Fine cutting edge shaped Bi2O3rods/reduced graphene oxide (RGO) composite for supercapacitor and visible-light photocatalytic applications.

Bi2O3 rods/RGO composite has been synthesized by a simple precipitation and calcination method. The crystallnity, structural, and morphological features were studied by X-ray diffraction (XRD), field-emission scanning electron microscopy (FE-SEM), and high resolution transmission electron microscopy (HR-TEM) techniques. The supercapacitor behavior was studied using cyclic voltammetry, galvanostatic charge discharge and impedance analysis, respectively. The Bi2O3 rods/RGO nanocomposite exhibits a maximum specific capacitance of 1041Fg-1 at a current density of 2Ag-1. The photocatalytic activity of Bi2O3 rods/RGO composite was evaluated by photocatalytic degradation of methylene blue (MB) dye under visible-light irradiation. The enhancement of photocatalytic properties of Bi2O3 rods/RGO composite attributed to the synergistic effect between Bi2O3 rods and graphene sheets which effectively prevents recombination of the photogenerated electron-hole pairs in Bi2O3 rods. The present study provides a new approach in improving the performance of Bi2O3 rods/RGO composite in energy and environmental applications.

Facile synthesis of novel CaFe2O4/g-C3N4 nanocomposites for degradation of methylene blue under visible-light irradiation.

Hybrid organic/inorganic nanocomposites comprised of calcium ferrite (CaFe2O4) and graphitic carbon nitride (g-C3N4) were prepared via a simple two-step process. The hybridized CaFe2O4/g-C3N4 heterostructure was characterized by a variety of techniques, including X-ray diffraction (XRD), Fourier transform-infrared spectroscopy (FT-IR), UV-vis diffuse reflectance spectroscopy (UV-vis DRS), scanning electron microscopy (SEM), transmission electron microscopy (TEM), energy dispersive analysis of X-rays (EDS), X-ray photoelectron spectroscopy (XPS), photoluminescence spectroscopy, electrochemical impedance spectroscopy (EIS), and photoelectrochemical studies. Photocatalytic activity of the prepared samples was evaluated against degradation of methylene blue (MB) under visible-light irradiation. The photocatalytic activity of CaFe2O4 30%/g-C3N4 nanocomposite, as optimum photocatalyst, for degradation of MB was superior to the pure CaFe2O4 and g-C3N4 samples. It was demonstrated that the photogenerated holes and superoxide ion radicals were the two main reactive species towards the photocatalytic degradation of MB over the nanocomposite. Based on the experimental results, a possible photocatalytic mechanism for the MB degradation over the nanocomposite was proposed. This work may provide some inspiration for the fabrication of spinel ferrites with efficient photocatalytic performance.