GeSe photovoltaics: doping, interfacial layer and devices.

Germanium selenide (GeSe) bulk crystals, thin films and solar cells are investigated with a focus on acceptor-doping with silver (Ag) and the use of an Sb2Se3 interfacial layer. The Ag-doping of GeSe occurred by a stoichiometric melt growth technique that created Ag-doped GeSe bulk crystals. A combination of capacitance voltage measurements, synchrotron radiation photoemission spectroscopy and surface space-charge calculations indicates that Ag-doping increases the hole density from 5.2 × 1015 cm-3 to 1.9 × 1016 cm-3. The melt-grown material is used as the source for thermally evaporated GeSe films within solar cells. The cell structure with the highest efficiency of 0.260% is FTO/CdS/Sb2Se3/undoped-GeSe/Au, compared with solar cells without the Sb2Se3 interfacial layer or with the Ag-doped GeSe.

Interface-Engineered Ni-Coated CdTe Heterojunction Photocathode for Enhanced Photoelectrochemical Hydrogen Evolution.

Photoelectrochemical (PEC) water splitting for hydrogen production using the CdTe photocathode has attracted much interest due to its excellent sunlight absorption property and energy band structure. This work presents a study of engineered interfacial energetics of CdTe photocathodes by deposition of CdS, TiO2, and Ni layers. A heterostructure CdTe/CdS/TiO2/Ni photocathode was fabricated by depositing a 100-nm n-type CdS layer on a p-type CdTe surface, with 50 nm TiO2 as a protective layer and a 10 nm Ni layer as a co-catalyst. The CdTe/CdS/TiO2/Ni photocathode exhibits a high photocurrent density (Jph) of 8.16 mA/cm2 at 0 V versus reversible hydrogen electrode (VRHE) and a positive-shifted onset potential (Eonset) of 0.70 VRHE for PEC hydrogen evolution under 100 mW/cm2 AM1.5G illumination. We further demonstrate that the CdTe/CdS p-n junction promotes the separation of photogenerated carriers, the TiO2 layer protects the electrode from corrosion, and the Ni catalyst improves the charge transfer across the electrode/electrolyte interface. This work provides new insights for designing noble metal-free photocathodes toward solar hydrogen development.

Impedance spectroscopy of Sb2Se3 photovoltaics consisting of (Sb4Se6)n nanoribbons under light illumination.

Sb2Se3, consisting of one-dimensional (Sb4Se6)n nanoribbons has drawn attention as an intriguing light absorber from the photovoltaics (PVs) research community. However, further research is required on the performance-limiting factors in Sb2Se3 PVs. In this study, we investigated the charge carrier behavior in Sb2Se3 PVs by impedance spectroscopy (IS) under light illumination. (Sb4Se6)n nanoribbons with two different orientations were used to investigate the effect of crystal orientation on the device performance. Regardless of the (Sb4Se6)n orientation, negative capacitance was observed at forward bias, representing a recombination pathway at the TiO2/Sb2Se3 interface. A comparison of the recombination resistances and lifetimes of two different Sb2Se3 PVs showed that a better interface could be formed by placing the (Sb4Se6)n ribbons parallel to the TiO2 layer. Based on these observations, an ideal structure of the Sb2Se3/TiO2 interface is proposed, which will enhance the performance of Sb2Se3 PVs toward its theoretical limit.

Sb2S3 Thin-Film Solar Cells Fabricated from an Antimony Ethyl Xanthate Based Precursor in Air.

