Influence of Polymorphism on the Magnetic Properties of Co5TeO8 Spinel.

This study presents the influence of polymorphism on the magnetic properties of Co5TeO8. This compound with a spinel-like structure [Co2]A[Co3Te]BO8 was synthesized into two polymorphs: one disordered within a cubic Fd3̅m structure, where Co2+ and Te6+ ions are randomly distributed on the octahedral B sites [the disordered polymorph can also be presented as an inverse spinel of the formula Co(Co1.5Te0.5)O4] and the other ordered with a cubic P4332 structure where Co2+ and Te6+ ions are ordered on the B sites. The macroscopic magnetic measurements showed that both polymorphs present a ferrimagnetic ordering, below ∼40 K, and a second transition is also observed at 27 K for the ordered polymorph. Neutron powder diffraction data between room temperature and 1.7 K showed as well the presence of short-range magnetic ordered clusters, which appears for both polymorphs below 200 K. At lower temperature, these short-range orders are transformed into long-range ferrimagnetic orders. Below TC = 40 K, the colinear ferrimagnetic structure of the disordered polymorph is described with the I41/am'd' space group. The ordered polymorph undergoes an incommensurate ferrimagnetic spiral spin ordering below TC1 = 45 K, followed by a second magnetic phase transition at TC2 = 27 K. This last transition is associated with the emergence of an additional ferrimagnetic component and an abrupt change in the magnitude of the magnetic propagation vector k = [0, 0, γ] from γ = 0.086 at T = 30 K to γ ≈ 0.14 in the range between 27 and 1.7 K. The magnetic symmetry of the ordered polymorph is described with the P43(00γ)0 magnetic superspace group. We evidenced that the ordering of Co2+/Te6+ on the B sites changes all of the Co-Co and Co-O distances and thus all JAB, JAA, and JBB exchange interactions, between the A and B sites, which are able to stabilize the incommensurate spin modulation in the ordered polymorph.

Universal A-Cation Splitting in LiNbO3-Type Structure Driven by Intrapositional Multivalent Coupling.

Understanding the electric dipole switching in multiferroic materials requires deep insight of the atomic-scale local structure evolution to reveal the ferroelectric mechanism, which remains unclear and lacks a solid experimental indicator in high-pressure prepared LiNbO3-type polar magnets. Here, we report the discovery of Zn-ion splitting in LiNbO3-type Zn2FeNbO6 established by multiple diffraction techniques. The coexistence of a high-temperature paraelectric-like phase in the polar Zn2FeNbO6 lattice motivated us to revisit other high-pressure prepared LiNbO3-type A2BB'O6 compounds. The A-site atomic splitting (∼1.0-1.2 Šbetween the split-atom pair) in B/B'-mixed Zn2FeTaO6 and O/N-mixed ZnTaO2N is verified by both powder X-ray diffraction structural refinements and high angle annular dark field scanning transmission electron microscopy images, but is absent in single-B-site ZnSnO3. Theoretical calculations are in good agreement with experimental results and suggest that this kind of A-site splitting also exists in the B-site mixed Mn-analogues, Mn2FeMO6 (M = Nb, Ta) and anion-mixed MnTaO2N, where the smaller A-site splitting (∼0.2 Šatomic displacement) is attributed to magnetic interactions and bonding between A and B cations. These findings reveal universal A-site splitting in LiNbO3-type structures with mixed multivalent B/B', or anionic sites, and the splitting-atomic displacement can be strongly suppressed by magnetic interactions and/or hybridization of valence bands between d electrons of the A- and B-site cations.

Pb2MnTeO6 Double Perovskite: An Antipolar Anti-ferromagnet.

