Development of anodic titania nanotubes for application in high sensitivity amperometric glucose and uric acid biosensors.

The purpose of this study was to develop novel nanoscale biosensors using titania nanotubes (TNTs) made by anodization. Titania nanotubes were produced on pure titanium sheets by anodization at room temperature. In this research, the electrolyte composition ethylene glycol 250 mL/NH4F 1.5 g/DI water 20 mL was found to produce the best titania nanotubes array films for application in amperometric biosensors. The amperometric results exhibit an excellent linearity for uric acid (UA) concentrations in the range between 2 and 14 mg/dL, with 23.3 (µA·cm-2)·(mg/dL)-1 UA sensitivity, and a correlation coefficient of 0.993. The glucose biosensor presented a good linear relationship in the lower glucose concentration range between 50 and 125 mg/dL, and the corresponding sensitivity was approximately 249.6 (µA·cm-2)·(100 mg/dL)-1 glucose, with a correlation coefficient of 0.973.

Study of sodium ion selective electrodes and differential structures with anodized indium tin oxide.

The objective of this work is the study and characterization of anodized indium tin oxide (anodized-ITO) as a sodium ion selective electrode and differential structures including a sodium-selective-membrane/anodized-ITO as sensor 1, an anodized-ITO membrane as the contrast sensor 2, and an ITO as the reference electrode. Anodized-ITO was fabricated by anodic oxidation at room temperature, a low cost and simple manufacture process that makes it easy to control the variation in film resistance. The anodized-ITO based on EGFET structure has good linear pH sensitivity, approximately 54.44 mV/pH from pH 2 to pH 12. The proposed sodium electrodes prepared by PVC-COOH, DOS embedding colloid, and complex Na-TFBD and ionophore B12C4, show good sensitivity at 52.48 mV/decade for 10(-4) M to 1 M, and 29.96 mV/decade for 10(-7) M to 10(-4) M. The sodium sensitivity of the differential sodium-sensing device is 58.65 mV/decade between 10(-4) M and 1 M, with a corresponding linearity of 0.998; and 19.17 mV/decade between 10(-5) M and 10(-4) M.