New Insights into the Nature of Co-components and Their Impact on Pd Structure: X-ray Absorption Studies on Toluene Acetoxylation Catalysts.

Co-components are a powerful tool to tune the performance of catalysts, but their nature and their impact on the catalysts is often controversially discussed. In this study X-ray absorption spectroscopy (XAS) was employed to elucidate the nature of co-components and their impact on the catalytic reaction. In anatase-supported Pd-based catalysts for the gas-phase acetoxylation of toluene, less noble co-components (e.g., Mn, Co, and Sb) spread over the support in their oxidic form and changed their valence state on stream. Incorporated atoms such as C or a small part of the Sb affect the electronic structure of Pd. For the noble Au, only a weak interaction with the support and Pd was observed during time on stream. Only XAS at the K-edges together with investigations of the Pd L-edge for a better understanding of the electronic structure, supplemented by STEM for elemental mapping, allow such detailed insights.

Tailoring the synthesis of supported Pd catalysts towards desired structure and size of metal particles.

In a systematic study, the influence of different preparation parameters on phase composition and size of metal crystallites and particles in Pd-Cu/TiO(2) and Pd-Sb/TiO(2) catalyst materials has been explored. Temperature and atmosphere of thermal pretreatment (pure He or 10% H(2)/He), nature of metal precursors (chlorides, nitrates or acetates) as well as of ammonium additives (ammonium sulfate, nitrate, carbonate) and urea were varied with the aim of tailoring the synthesis procedure for the preferential formation of metal particles with similar size and structure as observed recently in active catalysts after long-term equilibration under catalytic reaction conditions in acetoxylation of toluene to benzylacetate. Among the metal precursors and additives, the chloride metal precursors and (NH(4))(2)SO(4) were most suitable. Upon thermal pretreatment of Pd-Sb or Pd-Cu precursors, chloroamine complexes of Pd and Cu are formed, which decompose above 220 degrees C to metallic phases independent of the atmosphere. In He, metallic Pd particles were formed with both the co-components. In H(2)/He flow, Pd-Cu precursors were converted to core-shell particles with a Cu shell and a Pd core, while Sb(1)Pd(1) and Sb(7)Pd(20) alloy phases were formed in the presence of Sb. Metal crystallites of about 40 nm agglomerate to particles of up to 150 nm in He and to even larger size in H(2)/He.