Pb2MnTeO6, a new double perovskite, was synthesized. Its crystal structure was determined by synchrotron X-ray and powder neutron diffraction. Pb2MnTeO6 is monoclinic (I2/m) at room temperature with a regular arrangement of all the cations in their polyhedra. However, when the temperature is lowered to ∼120 K it undergoes a phase transition from I2/m to C2/c structure. This transition is accompanied by a displacement of the Pb atoms from the center of their polyhedra due to the 6s(2) lone-pair electrons, together with a surprising off-centering of Mn(2+) (d(5)) magnetic cations. This strong first-order phase transition is also evidenced by specific heat, dielectric, Raman, and infrared spectroscopy measurements. The magnetic characterizations indicate an anti-ferromagnetic (AFM) order below TN ≈ 20 K; analysis of powder neutron diffraction data confirms the magnetic structure with propagation vector k = (0 1 0) and collinear AFM spins. The observed jump in dielectric permittivity near ∼150 K implies possible anti-ferroelectric behavior; however, the absence of switching suggests that Pb2MnTeO6 can only be antipolar. First-principle calculations confirmed that the crystal and magnetic structures determined are locally stable and that anti-ferroelectric switching is unlikely to be observed in Pb2MnTeO6.

Low-Temperature Cationic Rearrangement in a Bulk Metal Oxide.

Cationic rearrangement is a compelling strategy for producing desirable physical properties by atomic-scale manipulation. However, activating ionic diffusion typically requires high temperature, and in some cases also high pressure in bulk oxide materials. Herein, we present the cationic rearrangement in bulk Mn2 FeMoO6 at unparalleled low temperatures of 150-300 (o) C. The irreversible ionic motion at ambient pressure, as evidenced by real-time powder synchrotron X-ray and neutron diffraction, and second harmonic generation, leads to a transition from a Ni3 TeO6 -type to an ordered-ilmenite structure, and dramatic changes of the electrical and magnetic properties. This work demonstrates a remarkable cationic rearrangement, with corresponding large changes in the physical properties in a bulk oxide at unprecedented low temperatures.

Magnetic Interactions in the Double Perovskites R2NiMnO6 (R = Tb, Ho, Er, Tm) Investigated by Neutron Diffraction.

R2NiMnO6 (R = Tb, Ho, Er, Tm) perovskites have been prepared by soft-chemistry techniques followed by high oxygen-pressure treatments; they have been investigated by X-ray diffraction, neutron powder diffraction (NPD), and magnetic measurements. In all cases the crystal structure is defined in the monoclinic P21/n space group, with an almost complete order between Ni(2+) and Mn(4+) cations in the octahedral perovskite sublattice. The low temperature NPD data and the macroscopic magnetic measurements indicate that all the compounds are ferrimagnetic, with a net magnetic moment different from zero and a distinct alignment of Ni and Mn spins depending on the nature of the rare-earth cation. The magnetic structures are different from the one previously reported for La2NiMnO6, with a ferromagnetic structure involving Mn(4+) and Ni(2+) moments. This spin alignment can be rationalized taking into account the Goodenough-Kanamori rules. The magnetic ordering temperature (TCM) decreases abruptly as the size of the rare earth decreases, since TCM is mainly influenced by the superexchange interaction between Ni(2+) and Mn(4+) (Ni(2+)-O-Mn(4+) angle) and this angle decreases with the rare-earth size. The rare-earth magnetic moments participate in the magnetic structures immediately below TCM.

Hole doping and structural transformation in CsTl1-xHgxCl3.

CsTlCl(3) and CsTlF(3) perovskites have been theoretically predicted to be superconductors when properly hole-doped. Both compounds have been previously prepared as pure compounds: CsTlCl(3) in a tetragonal (I4/m) and a cubic (Fm3̅m) perovskite polymorph and CsTlF(3) as a cubic perovskite (Fm3̅m). In this work, substitution of Tl in CsTlCl(3) with Hg is reported, in an attempt to hole-dope the system and induce superconductivity. The whole series CsTl(1-x)HgxCl(3) (x = 0.0, 0.1, 0.2, 0.4, 0.6, and 0.8) was prepared. CsTl(0.9)Hg(0.1)Cl(3) is tetragonal as the more stable phase of CsTlCl(3). However, CsTl(0.8)Hg(0.2)Cl(3) is already cubic with the space group Fm3̅m and with two different positions for Tl(+) and Tl(3+). For x = 0.4 and 0.5, solid solutions could not be formed. For x ≥ 0.6, the samples are primitive cubic perovskites with one crystallographic position for Tl(+), Tl(3+), and Hg(2+). All of the samples formed are insulating, and there is no signature of superconductivity. X-ray absorption spectroscopy indicates that all of the samples have a mixed-valence state of Tl(+) and Tl(3+). Raman spectroscopy shows the presence of the active Tl-Cl-Tl stretching mode over the whole series and the intensity of the Tl-Cl-Hg mode increases with increasing Hg content. First-principle calculations confirmed that the phases are insulators in their ground state and that Hg is not a good dopant in the search for superconductivity in this system.

