RESUMO
Raman analysis of dilute aqueous solutions is normally prevented by their low signal levels. A very general method to increase the concentration to detectable levels is to evaporate droplets of the sample to dryness, creating solid deposits which are then Raman probed. Here, superhydrophobic (SHP) wires with hydrophilic tips have been used as supports for drying droplets, which have the advantage that the residue is automatically deposited at the tip. The SHP wires were readily prepared in minutes using electroless galvanic deposition of Ag onto copper wires followed by modification with a polyfluorothiol (3,3,4,4,5,5,6,6,7,7,8,8,9,9,10,10,10-heptadecafluoro-1-decanethiol, HDFT). Cutting the coated wires with a scalpel revealed hydrophilic tips which could support droplets whose maximum size was determined by the wire diameter. Typically, 230 µm wires were used to support 0.6 µL droplets. Evaporation of dilute melamine droplets gave solid deposits which could be observed by scanning electron microscopy (SEM) and Raman spectroscopy. The limit of detection for melamine using a two stage evaporation procedure was 1 × 10(-6) mol dm(-3). The physical appearance of dried droplets of sucrose and glucose showed that the samples retained significant amounts of water, even under high vacuum. Nonetheless, the Raman detection limits of sucrose and glucose were 5 × 10(-4) and 2.5 × 10(-3) mol dm(-3), respectively, which is similar to the sensitivity reported for surface-enhanced Raman spectroscopy (SERS) detection of glucose. It was also possible to quantify the two sugars in mixtures at concentrations which were similar to those found in human blood through multivariate analysis.
Assuntos
Cobre/química , Interações Hidrofóbicas e Hidrofílicas , Hidrocarbonetos Fluorados/química , Tamanho da Partícula , Prata/química , Soluções , Análise Espectral Raman , Compostos de Sulfidrila/química , Propriedades de Superfície , Volatilização , Água/químicaRESUMO
SERS primers have been used to directly detect specific PCR products utilizing the difference in adsorption of single-stranded and double-stranded DNA onto nanoparticle surfaces. Herein, seven parameters important for improved positive SERS assays for real applications were investigated. First, we applied a model system for optimization experiments, followed by a PCR assay to detect pathogen DNA, and then the introduction of a new assay that utilizes the 5'â3' exonuclease activity of Taq DNA polymerase to partly digest the SERS probe, generating dye-labeled single-stranded DNA increasing the SERS signals for detection of pathogen DNA. Applying the model system, it was found that uni-molecular SERS primers perform better than bi-molecular SERS primers. However, within the PCR assays, it was found that uni- and bi-molecular SERS primers performed very similarly, and the most reproducible results were obtained using the 5'â3' exonuclease digestion assay. These SERS-based assays offer new routes over conventional fluorescence-based techniques without compromising sensitivity or selectivity.
Assuntos
Primers do DNA/análise , DNA Bacteriano/análise , Análise Espectral Raman/métodos , Primers do DNA/genética , DNA Bacteriano/genéticaRESUMO
Colorimetric detection of analytes using gold nanoparticles along with surface-enhanced Raman spectroscopy (SERS) are areas of intense research activity since they both offer sensing of very low concentrations of target species. Multimodal detection promotes the simultaneous detection of a sample by a combination of different techniques; consequently, surface chemistry design in the development of multimodal nanosensors is important for rapid and sensitive evaluation of the analytes by diverse analytical methods. Herein it is shown that nanoparticle size plays an important role in the design of functional nanoparticles for colorimetric and SERS-based sensing applications, allowing controlled nanoparticle assembly and tunable sensor response. The design and preparation of robust nanoparticle systems and their assembly is reported for trace detection of Ni(II) ions as a model system in an aqueous solution. The combination of covalently attached nitrilotriacetic acid moieties along with the L-carnosine dipeptide on the nanoparticle surface represents a highly sensitive platform for rapid and selective detection of Ni(II) ions. This systematic study demonstrates that significantly lower detection limits can be achieved by finely tuning the assembly of gold nanoparticles of different core sizes. The results clearly demonstrate the feasibility and usefulness of a multimodal approach.
