Assessing the surface roughness of a posterior resin composite: effect of surface sealing.

This study assessed the in vitro influence of surface sealing on the surface roughness of a posterior resin composite before and after toothbrushing. Thirty specimens (13 mm diameter x 1 mm high) were fabricated from Filtek-P60 resin composite and randomly assigned to three groups (n = 10): a non-sealed control and two groups sealed with one of the tested materials-a surface-penetrating sealant (Protect-it!-PI) and a one bottle adhesive system (Single Bond-SB). The samples were subjected to a surface roughness reading to determine the initial roughness, then submitted to simulated toothbrushing with 35,600 cycles for 100 minutes. Specimens were then cleaned and a post-abrasion surface roughness reading accomplished. Means (microm), recorded before (B) and after (A) toothbrushing, and standard deviations were: Control--(B): 0.032 (+/- 0.005), (A): 0.054 (+/- 0.005); PI-(B): 0.034 (+/- 0.005), (A): 0.060 (+/- 0.034); SB (B): 0.031 (+/- 0.004), (A): 0.047 (+/- 0.007). Data were tabulated and submitted to two-way ANOVA. No statistically significant difference was observed when the control and experimental groups were compared. However, a significant difference (p < 0.05) was found between the measurements performed before and after toothbrushing. Based on these results, it may be concluded that using either a surface penetrating sealant or a one bottle adhesive system did not provide the optimization of superficial integrity. The use of a dentifrice and toothbrush resulted in significant alterations to the surface smoothness of the resin composite.

Avaliação in vitro da microinfiltração marginal e análise da fenda marginal cervical através da microscopia eletrônica de varredura, em restaurações de classe V de resina composta. Efeito dos sistemas adesivos e técnica de preparo cavitário / In vitro evaluation of marginal microleakage and cervical gap using SEM in class V restaurations with composite resin. Effects bonding systems and dental cavity techniques

O objetivo deste trabalho foi avaliar a formação de fendas marginais cervicais através da microscopia eletrônica de varredura, assim como, a microinfiltração marginal em preparos de classe V. foram utilizadas duas técnicas de preparo: P1 utilizando fresa carbide no 245 e P2 que utilizou o jato de ar abrasivo Mach 4.0 (80psi de pressão, 27 µm de tamanho de partícula). O tamanho das cavidades foi padronizado com 1,5 mm de profundidade, 2,0 mm de altura e 3,0 mm de largura. Os materiais utilizados foram: G1 ­Optibond solo Plus, G2 ­ Prime & BondNT e G3 ­ Scotchbond Multiuso Plus (grupo controle), a resina composta Point 4 utilizada para restaurar as cavidades foi padronizada para todas as restaurações. Foram utilizados 42 dentes molares hígidos divididos em 3 grupos de 14 cada, utilizando a face vestibular e lingual sendo que os preparos mostraram a margem oclusal em esmalte e a margem cervical em cemento/dentina. Após as restaurações serem confeccionadas foram armazenadas em água deionizada durante 24 horas, para posteriormente realizar os procedimentos de acabamento e polimento, a seguir os dentes foram isolados com araldite e esmalte para unha e submetidos a testes de ciclagem térmico (400 ciclos) e imediatamente imersos numa solução de nitrato de prata, durante 2 horas, removidos, lavados e colocados numa solução fotoreveladora durante 16 horas. Nessas condições os dentes foram limpos e seccionados no sentido mésio/distal obtendo duas metades as quais por sua vez foram seccionadas no sentido vestíbulo lingual dividindo as restaurações pela metade. Assim, uma metade da restauração foi avaliada através da lupa esteroscópica para observar a microinfiltração e a outra metade preparada e metalizada para ser avaliada através da microscopia eletrônica de varredura. A análise estatística aplicada aos resultados permite concluir que: 1) o preparo cavitário com jato de ar abrasivo promove em média maior amplitude de fenda; 2) os sistemas adesivos não conseguem impedir a formação de fendas; 3) a interação preparo com fresa e sistema adesivo Optibond Solo Plus mostrou o melhor comportamento, com uma amplitude de fenda marginal cervical de 0,84 µm; a interação jato de ar abrasivo e o sistema adesivo Scotchbond Multiuso Plus mostrou 6,36 µm de amplitude média de fenda marginal; 4) na região oclusal o sistema adesivo Optibond Solo Plus mostrou tendência de comportamento inferior quando comparado com os sistemas adesivos Scotchbond Multiuso Plus e Prime & Bond NT que foram eficazes no controle da microinfiltração marginal; 5) na região cervical, o sistema Optibond Solo Plus se mostrou eficiente no controle da microinfiltração marginal, no entanto, os sistemas Scotchbond Multiuso Plus e Prime & Bond NT mostraram valores críticos de microinfiltração e similares entre si. De acordo com estas considerações, maiores pesquisas deverão ser feitas para comprovar a real efetividade dos sistemas adesivos com carga