Giant magnetoresistance in the half-metallic double-perovskite ferrimagnet Mn2FeReO6.

The first transition-metal-only double perovskite compound, Mn(2+) 2 Fe(3+) Re(5+) O6 , with 17 unpaired d electrons displays ferrimagnetic ordering up to 520 K and a giant positive magnetoresistance of up to 220 % at 5 K and 8 T. These properties result from the ferrimagnetically coupled Fe and Re sublattice and are affected by a two-to-one magnetic-structure transition of the Mn sublattice when a magnetic field is applied. Theoretical calculations indicate that the half-metallic state can be mainly attributed to the spin polarization of the Fe and Re sites.

Designing polar and magnetic oxides: Zn2FeTaO6--in search of multiferroics.

Polar oxides are technically of great interest but difficult to prepare. Our recent discoveries predicted that polar oxides can be synthesized in the corundum-derivative A2BB'O6 family with unusually small cations at the A-site and a d(0) electron configuration ion at B'-site. When magnetic transition-metal ions are incorporated more interesting polar magnetic oxides can form. In this work we experimentally verified this prediction and prepared LiNbO3 (LN)-type polar magnetic Zn2FeTaO6 via high pressure and temperature synthesis. The crystal structure analysis indicates highly distorted ZnO6 and (Fe/Ta)O6 octahedra, and an estimated spontaneous polarization (PS) of ∼50 µC/cm(2) along the c-axis was obtained from point charge model calculations. Zn2Fe(3+)Ta(5+)O6 has a lower magnetic transition temperature (TN ∼ 22 K) than the Mn2FeTaO6 analogue but is less conductive. The dielectric and polarization measurements indicate a potentially switchable component.

Magnetic-structure-stabilized polarization in an above-room-temperature ferrimagnet.

Above-room-temperature polar magnets are of interest due to their practical applications in spintronics. Here we present a strategy to design high-temperature polar magnetic oxides in the corundum-derived A2BB'O6 family, exemplified by the non-centrosymmetric (R3) Ni3TeO6-type Mn(2+)2Fe(3+)Mo(5+)O6, which shows strong ferrimagnetic ordering with TC = 337 K and demonstrates structural polarization without any ions with (n-1)d(10)ns(0), d(0), or stereoactive lone-pair electrons. Density functional theory calculations confirm the experimental results and suggest that the energy of the magnetically ordered structure, based on the Ni3TeO6 prototype, is significantly lower than that of any related structure, and accounts for the spontaneous polarization (68 µC cm(-2)) and non-centrosymmetry confirmed directly by second harmonic generation. These results motivate new directions in the search for practical magnetoelectric/multiferroic materials.

Unraveling the Most Relevant Features for the Design of Iridium Mixed Oxides with High Activity and Durability for the Oxygen Evolution Reaction in Acidic Media.

Proton exchange membrane water electrolysis (PEMWE) is the technology of choice for the large-scale production of green hydrogen from renewable energy. Current PEMWEs utilize large amounts of critical raw materials such as iridium and platinum in the anode and cathode electrodes, respectively. In addition to its high cost, the use of Ir-based catalysts may represent a critical bottleneck for the large-scale production of PEM electrolyzers since iridium is a very expensive, scarce, and ill-distributed element. Replacing iridium from PEM anodes is a challenging matter since Ir-oxides are the only materials with sufficient stability under the highly oxidant environment of the anode reaction. One of the current strategies aiming to reduce Ir content is the design of advanced Ir-mixed oxides, in which the introduction of cations in different crystallographic sites can help to engineer the Ir active sites with certain characteristics, that is, environment, coordination, distances, oxidation state, etc. This strategy comes with its own problems, since most mixed oxides lack stability during the OER in acidic electrolyte, suffering severe structural reconstruction, which may lead to surfaces with catalytic activity and durability different from that of the original mixed oxide. Only after understanding such a reconstruction process would it be possible to design durable and stable Ir-based catalysts for the OER. In this Perspective, we highlight the most successful strategies to design Ir mixed oxides for the OER in acidic electrolyte and discuss the most promising lines of evolution in the field.