The rapidly expanding demand for photovoltaics (PVs) requires stable, quick, and easy to manufacture solar cells based on socioeconomically and ecologically viable earth-abundant resources. Sb2S3 has been a potential candidate for solar PVs and the efficiency of planar Sb2S3 thin-film solar cells has witnessed a reasonable rise from 5.77% in 2014 to 8% in 2022. Herein, the aim is to bring new insight into Sb2S3 solar cell research by investigating how the bulk and surface properties of the Sb2S3 absorber and the current-voltage and deep-level defect characteristics of solar cells based on these films are affected by the ultrasonic spray pyrolysis deposition temperature and the molar ratio of thiourea to SbEX in solution. The properties of the Sb2S3 absorber are characterized by bulk- and surface-sensitive methods. Solar cells are characterized by temperature-dependent current-voltage, external quantum efficiency, and deep-level transient spectroscopy measurements. In this paper, the first thin-film solar cells based on a planar Sb2S3 absorber grown from antimony ethyl xanthate (SbEX) by ultrasonic spray pyrolysis in air are demonstrated. Devices based on the Sb2S3 absorber grown at 200 °C, especially from a solution of thiourea and SbEX in a molar ratio of 4.5, perform the best by virtue of suppressed surface oxidation of Sb2S3, favorable band alignment, Sb-vacancy concentration, a continuous film morphology, and a suitable film thickness of 75 nm, achieving up to 4.1% power conversion efficiency, which is the best efficiency to date for planar Sb2S3 solar cells grown from xanthate-based precursors. Our findings highlight the importance of developing synthesis conditions to achieve the best solar cell device performance for an Sb2S3 absorber layer pertaining to the chosen deposition method, experimental setup, and precursors.

Hybrid photocathode based on a Ni molecular catalyst and Sb2Se3 for solar H2 production.

We report a H2 evolving hybrid photocathode based on Sb2Se3 and a precious metal free molecular catalyst. Through the use of a high surface area TiO2 scaffold, we successfully increased the Ni molecular catalyst loading from 7.08 ± 0.43 to 45.76 ± 0.81 nmol cm-2, achieving photocurrents of 1.3 mA cm-2 at 0 V vs. RHE, which is 81-fold higher than the device without the TiO2 mesoporous layer.

Interrelation of the CdTe Grain Size, Postgrowth Processing, and Window Layer Selection on Solar Cell Performance.

Recent improvements to the CdTe solar cell device structure have focused on replacing the CdS window layer with a more transparent material to reduce parasitic absorption and increase Jsc, as well as incorporating selenium into the absorber layer to achieve a graded band gap. However, altering the CdTe device structure is nontrivial due to the interdependent nature of device processing steps. The choice of the window layer influences the grain structure of the CdTe layer, which in turn can affect the chloride treatment, which itself may contribute to intermixing between the window and absorber layers. This work studies three different device architectures in parallel, allowing for an in-depth comparison of processing conditions for CdTe solar cells grown on CdS, SnO2, and CdSe. Direct replacement of the CdS window layer with a wider band gap SnO2 layer is hindered by poor growth of the absorber, producing highly strained CdTe films and a weak junction. This is alleviated by inserting a CdSe layer between the SnO2 and CdTe, which improves the growth of CdTe and results in a graded CdSexTe1-x absorber layer. For each substrate, the CdTe deposition rate and postgrowth chloride treatment are systematically varied, highlighting the distinct processing requirements of each device structure.

Routes to increase performance for antimony selenide solar cells using inorganic hole transport layers.

Simple compound antimony selenide (Sb2Se3) is a promising emergent light absorber for photovoltaic applications benefiting from its outstanding photoelectric properties. Antimony selenide thin film solar cells however, are limited by low open circuit voltage due to carrier recombination at the metallic back contact interface. In this work, solar cell capacitance simulator (SCAPS) is used to interpret the effect of hole transport layers (HTL), i.e., transition metal oxides NiO and MoO x thin films on Sb2Se3 device characteristics. This reveals the critical role of NiO and MoO x in altering the energy band alignment and increasing device performance by the introduction of a high energy barrier to electrons at the rear absorber/metal interface. Close-space sublimation (CSS) and thermal evaporation (TE) techniques are applied to deposit Sb2Se3 layers in both substrate and superstrate thin film solar cells with NiO and MoO x HTLs incorporated into the device structure. The effect of the HTLs on Sb2Se3 crystallinity and solar cell performance is comprehensively studied. In superstrate device configuration, CSS-based Sb2Se3 solar cells with NiO HTL showed average improvements in open circuit voltage, short circuit current density and power conversion efficiency of 12%, 41%, and 42%, respectively, over the standard devices. Similarly, using a NiO HTL in TE-based Sb2Se3 devices improved open circuit voltage, short circuit current density and power conversion efficiency by 39%, 68%, and 92%, respectively.

Microscopic Analysis of Interdiffusion and Void Formation in CdTe(1-x)Sex and CdTe Layers.