The aim of this study was to evaluate the formation of cervical gap with SEM, and the marginal microleakage in cavities class V. There were used two techniques for the preparations: P1 using a carbide # 245 and P2 using abrasive air Mach 4.0 (80 psi of preasure, 27µm measurement of the particle). The measurements of the cavities were standardized in 1.5mm of deepness, 2,0mm of highness and 3,0mm of lengthiness. The materials used were: G1 Optibond Solo Plus, G2 Prime & Bond NT and G3 Scotchbond Multipurpose Plus (control group), it was used the composite Point 4 as the restorative material for all cavities. Forty-two healthy molars, divided in three groups of 14 each one, were used. Cavities were prepared in the buccal and lingual faces, its occlusal margin was in enamel and its cervical margin was in dentin/cement. After that, finishing and polishing was made. Teeth were isolated with araldite and nail varnish and thermocycled (400 times). The preparations were dyed with silver nitrate for two hours. Preparations were stored in a photo developing solution for 16 hours. After that time teeth were cleaned and cut (buccal/lingual) Half of the preparation was observed in a stereoscopic microscope and the other half in a SEM. Results: 1.Preparations with abrasive air had a bigger gap; 2.Bonding systems do not eliminate the formation of gaps; 3.Best results were found in the group prepared with bur and the adhesive Optibond Solo Plus, with a cervical gap 0,84nm, and in the other hand Scotchbond Multiuso Plus showed marginal gaps of 6,36nm; 4.In the occlusal margin Optibond Solo Plus had more microleakage tha Scotchbond Multipurpose Plus and Prime & Bond NT.; 5. In the cervical margin, Optibond Solo Plus had good behavior controlling the marginal microleakage, compared with Scotchbond Multipurpose Plus and Prime & Bond that had similar leakage between them. According to this study there must be made more research to prove the real effectiveness of bonding systems with fillers

Avaliação in vitro da microinfiltração marginal e análise da fenda marginal cervical através da microscopia eletrônica de varredura, em restaurações de classe V de resina composta. Efeito dos sistemas adesivos e técnica de preparo cavitário / In vitro evaluation of marginal microleakage and cervical gap using SEM in class V restaurations with compositee resin. Effects bonding systems and dental cavity techniques

O objetivo deste trabalho foi avaliar a formação de fendas marginais cervicais através da microscopia eletrônica de varredura, assim como, a microinfiltração marginal em preparos de classe V, foram utilizadas duas técnicas de preparo: P1 utilizando fresa carbide nº245 e P2 que utilizou o jato de ar abrasivo Mach 4.0 (80psi de pressão, 27 um de tamanho de partícula). O tamanho das cavidades foi padronizado com 1,5 mm de profundidade, 2,0 mm de altura e 3,0 mm de largura. Os materiais utilizados foram: G1 - Optibond solo Plus, G2 - Prime & Bond NT e G3 - Scotchbond Multiuso Plus (grupo controle), a resina composta Point 4 utilizada para restaurar as cavidades foi padronizada para todas as restaurações. Foram utilizados 42 dentes molares hígidos divididos em 3 grupos de 14 cada, utilizando a face vestibular e lingual sendo que os preparos mostraram a margem oclusal em esmalte e a margem cervical em cemento/dentina...