Active and durable R2MnRuO7 pyrochlores with low Ru content for acidic oxygen evolution.

The production of green hydrogen in water electrolyzers is limited by the oxygen evolution reaction (OER). State-of-the-art electrocatalysts are based on Ir. Ru electrocatalysts are a suitable alternative provided their performance is improved. Here we show that low-Ru-content pyrochlores (R2MnRuO7, R = Y, Tb and Dy) display high activity and durability for the OER in acidic media. Y2MnRuO7 is the most stable catalyst, displaying 1.5 V at 10 mA cm-2 for 40 h, or 5000 cycles up to 1.7 V. Computational and experimental results show that the high performance is owed to Ru sites embedded in RuMnOx surface layers. A water electrolyser with Y2MnRuO7 (with only 0.2 mgRu cm-2) reaches 1 A cm-2 at 1.75 V, remaining stable at 200 mA cm-2 for more than 24 h. These results encourage further investigation on Ru catalysts in which a partial replacement of Ru by inexpensive cations can enhance the OER performance.

Highly active and stable OER electrocatalysts derived from Sr2MIrO6 for proton exchange membrane water electrolyzers.

Proton exchange membrane water electrolysis is a promising technology to produce green hydrogen from renewables, as it can efficiently achieve high current densities. Lowering iridium amount in oxygen evolution reaction electrocatalysts is critical for achieving cost-effective production of green hydrogen. In this work, we develop catalysts from Ir double perovskites. Sr2CaIrO6 achieves 10 mA cm-2 at only 1.48 V. The surface of the perovskite reconstructs when immersed in an acidic electrolyte and during the first catalytic cycles, resulting in a stable surface conformed by short-range order edge-sharing IrO6 octahedra arranged in an open structure responsible for the high performance. A proton exchange membrane water electrolysis cell is developed with Sr2CaIrO6 as anode and low Ir loading (0.4 mgIr cm-2). The cell achieves 2.40 V at 6 A cm-2 (overload) and no loss in performance at a constant 2 A cm-2 (nominal load). Thus, reducing Ir use without compromising efficiency and lifetime.

Stabilization and study of SrFe(1-x)Mn(x)O2 oxides with infinite-layer structure.

A series of layered oxides of nominal composition SrFe(1-x)Mn(x)O(2) (x = 0, 0.1, 0.2, 0.3) have been prepared by the reduction of three-dimensional perovskites SrFe(1-x)Mn(x)O(3-δ) with CaH(2) under mild temperature conditions of 583 K for 2 days. The samples with x = 0, 0.1, and 0.2 exhibit an infinite-layer crystal structure where all of the apical O atoms have been selectively removed upon reduction. A selected sample (x = 0.2) has been studied by neutron powder diffraction (NPD) and X-ray absorption spectroscopy. Both techniques indicate that Fe and Mn adopt a divalent oxidation state, although Fe(2+) ions are under tensile stress whereas Mn(2+) ions undergo compressive stress in the structure. The unit-cell parameters progressively evolve from a = 3.9932(4) Å and c = 3.4790(4) Å for x = 0 to a = 4.00861(15) Å and c = 3.46769(16) Å for x = 0.2; the cell volume presents an expansion across the series from V = 55.47(1) to 55.722(4) Å(3) for x = 0 and 0.2, respectively, because of the larger effective ionic radius of Mn(2+) versus Fe(2+) in four-fold coordination. Attempts to prepare Mn-rich compositions beyond x = 0.2 were unsuccessful. For SrFe(0.8)Mn(0.2)O(2), the magnetic properties indicate a strong magnetic coupling between Fe(2+) and Mn(2+) magnetic moments, with an antiferromagnetic temperature T(N) above room temperature, between 453 and 523 K, according to temperature-dependent NPD data. The NPD data include Bragg reflections of magnetic origin, accounted for with a propagation vector k = ((1)/(2), (1)/(2), (1)/(2)). A G-type antiferromagnetic structure was modeled with magnetic moments at the Fe/Mn position. The refined ordered magnetic moment at this position is 1.71(3) µ(B)/f.u. at 295 K. This is an extraordinary example where Mn(2+) and Fe(2+) ions are stabilized in a square-planar oxygen coordination within an infinite-layer structure. The layered SrFe(1-x)Mn(x)O(2) oxides are kinetically stable at room temperature, but in air at ~170 °C, they reoxidize and form the perovskites SrFe(1-x)Mn(x)O(3-δ). A cubic phase is obtained upon reoxidation of the layered compound, whereas the starting precursor SrFeO(2.875) (Sr(8)Fe(8)O(23)) was a tetragonal superstructure of perovskite.

