RESUMO
In adhesive joints used in several industrial applications, the adherends' bonding is made using an adhesive, which is usually an epoxy resin. However, since these adhesives are derived from petroleum fractions, they are harmful to the environment, due to the pollutants produced both during their manufacture and subsequent use. Thus, in recent years, effective steps have been made to replace these adhesives with ecological (green) ones. The present work focuses on the study of aluminum A1050 joints bonded with a green adhesive; the study also involves the electrochemical anodization method applied to adherends for nano-functionalization. The nanostructured aluminum adherends allow the formation of an expanded surface area for adhesion, compared to the non-anodized adherends. For comparison reasons, two different adhesives (Araldite LY1564 and Green Super Sap) were used. In addition, for the same reasons, both anodized and non-anodized aluminum adherends were joined with both types of adhesives. The lap joints were subsequently tested under both shear-tension and three-point bending conditions. The major findings were that aluminum A1050 anodization in all cases resulted in shear strength enhancement of the joints, while joints with both aluminum anodized and non-anodized adherends and bonded with the eco-friendly adhesive showed a superior shear behavior as compared to the respective joints bonded with Araldite adhesive.
RESUMO
The response of fiber-reinforced polymer composites to an externally applied mechanical excitation is closely related to the microscopic stress transfer mechanisms taking place in the fiber-matrix interphasial region. In particular, in the case of viscoelastic responses, these mechanisms are time dependent. Defining the interphase thickness as the maximum radial distance from the fiber surface where a specific matrix property is affected by the fiber presence, it is important to study its variation with time. In the present investigation, the stress relaxation behavior of a glass fiber-reinforced polymer (GFRP) under flexural conditions was studied. Next, applying the hybrid viscoelastic interphase model (HVIM), developed by the first author, the interphase modulus and interphase thickness were both evaluated, and their variation with time during the stress relaxation test was plotted. It was found that the interphase modulus decreases with the radial distance, being always higher than the bulk matrix modulus. In addition, the interphase thickness increases with time, showing that during stress relaxation, fiber-matrix debonding takes place. Finally, the effect of fiber interaction on the interphase modulus was found. It is observed that fiber interaction depends on both the fiber-matrix degree of adhesion as well as the fiber volume fraction and the time-dependent interphase modulus.
RESUMO
The hypothesis of the present research is that by altering the substrate topography and/or stiffness to make it biomimetic, we can modulate cells behavior. Substrates with similar surface chemistry and varying stiffnesses and topographies were prepared. Bulk PCL and CNTs-reinforced PCL composites were manufactured by solvent casting method and electrospinning and further processed to obtain tunable moduli of elasticity in the range of few MPa. To ensure the same chemical profile for the substrates, a protein coating was added. Substrate topography and properties were investigated. Further on, the feedback of Wharton's Jelly Umbilical Cord Mesenchymal Stem Cells to substrates characteristics was investigated. Solvent casting scaffolds displayed superior mechanical properties compared to the corresponding electrospun films. However, the biomimetic fibrous texture of the electrospun substrates induced improved feedback of the cells with respect to their viability and proliferation. Cells' adhesion and differentiation was remarkably pronounced on solvent casting substrates compared to the electrospun substrates. Soft substates improved cells multiplication and migration, while stiff substrates induced differentiation into bone cells. Aspects related to the key factors and the ideal properties of substrates and microenvironments were clarified, aiming towards the deep understanding of the required optimum biomimetic features of biomaterials.
RESUMO
The goal of the present investigation was to find a solution to crucial engineering aspects related to the elaboration of multi-layered tissue-biomimicking composites. 3D printing technology was used to manufacture single-layered and gradient multi-layered 3D porous scaffolds made of poly-lactic acid (PLA). The scaffolds manufacturing process was optimized after adjusting key printing parameters. The scaffolds with 60 µm side length (square-shaped pores) showed increased stiffness values comparing to the other specimens. A silicone adhesive has been further used to join biomedical titanium plates, and the PLA scaffolds; in addition, titania nanotubes (TNTs were produced on the titanium for improved adhesion. The titanium-PLA scaffold single lap joints were evaluated in micro-tensile testing. The electrochemical processing of the titanium surface resulted in a 248% increase of the ultimate strength in the overlap area for dry specimens and 40% increase for specimens immersed in simulated body fluid. Finally, the biocompatibility of the produced scaffolds was evaluated with primary cell populations obtained after isolation from bone residual tissue. The manufactured scaffolds present promising features for applications in orthopedic implantology and are worth further.
RESUMO
The effect of an electric field within specific intensity limits on the activity of human cells has been previously investigated. However, there are a considerable number of factors that influence the in vitro development of cell populations. In biocompatibility studies, the nature of the substrate and its topography are decisive in osteoblasts bone cells development. Further on, electrical field stimulation may activate biochemical paths that contribute to a faster, more effective self-adjustment and proliferation of specific cell types on various nanosubstrates. Within the present research, an electrical stimulation device has been manufactured and optimum values of parameters that led to enhanced osteoblasts activity, with respect to the alkaline phosphatase and total protein levels, have been found. Homogeneous electric field distribution induced by a highly organized titanium dioxide nanotubes substrate had an optimum effect on cell response. Specific substrate topography in combination with appropriate electrical stimulation enhanced osteoblasts bone cells capacity to self-adjust the levels of their specific biomarkers. The findings are of importance in the future design and development of new advanced orthopaedic materials for hard tissue replacement.
Assuntos
Materiais Biocompatíveis/farmacologia , Osteoblastos/efeitos dos fármacos , Osteoblastos/fisiologia , Osteócitos/efeitos dos fármacos , Osteócitos/fisiologia , Fosfatase Alcalina/metabolismo , Osso e Ossos/efeitos dos fármacos , Osso e Ossos/metabolismo , Diferenciação Celular/efeitos dos fármacos , Proliferação de Células/efeitos dos fármacos , Células Cultivadas , Estimulação Elétrica/métodos , Feminino , Humanos , Pessoa de Meia-Idade , Nanotubos , Osteoblastos/metabolismo , Osteócitos/metabolismo , Propriedades de Superfície/efeitos dos fármacos , Titânio/farmacologiaRESUMO
Titanium and its alloys are the most popular biomaterials replacing hard tissues in implant surgeries. Clinicians are generally pleased by titanium mechanical properties and non-toxicity performances; on the other hand, there have been reported several cases of titanium implantation failure, phenomenon explained sometimes as "non adherence of human tissue to the metallic surface." Yet, researchers reported that titanium surfaces are favorable for osteoblasts adhesion. Therefore, titanium integration into the human body remains an unsolved problem. In the present study, biocompatibility tests were performed on titanium and TiO(2) nanotubes substrates, involving human bone marrow cells. The combination of a newly developed analytical model based on the hybrid interphase concept, applicable to systems consisting of inert materials when in contact with living tissues, together with experimental results, confirmed previous research studies and lead to the conclusion that osteoblasts adhere efficiently to titanium surfaces. However, the present results suggest that osteoblasts strong anchorage at the very first moment of their contact with the metallic material leads to their apoptosis. It is most probable that in several cases this is the reason of failed implantation surgeries involving titanium.