Optical cooling of a Yb-doped alumino-phosphosilicate fiber in air by -250†mK.

Recent progress in the fabrication of Yb-doped silicate fibers with low concentration quenching and low background absorption loss has led to the demonstration of anti-Stokes-fluorescence cooling in several aluminosilicate compositions. This breakthrough is critical to combat deleterious thermal effects due to the quantum defect in fiber lasers and amplifiers. Since cooling efficiencies remain low (1-2.7%), it is paramount to engineer compositions that improve this metric. We report a silica fiber with a core glass heavily doped with aluminum and phosphorus that sets, to our knowledge, a few new records. This few-mode fiber (16-µm core) was cooled in air by -0.25 K from room temperature with ∼0.5 W of 1040-nm power. The measured cooling efficiency is 3.3% at low pump power and 2.8% at the power that produced maximum cooling. The critical quenching concentration inferred from the measured dependence of cooling on pump power and careful calibration of the pump absorption and saturation is 79 wt.%. The inferred background absorption loss is 15 dB/km. Together with the fiber's average Yb concentration of 4.2 wt.%, these metrics rank among the best reported in a silica glass.

High-efficiency radiation-balanced Yb-doped silica fiber laser with 200-mW output.

The focus of this study was the development of a second generation of fiber lasers internally cooled by anti-Stokes fluorescence. The laser consisted of a length of a single-mode fiber spliced to fiber Bragg gratings to form the optical resonator. The fiber was single-moded at the pump (1040 nm) and signal (1064 nm) wavelengths. Its core was heavily doped with Yb, in the initial form of CaF2 nanoparticles, and co-doped with Al to reduce quenching and improve the cooling efficiency. After optimizing the fiber length (4.1 m) and output-coupler reflectivity (3.3%), the fiber laser exhibited a threshold of 160 mW, an optical efficiency of 56.8%, and a radiation-balanced output power (no net heat generation) of 192 mW. On all three metrics, this performance is significantly better than the only previously reported radiation-balanced fiber laser, which is even more meaningful given that the small size of the single-mode fiber core (7.8-µm diameter). At the maximum output power (∼2 W), the average fiber temperature was still barely above room temperature (428 mK). This work demonstrates that with anti-Stokes pumping, it is possible to induce significant gain and energy storage in a small-core Yb-doped fiber while keeping the fiber cool.

Anti-Stokes fluorescence cooling of nanoparticle-doped silica fibers.

The first observation of cooling by anti-Stokes pumping in nanoparticle-doped silica fibers is reported. Four Yb-doped fibers fabricated using conventional modified chemical vapor deposition (MCVD) techniques were evaluated, namely, an aluminosilicate fiber and three fibers in which the Yb ions were encapsulated in CaF2, SrF2, or BaF2 nanoparticles. The nanoparticles, which oxidize during preform processing, provide a modified chemical environment for the Yb3+ ions that is beneficial to cooling. When pumped at the near-optimum cooling wavelength of 1040 nm at atmospheric pressure, the fibers experienced a maximum measured temperature drop of 20.5 mK (aluminosilicate fiber), 26.2 mK (CaF2 fiber), and 16.7 mK (SrF2 fiber). The BaF2 fiber did not cool but warmed slightly. The three fibers that cooled had a cooling efficiency comparable to that of the best previously reported Yb-doped silica fiber that cooled. Data analysis shows that this efficiency is explained by the fibers' high critical quenching concentration and low residual absorptive loss (linked to sub-ppm OH contamination). This study demonstrates the large untapped potential of nanoparticle doping in the current search for silicate compositions that produce optimum anti-Stokes cooling.

Localised structuring of metal-semiconductor cores in silica clad fibres using laser-driven thermal gradients.

The molten core drawing method allows scalable fabrication of novel core fibres with kilometre lengths. With metal and semiconducting components combined in a glass-clad fibre, CO2 laser irradiation was used to write localised structures in the core materials. Thermal gradients in axial and transverse directions allowed the controlled introduction, segregation and chemical reaction of metal components within an initially pure silicon core, and restructuring of heterogeneous material. Gold and tin longitudinal electrode fabrication, segregation of GaSb and Si into parallel layers, and Al doping of a GaSb core were demonstrated. Gold was introduced into Si fibres to purify the core or weld an exposed fibre core to a Si wafer. Ga and Sb introduced from opposite ends of a silicon fibre reacted to form III-V GaSb within the Group IV Si host, as confirmed by structural and chemical analysis and room temperature photoluminescence.