Effect of the Thermal Treatment of Fe/N/C Catalysts for the Oxygen Reduction Reaction Synthesized by Pyrolysis of Covalent Organic Frameworks.

A nitrogen-containing covalent organic framework obtained from the polymerization of 1,3-dicyanobenzene has been used as a starting material for the synthesis of Fe/N/C catalysts for the oxygen reduction reaction (ORR). In this work we report the effect of the thermal treatments on the nature and catalytic properties of the catalysts obtained after the thermal treatments. After the first thermal treatment, the catalysts obtained contain metallic iron and iron carbide particles, along with a minority fraction of inorganic FeN x sites. After acid leaching and a second thermal treatment, FeN x sites remain in the catalysts, along with a minor fraction of graphite-wrapped Fe3C particles. Both catalysts display high activity for the ORR, with the catalyst subjected to acid leaching and a second thermal treatment, 2HT-1,3DCB, displaying higher ORR activity and a lower production of H2O2. This observation suggests that iron particles, such as Fe3C, display ORR activity but mainly toward the two-electron pathway. On the contrary, FeN x ensembles promote the ORR via the four-electron pathway, that is, via H2O formation.

Effects of support and reaction pressure for the synthesis of dimethyl ether over heteropolyacid catalysts.

Dimethyl ether (DME) is an advanced second-generation biofuel produced via methanol dehydration over acid catalysts such as γ-Al2O3, at temperatures above 240 °C and pressures above 10 bar. Heteropolyacids such as tungstosilicic acid (HSiW) are Brønsted acid catalysts with higher DME production rates than γ-Al2O3, especially at low temperatures (140-180 °C). In this work, we show that the performance of supported HSiW for the production of DME is strongly affected by the nature of the support. TiO2 and SiO2 supported HSiW display the highest DME production rates of ca. 50 mmolDME/h/gHSiW. Characterization of acid sites via 1H-NMR, NH3-isotherms and NH3-adsrobed DRIFT reveal that HSiW/X have Brønsted acid sites, HSiW/TiO2 showing more and stronger sites, being the most active catalyst. Methanol production increases with T until 200 °C where a rapid decay in methanol conversion is observed. This effect is not irreversible, and methanol conversion increases to ca. 90% by increasing reaction pressure to 10 bar, with DME being the only product detected at all reaction conditions studied in this work. The loss of catalytic activity with the increasing temperature and its increasing with reaction pressure accounts to the degree of contribution of the pseudo-liquid catalysis under the reaction conditions studied.

La1.5Sr0.5NiMn0.5Ru0.5O6 Double Perovskite with Enhanced ORR/OER Bifunctional Catalytic Activity.

