RESUMO
A simple strategy was adopted for the preparation of an antimicrobial natural rubber/graphene oxide (NR/GO) composite film modified through the use of zwitterionic polymer brushes. An NR/GO composite film with antibacterial properties was prepared using a water-based solution-casting method. The composited GO was dispersed uniformly in the NR matrix and compensated for mechanical loss in the process of modification. Based on the high bromination activity of α-H in the structure of cis-polyisoprene, the composite films were brominated on the surface through the use of N-bromosuccinimide (NBS) under the irradiation of a 40 W tungsten lamp. Polymerization was carried out on the brominated films using sulfobetaine methacrylate (SBMA) as a monomer via surface-initiated atom transfer radical polymerization (SI-ATRP). The NR/GO composite films modified using polymer brushes (PSBMAs) exhibited 99.99% antimicrobial activity for resistance to Escherichia coli and Staphylococcus aureus. A novel polymer modification strategy for NR composite materials was established effectively, and the enhanced antimicrobial properties expand the application prospects in the medical field.
RESUMO
The intelligent response actuators based on bilayer polymer can deform under the stimulation of temperature, humidity, light, and other external environment, which is the focus of research. However, achieving multiple responses, high deformation, and programmability is still one of the challenges for these actuators. Herein, a nondetachable bilayer structure, polylactic acid-polypropylene carbonate/polyvinyl alcohol-polydopamine (PLA-PPC/PVA-PDA) multiresponse programmable actuator is prepared by a simple scraping film method. Using PLA-PPC as the solvent-driven response layer, the effects of length, thickness, shape, and solvent vapor on the deformation of PLA-PPC/PVA-PDA actuators are studied. Among them, the high curvature of the film stimulated by ethyl acetate (EA) solution is 29.85 cm-1 . Using PVA-PDA as the response layer to water molecules and infrared (IR) light, the bilayer film shows excellent curling performance. Moreover, the dynamic processes of human clothing and biomimetic squid under solvent stimulation, the picture rolling motion under water molecule stimulation, the biomimetic flower blooming and merging under the synergistic of water molecules and IR light, and the deformation process of biomimetic mimosa under the competition between water molecules and IR light are simulated, which broadens the road for the development of intelligent driving materials.
Assuntos
Poliésteres , Álcool de Polivinil , Humanos , Álcool de Polivinil/química , Temperatura , Água , SolventesRESUMO
An environmentally friendly pore size-controlled, superhydrophobic polylactic acid (PLA) membrane was successfully prepared by a simpler freeze solidification phase separation method (FSPS) and solution impregnation, which has application prospects in the field of oil-water separation. The pore size and structure of the membrane were adjusted by different solvent ratios and solution impregnation ratios. The PLA-FSPS membrane after solution impregnation (S-PLA-FSPS) had the characteristics of uniform pore size, superhydrophobicity and super lipophilicity, its surface roughness Ra was 338 nm, and the contact angle to water was 151°. The S-PLA-FSPS membrane was used for the oil-water separation. The membrane oil flux reached 16,084 L·m-2·h-1, and the water separation efficiency was 99.7%, which was much higher than that of other oil-water separation materials. In addition, the S-PLA-FSPS membrane could also be applied for the adsorption and removal of oil slicks and underwater heavy oil. The S-PLA-FSPS membrane has great application potential in the field of oil-water separation.
RESUMO
A practical "grafting-from" strategy is described to grow photochromic polymer brushes bearing spiropyran (SP) functional groups on graphene oxide (GO) surfaces via surface-initiated ring-opening metathesis polymerization (SI-ROMP). The Grubbs II catalyst was fixed on the GO surface, and the norbornene derivatives functionalized using spiropyran were synthesized from this active site via the ROMP method. The results indicated that the spiropyran-modified polymer brushes were obtained on the GO surface in the form of thin films. The solubility of GO modified by spiropyran polymers (GO-SPs) in organic solvents was significantly improved. The GO-SPs exhibited excellent photochromic properties, including fast coloration/decoloration. The modified GO with an isomeric structure was colored in 90 s under ultraviolet irradiation and decolored in 360 s under white light. The fading kinetic rate in the dark was slow and the kinetic attenuation curve followed bi-exponential decay. The GO-SP composite materials took more than 2 h to return to thermodynamically stable forms. The reversible change in the water contact angle reached 8° after continuous cycling with ultraviolet and visible light. GO-SP maintained its photochromic performance and possessed excellent fatigue resistance after more than six successive UV/light cycles. This work describes a practical strategy for the preparation of photochromic polymer brush modified GO composite materials and extends the applications of GO in photochromic materials.
RESUMO
In this study, dendritic polyamine chitosan beads with and without 2-aminomethyl pyridine were facilely prepared and characterized. Compared to CN (without the pyridine function), more adsorption active sites, larger pores, higher nitrogen content, higher specific surface area, and higher strength could be obtained for CNP (with the pyridine function). CNP microspheres afforded a larger adsorption capacity than those obtained by CN for different pH values; further, the uptake amounts of Cu(ii) were 0.84 and 1.12 mmol g-1 for CN and CNP beads, respectively, at pH 5. The CNP microspheres could scavenge Cu(ii) from highly acidic and salty solutions: the maximum simulated uptake amount of 1.93 mmol g-1 at pH 5 could be achieved. Due to the strong bonding ability and weakly basic property of pyridine groups, the adsorption capacity of Cu(ii) at pH 1 was 0.75 mmol g-1 in highly salty solutions, which was comparative to those obtained from the commercial pyridine chelating resin M4195 (Q Cu(II) = 0.78 mmol g-1 at pH 1). In addition, a distinct salt-promotion effect could be observed for CNP beads at both pH 5 and 1. Therefore, the prepared adsorbent CNP beads can have promising potential applications in the selective capturing of heavy metals in complex solutions with higher concentrations of H+ and inorganic salts, such as wastewaters from electroplating liquid and battery industries.