBs) obtained based on synthetic gypsum by introducing additives derived from industrial wastes. Regularities were obtained for the influence of the type and amount of additives on the water/gypsum ratio (W/G), strength indicators and water resistance of high-strength GB. The introduction of a single-component additive to improve water resistance does not have a significant effect. Complex additives based on Portland cement, granulated blast-furnace slag, electric steel-smelting slag, expanded clay dust and granite screenings of various fractions have been developed that make the maximum contribution to improving the water resistance of a high-strength GB based on synthetic calcium sulphate dihydrate, which made it possible to increase the water-resistance coefficient from 0.39 to 0.82.

Combustion Synthesis and Reactive Spark Plasma Sintering of Non-Equiatomic CoAl-Based High Entropy Intermetallics.

The present work reports the direct production of a high-entropy (HE) intermetallic CoNi0.3Fe0.3Cr0.15Al material with a B2 structure from mechanically activated elemental powder mixtures. Fast and efficient combustion synthesis (CS), spark plasma sintering (SPS), and reactive SPS (RSPS) methods were used to synthesize the HE powders and bulks. The formation of the main B2 phase along with some amounts of secondary BCC and FCC phases are reported, and L12 intermetallic (CS scheme) and BCC based on Cr (CS + SPS and RSPS schemes at 1000 °C) were observed in all samples. The interaction between the components during heating to 1600 °C of the mechanically activated mixtures and CS powders has been studied. It has been shown that the formation of the CoNi0.3Fe0.3Cr0.15Al phase occurs at 1370 °C through the formation of intermediate intermetallic phases (Al9Me2, AlCo, AlNi3) and their solid solutions, which coincidences well with thermodynamic calculations and solubility diagrams. Compression tests at room and elevated temperatures showed that the alloy obtained by the RSPS method has enhanced mechanical properties (σp = 2.79 GPa, σ0.2 = 1.82 GPa, ε = 11.5% at 400 °C) that surpass many known alloys in this system. High mechanical properties at elevated temperatures are provided by the B2 ordered phase due to the presence of impurity atoms and defects in the lattice.

Effect of High-Pressure Torsion on the Microstructure and Magnetic Properties of Nanocrystalline CoCrFeNiGax (x = 0.5, 1.0) High Entropy Alloys.

In our search for an optimum soft magnet with excellent mechanical properties which can be used in applications centered around "electro mobility", nanocrystalline CoCrFeNiGax (x = 0.5, 1.0) bulk high entropy alloys (HEA) were successfully produced by spark plasma sintering (SPS) at 1073 K of HEA powders produced by high energy ball milling (HEBM). SPS of non-equiatomic CoCrFeNiGa0.5 particles results in the formation of a single-phase fcc bulk HEA, while for the equiatomic CoCrFeNiGa composition a mixture of bcc and fcc phases was found. For both compositions SEM/EDX analysis showed a predominant uniform distribution of the elements with only a small number of Cr-rich precipitates. High pressure torsion (HPT) of the bulk samples led to an increased homogeneity and a grain refinement: i.e., the crystallite size of the single fcc phase of CoCrFeNiGa0.5 decreased by a factor of 3; the crystallite size of the bcc and fcc phases of CoCrFeNiGa-by a factor of 4 and 10, respectively. The lattice strains substantially increased by nearly the same extent. After HPT the saturation magnetization (Ms) of the fcc phase of CoCrFeNiGa0.5 and its Curie temperature increased by 17% (up to 35 Am2/kg) and 31.5% (from 95 K to 125 K), respectively, whereas the coercivity decreased by a factor of 6. The overall Ms of the equiatomic CoCrFeNiGa decreased by 34% and 55% at 10 K and 300 K, respectively. At the same time the coercivity of CoCrFeNiGa increased by 50%. The HPT treatment of SPS-consolidated HEAs increased the Vickers hardness (Hv) by a factor of two (up to 5.632 ± 0.188) only for the non-equiatomic CoCrFeNiGa0.5, while for the equiatomic composition, the Hv remained unchanged (6.343-6.425 GPa).

Extremely hard and tough high entropy nitride ceramics.

Simultaneously hard and tough nitride ceramics open new venues for a variety of advanced applications. To produce such materials, attention is focused on the development of high-entropy ceramics, containing four or more metallic components distributed homogeneously in the metallic sublattice. While the fabrication of bulk high-entropy carbides and borides is well established, high-entropy nitrides have only been produced as thin films. Herein, we report on a newel three-step process to fabricate bulk high-entropy nitrides. The high-entropy nitride phase was obtained by exothermic combustion of mechanically-activated nanostructured metallic precursors in nitrogen and consolidated by spark plasma sintering. The fabricated bulk high-entropy nitride (Hf0.2Nb0.2Ta0.2Ti0.2Zr0.2)N demonstrates outstanding hardness (up to 33 GPa) and fracture toughness (up to 5.2 MPa∙m1/2), significantly surpassing expected values from mixture rules, as well as all other reported binary and high-entropy ceramics and can be used for super-hard coatings, structural materials, optics, and others. The obtained results illustrate the scalable method to produce bulk high-entropy nitrides with the new benchmark properties.