Iron-based nanoparticles prepared from yerba mate extract. Synthesis, characterization and use on chromium removal.

Iron-based nanoparticles were synthesized by a rapid method at room temperature using yerba mate (YM) extracts with FeCl3 in different proportions. Materials prepared from green tea (GT) extracts were also synthesized for comparison. These materials were thoroughly characterized by chemical analyses, XRD, magnetization, SEM-EDS, TEM-SAED, FTIR, UV-Vis, Raman, Mössbauer and XANES spectroscopies, and BET area analysis. It was concluded that the products are nonmagnetic iron complexes of the components of the extracts. The applicability of the materials for Cr(VI) (300 µM) removal from aqueous solutions at pH 3 using two Cr(VI):Fe molar ratios (MR), 1:3 and 1:0.5, has been tested. At Cr(VI):Fe MR = 1:3, the best YM materials gave complete Cr(VI) removal after two minutes of contact, similar to that obtained with commercial nanoscale zerovalent iron (N25), with dissolved Fe(II), and with a likewise prepared GT material. At a lower Cr(VI):Fe MR (1:0.5), although Cr(VI) removal was not complete after 20 min of reaction, the YM nanoparticles were more efficient than N25, GT nanoparticles and Fe(II) in solution. The results suggest that an optimal Cr(VI):Fe MR ratio could be reached when using the new YM nanoparticles, able to achieve a complete Cr(VI) reduction, and leaving very low Cr and Fe concentrations in the treated solutions. The rapid preparation of the nanoparticles would allow their use in removal of pollutants in soils and groundwater by direct injection of the mixture of precursors.

Treatment of phenylmercury salts by heterogeneous photocatalysis over TiO(2).

UV/TiO(2) photocatalysis of phenylmercury salts in aqueous solutions has been performed starting from both acetate (C(6)H(5)HgCH(3)CO(2), PMA) and chloride (C(6)H(5)HgCl, PMC) salts, in the presence or the absence of oxygen at acidic pH. Removal of Hg(II) in solution took place with the simultaneous deposit of dark or pale gray solids on the photocatalyst, identified as metallic Hg (when starting from PMA) or mixtures of Hg(0) and Hg(2)Cl(2) (when starting from PMC). Partial mineralization of the organic part of both compounds has also been achieved. Hg(II) removal and mineralization were enhanced in the absence of oxygen. PMA photocatalysis followed a saturation kinetics, going from first order at low concentration to zero order at higher concentrations (>0.5mM). For PMA, reaction was faster at high pH (11) with formation of mixtures of Hg and HgO. Phenol was detected as a product of the reaction in both cases, PMA and PMC, and no formation of dangerous methyl- or ethylmercury species was observed in the first case. A mechanism for the photocatalytic reaction has been proposed. The fact that calomel was found as a deposit when starting from PMC under nitrogen suggests that the mechanism of Hg(II) transformation proceeds through successive one-electron transfer reactions passing by mercurous forms.