Assuntos
Colorimetria/métodos , Ouro/química , Nanopartículas Metálicas/química , Nanoestruturas/química , Nanotecnologia/métodos , Níquel/química , Tamanho da PartículaRESUMO
A fast and cost-effective approach for the synthesis of substrates used in surface enhanced Raman scattering (SERS) has been developed using galvanic displacement. Deposition of silver onto commercially available Cu foil has resulted in the formation of multiple hierarchical structures, whose morphology show dependence on deposition time and temperature. Analysis of the surface structure by scanning electron microscopy revealed that the more complex silver structures correlated well with increased deposition time and temperature. Using Rhodamine 6G (R6G) as a model Raman probe it was also possible to relate the substrate morphology directly with subsequent SERS intensity from the R6G analyte as well as the reproducibility across a total of 15 replicate Raman maps (20 × 20 pixels) consisting of 400 spectra at a R6G concentration of 10(-4) M. The substrate with the highest reproducibility was then used to explore the limit of detection and this compared very favourably with colloidal-based SERS assessments of the same analyte.
Assuntos
Cobre/química , Prata/química , Análise Espectral Raman/métodos , Coloides , Limite de Detecção , Rodaminas/análise , Rodaminas/química , Soluções , Propriedades de Superfície , Temperatura , Fatores de TempoRESUMO
A highly SERS-active substrate was fabricated by trapping gold "nanoworms" on commercially available filter membranes providing significant enhancement of the Raman signal as a result of the remarkable electromagnetic couplings induced by the dense packing. The resultant substrate provides a simple and cost-effective porous SERS surface for use and quantitative analytical procedures.
RESUMO
Surface enhancement can provide improved detection sensitivity in a range of optical spectroscopies. When applied to bioanalysis these enhanced techniques allow for the detection of disease biomarkers at lower levels, which has a clear patient benefit. However, to achieve widespread clinical use of surface enhanced techniques there remain several "grand challenges". In this review we consider the substrates employed to achieve enhancement before reviewing each enhanced optical technique in detail; surface plasmon resonance, localised surface plasmon resonance, surface enhanced fluorescence, surface enhanced infrared absorption spectroscopy and surface enhanced (resonance) Raman spectroscopy. Finally we set out the "grand challenges" currently facing the field.
Assuntos
Técnicas de Química Analítica/métodos , Espectrometria de Fluorescência/métodos , Espectrofotometria Infravermelho/métodos , Análise Espectral Raman/métodos , Ressonância de Plasmônio de Superfície/métodos , Propriedades de SuperfícieRESUMO
Optical analysis in the near infrared region is of significant biological importance due to better tissue penetration and reduced autofluorescence. In this work, an improved synthesis of hollow gold nanospheres (HGNs), which provides a tunable localized surface plasmon resonance (LSPR) from 610 nm up to 1320 nm, is demonstrated. The scattering properties of these nanoparticles are shown using surface enhanced Raman scattering (SERS) at 1064 nm excitation wavelength and are compared to citrate reduced gold and silver nanoparticles of similar physical sizes and surface properties. After the addition of salts, a strong signal was observed from hollow gold with a LSPR of 650 nm and a weaker, yet observable, signal from HGNs with a LSPR of 775 nm. However, no obvious signals were observed in the case of standard citrate reduced gold, silver or HGNs with a LSPR of 1080 nm. The absorption properties of HGNs were investigated by monitoring their photothermal activity. In this case, different nanoparticle suspensions including citrate reduced gold, silver, and HGNs were illuminated by a continuous laser at 785 nm excitation wavelength and the absorption efficiency of HGNs with a LSPR of 775 nm was calculated to be 0.81% which is more than 5 times higher than the absorption efficiency of citrate reduced gold nanoparticles under similar conditions.
Assuntos
Ouro/química , Nanopartículas Metálicas/química , Nanosferas/química , Absorção , Lasers , Microscopia Eletrônica de Transmissão/métodos , Nanotecnologia/métodos , Fotoquímica/métodos , Fótons , Sais/química , Espalhamento de Radiação , Prata/química , Espectroscopia de Luz Próxima ao Infravermelho/métodos , Análise Espectral Raman/métodos , Ressonância de Plasmônio de Superfície/métodos , Propriedades de SuperfícieRESUMO
Improved positively charged nanoparticles are described to provide a simplified SERS substrate for DNA detection. Complete flocculation of the nanoparticles is prevented due to the controlled analyte induced aggregation. This provides a stable aggregation state which significantly extends the analysis window simplifying DNA detection by SERS.
Assuntos
Corantes/química , Nanopartículas Metálicas/química , Oligonucleotídeos/química , Prata/química , Análise Espectral Raman , Espermina/química , Propriedades de SuperfícieRESUMO
Brighter SERRS nanotags ideal for improved SERRS imaging were prepared by the controlled addition of electrolyte producing a dimer enriched solution, which was incubated with a Raman reporter before being stabilised by a polyethylene glycol (PEG) shell.