Lattice size induced moment formation on isolated Fe atoms in nanocrystalline Nb.

Measurements of the local susceptibility and 3d spin relaxation rate for single Fe impurities embedded in a nanocrystalline Nb host indicates the emergence of a local moment on Fe at and below a critical size of 11 nm. Our ab initio electronic structure calculations show that the moment formation occurs due to Stoner enhancement arising from a size dependent lattice expansion and a consequent shift in the Fermi level. We also show that a size-induced positive host spin polarization of the Nb-4d band electrons strongly influences the fluctuation rate of the Fe moment.

Nanostructuring of InP surface by low-energy ion beam irradiation.

The InP nanodots of size 55 to 100 nm and height 25 to 30 nm have been synthesized by low-energy Ar+-ion irradiation with different ion energies. Sizes and size distributions of the dots strongly depend on growth conditions. Rapid thermal annealed (RTA) of the patterned surface shows cluster formation for annealing temperature 400 degrees C and above. Raman investigations reveal optical phonon softening due to correlation length shortening and broadening of the optical modes from the patterned surface. The softening is due to confinement of phonons in embedded nanocrystallites within the patterned surface along with surface nanodots, and broadening is attributed to their size distributions, which increases with increase in ion energy. The lattice damage recovery is observed from the patterned surface subjected to RTA, which exhibits upward shift of the LO and TO phonons due to the presence of complex interfacial stress, associated with the removal of crystal defects with RTA.

Defect induced magnetism in highly oriented pyrolytic graphite: bulk magnetization and 19F hyperfine interaction studies.

We have made bulk and local investigations on defect induced magnetism in highly oriented pyrolytic graphite (HOPG) irradiated with a 40 MeV carbon beam. The local magnetic response of irradiated HOPG was studied by measuring the hyperfine field of recoil implanted (19)F using γ-ray time differential perturbed angular distribution (TDPAD) measurements. While the bulk magnetic properties of the irradiated sample show features characteristic of room temperature ferromagnetism, the hyperfine field data reflect enhanced paramagnetism with no indication of long range magnetic ordering. The experimental studies are further supported by ab initio density functional calculations. We believe that the ferromagnetic response in irradiated HOPG arises mostly from defect induced magnetic moments of carbon atoms in the near surface region, while those deep inside the host matrix remain paramagnetic.