Anti-Candida activity and biocompatibility of silver nanoparticles associated with denture glaze: a new approach to the management of denture stomatitis.

The association of silver nanoparticles (AgNps) to sealant agent Palaseal® can be a promising alternative for complete denture wearers who may develop denture stomatitis (DS). The study aimed to evaluate the anti-Candida and biocompatible potential of silver nanoparticles synthesized by three routes associated with denture glaze to prevent and/or treat oral candidiasis. Surface acrylic resin specimens were treated with different associations of glaze with AgNps (VER+AgUV, VER+AgTurk and VER+AgGm). As controls, specimens were treated with glaze+nystatin (VER+Nyst), glaze only (VER) or submerged in PBS (PBS). Afterwards, Candida albicans biofilm was developed for 24 h, 15 d and 30 d. Subsequently, the biofilm was quantified by CFU/mL, XTT assay and confocal laser scanning microscopy. Fibroblasts were submitted to conditioned medium with the same associations for 24, 48 and 72 h and LIVE/DEAD® viability test was carried out. Regardless of the period, there was a significant reduction (p < 0.01) of viable fungal cells load, as well as inhibition of fungal metabolic activity, in specimens treated with glaze+AgNps associations, compared to VER and PBS. The anti-Candida effects of the associations were similar to the VER+Nyst group, with emphasis on VER+AgGm, which showed the highest percentage values of non-viable fungal cells maintained over time. The associations did not prove toxicity to fibroblasts. The AgNps exerted antimicrobial activity against C. albicans biofilms and are biocompatible. The most effective results were achieved with the association of glaze+silver nanoparticles synthesized by the green chemistry method (AgGm), proving to be an innovative alternative in the management of DS.

Silver nanoparticles in denture adhesive: An antimicrobial approach against Candida albicans.

OBJECTIVE: To evaluate the antimicrobial potential of silver nanoparticles (Ag NPs) synthesized using three different routes (ultraviolet light, Turkevich, and green chemistry method using Glycine max extract) associated with COREGA® denture powder adhesive. METHODS: Heat-cured acrylic resin specimens were treated with different Ag NPs associated with the adhesive (AD + Ag UV, AD + Ag Turk, and AD + Ag Gm groups). As controls, the specimens were treated with a combination of adhesive and nystatin (AD + Nyst group), only adhesive (AD group), or submerged on the surface of the specimens (PBS group). After the treatments, biofilms of C. albicans developed for 3, 6, and 12 h on the specimen surfaces. The biofilm was quantified using colony-forming units per milliliter, colorimetric assay, and confocal laser scanning microscopy. RESULTS: Regardless of the period, we observed an inhibition of fungal load and a reduction in metabolic activity and biofilm mass in the resin specimens treated with the combinations AD/Ag NPs, compared to AD and PBS. The antimicrobial action of the AD + Turk and AD + Ag Gm groups was similar than that for the AD + Nyst group in all periods and viability tests, except for the biofilm mass (12 h). CONCLUSIONS: The COREGA® adhesive with Ag NPs, mainly those synthesized using the Turkevich and Glycine max methods, showed excellent antimicrobial activity against C. albicans biofilms, maintained for up to 12 h. CLINICAL SIGNIFICANCE: The association of Ag NPs to the adhesive can add preventive or therapeutic effects against denture stomatitis, to this prosthetic material.

Effects of a Biocomplex Formed by Two Scaffold Biomaterials, Hydroxyapatite/Tricalcium Phosphate Ceramic and Fibrin Biopolymer, with Photobiomodulation, on Bone Repair.