The use of CdSe layers has recently emerged as a route to improving CdTe photovoltaics through the formation of a CdTe(1-x)Sex (CST) phase. However, the extent of the Se diffusion and the influence it has on the CdTe grain structure has not been widely investigated. In this study, we used transmission electron microscopy (TEM), energy-dispersive X-ray spectroscopy (EDS), and electron backscatter diffraction (EBSD) to investigate the impact of growing CdTe layers on three different window layer structures CdS, CdSe, and CdS/CdSe. We demonstrate that extensive intermixing occurs between CdS, CdSe, and CdTe layers resulting in large voids forming at the front interface, which will degrade device performance. The use of CdS/CdSe bilayer structures leads to the formation of a parasitic CdS(1-x)Sex phase. Following removal of CdS from the cell structure, effective CdTe and CdSe intermixing was achieved. However, the use of sputtered CdSe had limited success in producing Se grading in CST.

Density Functional Theory and Experimental Determination of Band Gaps and Lattice Parameters in Kesterite Cu2ZnSn(SxSe1-x)4.

The structures and band gaps of copper-zinc-tin selenosulfides (CZTSSe) are investigated for a range of anion compositions through experimental analysis and complementary first-principles simulations. The band gap was found to be extremely sensitive to the Sn-anion bond length, with an almost linear correlation with the average Sn-anion bond length in the mixed anion phase Cu2ZnSn(SxSe1-x)4. Therefore, an accurate prediction of band gaps using first-principles methods requires the accurate reproduction of the experimental bond lengths. This is challenging for many widely used approaches that are suitable for large supercells. The HSE06 functional was found to predict the structure and band gap in good agreement with the experiment but is computationally expensive for large supercells. It was shown that a geometry optimization with the MS2 meta-GGA functional followed by a single point calculation of electronic properties using HSE06 is a reasonable compromise for modeling larger supercells that are often unavoidable in the study of point and extended defects.

How Oxygen Exposure Improves the Back Contact and Performance of Antimony Selenide Solar Cells.

The improvement of antimony selenide solar cells by short-term air exposure is explained using complementary cell and material studies. We demonstrate that exposure to air yields a relative efficiency improvement of n-type Sb2Se3 solar cells of ca. 10% by oxidation of the back surface and a reduction in the back contact barrier height (measured by J-V-T) from 320 to 280 meV. X-ray photoelectron spectroscopy (XPS) measurements of the back surface reveal that during 5 days in air, Sb2O3 content at the sample surface increased by 27%, leaving a more Se-rich Sb2Se3 film along with a 4% increase in elemental Se. Conversely, exposure to 5 days of vacuum resulted in a loss of Se from the Sb2Se3 film, which increased the back contact barrier height to 370 meV. Inclusion of a thermally evaporated thin film of Sb2O3 and Se at the back of the Sb2Se3 absorber achieved a peak solar cell efficiency of 5.87%. These results demonstrate the importance of a Se-rich back surface for high-efficiency devices and the positive effects of an ultrathin antimony oxide layer. This study reveals a possible role of back contact etching in exposing a beneficial back surface and provides a route to increasing device efficiency.

Evidence for Self-healing Benign Grain Boundaries and a Highly Defective Sb2Se3-CdS Interfacial Layer in Sb2Se3 Thin-Film Photovoltaics.

The crystal structure of Sb2Se3 gives rise to unique properties that cannot otherwise be achieved with conventional thin-film photovoltaic materials, such as CdTe or Cu(In,Ga)Se2. It has previously been proposed that grain boundaries can be made benign provided only the weak van der Waals forces between the (Sb4Se6)n ribbons are disrupted. Here, it is shown that non-radiative recombination is suppressed even for grain boundaries cutting across the (Sb4Se6)n ribbons. This is due to a remarkable self-healing process, whereby atoms at the grain boundary can relax to remove any electronic defect states within the band gap. Grain boundaries can, however, impede charge transport due to the fact that carriers have a higher mobility along the (Sb4Se6)n ribbons. Because of the ribbon misorientation, certain grain boundaries can effectively block charge collection. Furthermore, it is shown that CdS is not a suitable emitter to partner Sb2Se3 due to Sb and Se interdiffusion. As a result, a highly defective Sb2Se3 interfacial layer is formed that potentially reduces device efficiency through interface recombination.

Benchmark performance of low-cost Sb2Se3 photocathodes for unassisted solar overall water splitting.