Perovskites (ABO3) with transition metals in active B sites are considered alternative catalysts for the water oxidation to oxygen through the oxygen evolution reaction (OER) and for the oxygen reduction through the oxygen reduction reaction (ORR) back to water. We have synthesized a double perovskite (A2BB'O6) with different cations in A, B, and B' sites, namely, (La1.5Sr0.5)A(Ni0.5Mn0.5)B(Ni0.5Ru0.5)B'O6 (LSNMR), which displays an outstanding OER/ORR bifunctional performance. The composition and structure of the oxide has been determined by powder X-ray diffraction, powder neutron diffraction, and transmission electron microscopy to be monoclinic with the space group P21/ n and with cationic ordering between the ions in the B and B' sites. X-ray absorption near-edge spectroscopy suggests that LSNMR presents a configuration of ∼Ni2+, ∼Mn4+, and ∼Ru5+. This bifunctional catalyst is endowed with high ORR and OER activities in alkaline media, with a remarkable bifunctional index value of ∼0.83 V (the difference between the potentials measured at -1 mA cm-2 for the ORR and +10 mA cm-2 for the OER). The ORR onset potential ( Eonset) of 0.94 V is among the best reported to date in alkaline media for ORR-active perovskites. The ORR mass activity of LSNMR is 1.1 A g-1 at 0.9 V and 7.3 A g-1 at 0.8 V. Furthermore, LSNMR is stable in a wide potential window down to 0.05 V. The OER potential to achieve a current density of 10 mA cm-2 is 1.66 V. Density functional theory calculations demonstrate that the high ORR/OER activity of LSNMR is related to the presence of active Mn sites for the ORR- and Ru-active sites for the OER by virtue of the high symmetry of the respective reaction steps on those sites. In addition, the material is stable to ORR cycling and also considerably stable to OER cycling.

Na-doped ruthenium perovskite electrocatalysts with improved oxygen evolution activity and durability in acidic media.

The design of active and durable catalysts for the H2O/O2 interconversion is one of the major challenges of electrocatalysis for renewable energy. The oxygen evolution reaction (OER) is catalyzed by SrRuO3 with low potentials (ca. 1.35 VRHE), but the catalyst's durability is insufficient. Here we show that Na doping enhances both activity and durability in acid media. DFT reveals that whereas SrRuO3 binds reaction intermediates too strongly, Na doping of ~0.125 leads to nearly optimal OER activity. Na doping increases the oxidation state of Ru, thereby displacing positively O p-band and Ru d-band centers, weakening Ru-adsorbate bonds. The enhanced durability of Na-doped perovskites is concomitant with the stabilization of Ru centers with slightly higher oxidation states, higher dissolution potentials, lower surface energy and less distorted RuO6 octahedra. These results illustrate how high OER activity and durability can be simultaneously engineered by chemical doping of perovskites.

Chemical tunnel-splitting-engineering in a dysprosium-based molecular nanomagnet.

Total control over the electronic spin relaxation in molecular nanomagnets is the ultimate goal in the design of new molecules with evermore realizable applications in spin-based devices. For single-ion lanthanide systems, with strong spin-orbit coupling, the potential applications are linked to the energetic structure of the crystal field levels and quantum tunneling within the ground state. Structural engineering of the timescale of these tunneling events via appropriate design of crystal fields represents a fundamental challenge for the synthetic chemist, since tunnel splittings are expected to be suppressed by crystal field environments with sufficiently high-order symmetry. Here, we report the long missing study of the effect of a non-linear (C4) to pseudo-linear (D4d) change in crystal field symmetry in an otherwise chemically unaltered dysprosium complex. From a purely experimental study of crystal field levels and electronic spin dynamics at milliKelvin temperatures, we demonstrate the ensuing threefold reduction of the tunnel splitting.

Magnetostriction-polarization coupling in multiferroic Mn2MnWO6.

Double corundum-related polar magnets are promising materials for multiferroic and magnetoelectric applications in spintronics. However, their design and synthesis is a challenge, and magnetoelectric coupling has only been observed in Ni3TeO6 among the known double corundum compounds to date. Here we address the high-pressure synthesis of a new polar and antiferromagnetic corundum derivative Mn2MnWO6, which adopts the Ni3TeO6-type structure with low temperature first-order field-induced metamagnetic phase transitions (T N = 58 K) and high spontaneous polarization (~ 63.3 µC·cm-2). The magnetostriction-polarization coupling in Mn2MnWO6 is evidenced by second harmonic generation effect, and corroborated by magnetic-field-dependent pyroresponse behavior, which together with the magnetic-field-dependent polarization and dielectric measurements, qualitatively indicate magnetoelectric coupling. Piezoresponse force microscopy imaging and spectroscopy studies on Mn2MnWO6 show switchable polarization, which motivates further exploration on magnetoelectric effect in single crystal/thin film specimens.