There are several treatment methods available for bone repair, although the effectiveness becomes limited in cases of large defects. The objective of this pre-clinical protocol was to evaluate the grafting of hydroxyapatite/tricalcium phosphate (BCP) ceramic biomaterial (B; QualyBone BCP®, QualyLive, Amadora, Portugal) together with the heterologous fibrin biopolymer (FB; CEVAP/UNESP Botucatu, Brazil) and with photobiomodulation (PBM; Laserpulse®, Ibramed, Amparo, Brazil) in the repair process of bone defects. Fifty-six rats were randomly divided into four groups of seven animals each: the biomaterial group (G1/B), the biomaterial plus FB group (G2/BFB); the biomaterial plus PBM group (G3/B + PBM), and the biomaterial plus FB plus PBM group (G4/BFB + PBM). After anesthesia, a critical defect was performed in the center of the rats' parietal bones, then filled and treated according to their respective groups. The rats were euthanized at 14 and 42 postoperative days. Histomorphologically, at 42 days, the G4/BFB + PBM group showed a more advanced maturation transition, with more organized and mature bone areas forming concentric lamellae. A birefringence analysis of collagen fibers also showed a more advanced degree of maturation for the G4/BFB + PBM group. In the comparison between the groups, in the two experimental periods (14 and 42 days), in relation to the percentage of formation of new bone tissue, a significant difference was found between all groups (G1/B (5.42 ± 1.12; 21.49 ± 4.74), G2/BFB (5.00 ± 0.94; 21.77 ± 2.83), G3/B + PBM (12.65 ± 1.78; 29.29 ± 2.93), and G4/BFB + PBM (12.65 ± 2.32; 31.38 ± 2.89)). It was concluded that the use of PBM with low-level laser therapy (LLLT) positively interfered in the repair process of bone defects previously filled with the biocomplex formed by the heterologous fibrin biopolymer associated with the synthetic ceramic of hydroxyapatite and tricalcium phosphate.

Development of novel Ti-Mo-Mn alloys for biomedical applications.

Due to excellent biocompatibility and corrosion resistance, the application of titanium alloys in orthopedic and dental implants has been increasing since the 1970s. However, the elasticity of these alloys as measured by their Young's modulus is still about two to four times higher than that of human cortical bone. The most widely used titanium alloy for biomedical applications is Ti-6Al-4V, however, previous studies have shown that the vanadium used in this alloy causes allergic reactions in human tissue and aluminum, also used in the alloy, has been associated with neurological disorders. To solve this problem, new titanium alloys without the presence of these elements and with the addition of different elements, usually beta-stabilizers, are being developed. Manganese is a strong candidate as an alloying element for the development of new beta-type titanium alloys, due to its abundance and low cytotoxicity. In this study, Ti-10Mo-5Mn, Ti-15Mo-2.5Mn and Ti-15Mo-5Mn alloys were prepared in an arc furnace, which resulted in an alloy structure clearly showing the predominance of the beta phase with a body-centered cubic crystalline structure. The observed microstructure confirmed the results on the structural characterization of alloys. Measurement of the indirect cytotoxicity of the alloys showed that the extracts of the studied alloys are not cytotoxic for fibroblastic cells.

Influence of curing accelerator for cyanoacrylate glues on physical properties of adhesive resins

The objectives of this study were to evaluate the effect of a curing accelerator (CA) on the ultimate tensile strength (UTS) and degree of conversion (DC) of two adhesive systems, Single Bond and Clearfil SE Bond, as well as to identify the composition of the CA hour-glass adhesive resin samples with a cross sectional area of 0,8 mm² at the "neck" were tested in tension using a Universal Testing Machine. Fourier transform infrared spectroscopy (FTIR) was used to analyse thin films of each adhesive resin. All samples were stored in the dark for 24 hours before they were tested. During the UTS and FTIR analyses, the contact of the CA with samples was either avoided or not. The gas chromatography mass spectrocopy (GC-MS) and the nuclear magnetic resonance (NMR) analyses determined the molecular weight and structure of the CA. UTS and DC were analyzed by ANOVA and Tukey's test at 95% of confidence. The use of the CA did not affect the UST (p=0.5996) but increased the DC of the samples (p<0.0001). The compound identified by GC-MS and NMR was N-dimethyl p-toluidine. The application of CA in microtensile bond strength methodology raises concern regarding its effects on poorly polymerized adhesive systems.