Determining cost-effective semiconductors exhibiting desirable properties for commercial photoelectrochemical water splitting remains a challenge. Herein, we report a Sb2Se3 semiconductor that satisfies most requirements for an ideal high-performance photoelectrode, including a small band gap and favourable cost, optoelectronic properties, processability, and photocorrosion stability. Strong anisotropy, a major issue for Sb2Se3, is resolved by suppressing growth kinetics via close space sublimation to obtain high-quality compact thin films with favourable crystallographic orientation. The Sb2Se3 photocathode exhibits a high photocurrent density of almost 30 mA cm-2 at 0 V against the reversible hydrogen electrode, the highest value so far. We demonstrate unassisted solar overall water splitting by combining the optimised Sb2Se3 photocathode with a BiVO4 photoanode, achieving a solar-to-hydrogen efficiency of 1.5% with stability over 10 h under simulated 1 sun conditions employing a broad range of solar fluxes. Low-cost Sb2Se3 can thus be an attractive breakthrough material for commercial solar fuel production.

GeSe: Optical Spectroscopy and Theoretical Study of a van der Waals Solar Absorber.

The van der Waals material GeSe is a potential solar absorber, but its optoelectronic properties are not yet fully understood. Here, through a combined theoretical and experimental approach, the optoelectronic and structural properties of GeSe are determined. A fundamental absorption onset of 1.30 eV is found at room temperature, close to the optimum value according to the Shockley-Queisser detailed balance limit, in contrast to previous reports of an indirect fundamental transition of 1.10 eV. The measured absorption spectra and first-principles joint density of states are mutually consistent, both exhibiting an additional distinct onset ∼0.3 eV above the fundamental absorption edge. The band gap values obtained from first-principles calculations converge, as the level of theory and corresponding computational cost increases, to 1.33 eV from the quasiparticle self-consistent GW method, including the solution to the Bethe-Salpeter equation. This agrees with the 0 K value determined from temperature-dependent optical absorption measurements. Relaxed structures based on hybrid functionals reveal a direct fundamental transition in contrast to previous reports. The optoelectronic properties of GeSe are resolved with the system described as a direct semiconductor with a 1.30 eV room temperature band gap. The high level of agreement between experiment and theory encourages the application of this computational methodology to other van der Waals materials.

Band Alignments, Band Gap, Core Levels, and Valence Band States in Cu3BiS3 for Photovoltaics.

The earth-abundant semiconductor Cu3BiS3 (CBS) exhibits promising photovoltaic properties and is often considered analogous to the solar absorbers copper indium gallium diselenide (CIGS) and copper zinc tin sulfide (CZTS) despite few device reports. The extent to which this is justifiable is explored via a thorough X-ray photoemission spectroscopy (XPS) analysis: spanning core levels, ionization potential, work function, surface contamination, cleaning, band alignment, and valence-band density of states. The XPS analysis overcomes and addresses the shortcomings of prior XPS studies of this material. Temperature-dependent absorption spectra determine a 1.2 eV direct band gap at room temperature; the widely reported 1.4-1.5 eV band gap is attributed to weak transitions from the low density of states of the topmost valence band previously being undetected. Density functional theory HSE06 + SOC calculations determine the band structure, optical transitions, and well-fitted absorption and Raman spectra. Valence band XPS spectra and model calculations find the CBS bonding to be superficially similar to CIGS and CZTS, but the Bi3+ cations (and formally occupied Bi 6s orbital) have fundamental impacts: giving a low ionization potential (4.98 eV), suggesting that the CdS window layer favored for CIGS and CZTS gives detrimental band alignment and should be rejected in favor of a better aligned material in order for CBS devices to progress.

Self-Catalyzed CdTe Wires.

CdTe wires have been fabricated via a catalyst free method using the industrially scalable physical vapor deposition technique close space sublimation. Wire growth was shown to be highly dependent on surface roughness and deposition pressure, with only low roughness surfaces being capable of producing wires. Growth of wires is highly (111) oriented and is inferred to occur via a vapor-solid-solid growth mechanism, wherein a CdTe seed particle acts to template the growth. Such seed particles are visible as wire caps and have been characterized via energy dispersive X-ray analysis to establish they are single phase CdTe, hence validating the self-catalysation route. Cathodoluminescence analysis demonstrates that CdTe wires exhibited a much lower level of recombination when compared to a planar CdTe film, which is highly beneficial for semiconductor applications.