Extended Shear Deformation of the Immiscible Cu-Nb Alloy Resulting in Nanostructuring and Oxygen Ingress with Enhancement in Mechanical Properties.

Deformation processing of immiscible systems is observed to disrupt thermodynamic equilibrium, often resulting in nonequilibrium microstructures. The microstructural changes including nanostructuring, hierarchical distribution of phases, localized solute supersaturation, and oxygen ingress result from high-strain extended deformation, causing a significant change in mechanical properties. Because of the dynamic evolution of the material under large strain shear load, a detailed understanding of the transformation pathway has not been established. Additionally, the influence of these microstructural changes on mechanical properties is also not well characterized. Here, an immiscible Cu-4 at. % Nb alloy is subjected to a high-strain shear deformation (∼200); the deformation-induced changes in the morphology, crystal structure, and composition of Cu and Nb phases as a function of total strain are characterized using transmission electron microscopy and atom probe tomography. Furthermore, a multimodal experiment-guided computational approach is used to depict the initiation of deformation by an increase in misorientation boundaries by crystal plasticity-based grain misorientation modeling (strain ∼0.6). Then, co-deformation and nanolamination of Cu and Nb are envisaged by a finite element method-based computational fluid dynamic model with strain ranging from 10 to 200. Finally, the experimentally observed amorphization of the severely sheared supersaturated Cu-Nb-O phase was validated using the first principle-based simulation using density functional theory while highlighting the influence of oxygen ingress during deformation. Furthermore, the nanocrystalline microstructure shows a >2-fold increase in hardness and compressive yield strength of the alloy, elucidating the potential of deformation processing to obtain high-strength low-alloyed metals. Our approach presents a step-by-step evolution of a microstructure in an immiscible alloy undergoing severe shear deformation, which is broadly applicable to materials processing based on friction stir, extrusion, rolling, and surface shear deformation under wear and can be directly applied to understanding material behavior during these processes.

Unraveling the Role of Interfaces on the Spall Failure of Cu/Ta Multilayered Systems.

Molecular dynamics (MD) simulations are carried out to investigate the effects of the type and spacing of FCC/BCC interfaces on the deformation and spall behavior. The simulations are carried out using model Cu/Ta multilayers with six different types of interfaces. The results suggest that interface type can significantly affect the structure and intensity of the incoming shock wave, change the activated slip systems, alter dislocation slip and twinning behavior, affect where and how voids are nucleated during spallation and the resulting spall strength. Moreover, the above aspects are significantly affected by the interface spacing. A transition from homogeneous to heterogeneous dislocation nucleation occurs as the interface spacing is decreased to 6 nm. Depending on interface type and spacing, damage (voids) nucleation and spall failure is observed to occur not only at the Cu/Ta interfaces, but also in the weaker Cu layer interior, or even in the stronger Ta layer interior, although different mechanisms underlie each of these three distinct failure modes. These findings point to the fact that, depending on the combination of interface type and spacing, interfaces can lead to both strengthening and weakening of the Cu/Ta multilayered microstructures.

In-situ atomic-scale observation of irradiation-induced void formation.

The formation of voids in an irradiated material significantly degrades its physical and mechanical properties. Void nucleation and growth involve discrete atomic-scale processes that, unfortunately, are not yet well understood due to the lack of direct experimental examination. Here we report an in-situ atomic-scale observation of the nucleation and growth of voids in hexagonal close-packed magnesium under electron irradiation. The voids are found to first grow into a plate-like shape, followed by a gradual transition to a nearly equiaxial geometry. Using atomistic simulations, we show that the initial growth in length is controlled by slow nucleation kinetics of vacancy layers on basal facets and anisotropic vacancy diffusivity. The subsequent thickness growth is driven by thermodynamics to reduce surface energy. These experiments represent unprecedented resolution and characterization of void nucleation and growth under irradiation, and might help with understanding the irradiation damage of other hexagonal close-packed materials.