The Influence of a Binder in a Composite Electrode: The Case Study of Vanadyl Phosphate in Aqueous Electrolyte.

Layered VOPO4·2H2O is synthesized by the sonochemical method. An X-ray powder diffraction is used to examine the crystal structure, while scanning electron microscopy is used to reveal the morphology of the powder. The crystal structure refinement is performed in the P4/nmmZ space group. The electrochemical intercalation of several cations (Na+, Mg2+, Ca2+, and Al3+) in saturated nitrate aqueous solutions is investigated. The most notable reversible activity is found for the cycling in aluminium nitrate aqueous solution in the voltage range from -0.1 to 0.8 V vs. SCE. During the preparation of the electrode, it is observed that the structure is prone to changes that have not been recorded in the literature so far. Namely, the use of conventional binder PVDF in NMP solution deteriorates the structure and lowers the powder's crystallinity, while the use of Nafion solution causes the rearrangement of the atoms in a new crystal form that can be described in the monoclinic P21/c space group. Consequently, these structural changes affect electrochemical performances. The observed differences in electrochemical performances are a result of structural rearrangements.

Crystal Structure and Electrical Properties of Ruthenium-Substituted Calcium Copper Titanate.

This paper reports a detailed study of crystal structure and dielectric properties of ruthenium-substituted calcium-copper titanates (CaCu3Ti4-xRuxO12, CCTRO). A series of three samples with different stoichiometry was prepared: CaCu3Ti4-xRuxO12, x = 0, 1 and 4, abbreviated as CCTO, CCT3RO and CCRO, respectively. A detailed structural analysis of CCTRO samples was done by the Rietveld refinement of XRPD data. The results show that, regardless of whether Ti4+ or Ru4+ ions are placed in B crystallographic position in AA'3B4O12 (CaCu3Ti4-xRuxO12) unit cell, the crystal structure remains cubic with Im3¯ symmetry. Slight increases in the unit cell parameters, cell volume and interatomic distances indicate that Ru4+ ions with larger ionic radii (0.62 Å) than Ti4+ (0.605 Å) are incorporated in the CaCu3Ti4-xRuxO12 crystal lattice. The structural investigations were confirmed using TEM, HRTEM and ADF/STEM analyses, including EDXS elemental mapping. The effect of Ru atoms share in CaCu3Ti4-xRuxO12 samples on their electrical properties was determined by impedance and dielectric measurements. Results of dielectric measurements indicate that one atom of ruthenium per CaCu3Ti4-xRuxO12 unit cell transforms dielectric CCTO into conductive CCT3RO while preserving cubic crystal structure. Our findings about CCTO and CCT3RO ceramics promote them as ideal tandem to overcome the problem of stress on dielectric-electrode interfaces in capacitors.