The Effect of Incorporation of 0.5 %wt. Silica Nanoparticles on the Micro Shear Bond Strength of a Resin Modified Glass Ionomer Cement.

STATEMENT OF THE PROBLEM: The clinical success of glass ionomer restorations depends on the strength of resin-modified glass ionomer (RMGI) cement bonding to dentin and there is limited information available regarding the bond strength of resin modified glass ionomers containing silica nanoparticles to dental structures. PURPOSE: The aim of this study was to compare the microshear bond strength (µSBS) of RMGI with and without silica (SiO2) nanoparticles to dentin of permanent teeth. MATERIALS AND METHOD: In this experimental study, the occlusal surfaces of 30 freshly extracted intact third molars were ground to expose the flat dentin and after conditioning with 20% poly acrylic acid, were randomly assigned to two main groups (n=15). The first group was filled with RMGI (Fuji II LC, GC) and the second group was filled with RMGI plus 0.5%wt. silica nanoparticles. Then, each main group was divided into three subgroups, and then stored in an incubator at 37 oC with 100% humidity for 1, 7, and 30 days. The µSBS test was performed using a universal testing machine (1 mm/min). The data were analyzed by t-test, repeated measures ANOVA and Tukey test (p< 0.05). RESULTS: There were no statistically significant differences between the mean µSBS of the groups with and without nanoparticles along the different storage periods (p> 0.05). There was significant difference in µSBS values among the three different storage periods in all the tested materials (p< 0.05). CONCLUSION: Incorporation of 0.5 %wt. silica nanoparticles did not compromise the µSBS of Fuji II LC RMGI to dentin.

Dual function of proanthocyanidins as both MMP inhibitor and crosslinker in dentin biomodification: A literature review.

Proanthocyanidin, a natural phytochemical bioactive agent, simultaneously can silence the activity of dentinal proteases and crosslink the collagen matrix; both of these phenomena would be the fundamentals for bio-stability of resin-dentin interface which is essential for a promising adhesive dentistry. This review provides an overview of the data developed by different groups of researchers and highlighted topics are proanthocyanidin chemistry, natural resources and the unique interactions between proanthocyanidincollagen and proanthocyanidin-MMPs in dentin. Besides, clinical applications of proanthocyanidin in the form of proanthocyanidin-containing adhesives, preconditioners and etchants have been reviewed. One hundred and twelve studies have been published in peer-reviewed journals from 1981 to 2017, all were comprised in this review, some of them have been actually proven to be promising from clinical point of view and others need further assessment before their adoption as clinically practicable protocols.

Bonding Durability of Four Adhesive Systems.

OBJECTIVES: This study aimed to compare the durability of four adhesive systems by assessing their microtensile bond strength (MTBS) and microleakage during six months of water storage. MATERIALS AND METHODS: A total of 128 human third molars were used. The adhesives tested were Scotch Bond Multipurpose (SBMP), Single Bond (SB), Clearfil-SE bond (CSEB), and All-Bond SE (ABSE). After sample preparation for MTBS testing, the microspecimens were subjected to microtensile tester after one day and six months of water storage. For microleakage evaluation, facial and lingual class V cavities were prepared and restored with composite. After thermocycling, microleakage was evaluated. Bond strength values were subjected to one-way ANOVA and Tamhane's test, and the microleakage data were analyzed by the Kruskal-Wallis, Dunn, Mann Whitney and Wilcoxon tests (P<0.05). RESULTS: Single Bond yielded the highest and ABSE yielded the lowest bond strength at one day and six months. Short-term bond strength of SBMP and CSEB was similar. After six months, a significant decrease in bond strength was observed in ABSE and SBMP groups. At one day, ABSE showed the highest microleakage at the occlusal margin; however, at the gingival margin, there was no significant difference among groups. Long-term microleakage of all groups at the occlusal margins was similar, whilst gingival margins of SBMP and SB showed significantly higher microleakage. CONCLUSION: The highest MTBS and favorable sealability were obtained by Clearfil SE bond. Water storage had no effect on microleakage of self-etch adhesives at the gingival margin or MTBS of CSEB and SB.