RESUMO
Sterilization through γ-irradiation has been reported to affect collagen mechanical properties, but its possible effects on gelatin based materials have not been investigated up to now. Herein we report the results of a mechanical, chemical and thermal study performed on gelatin films before and after γ-irradiation. The investigation was performed on uncrosslinked films as well as on crosslinked films. To this aim, two common crosslinking agents, glutaraldehyde and genipin, at different concentration (0.15, 0.30 and 0.67%) were used. The results indicate that sterilization significantly affects the mechanical properties of uncrosslinked films, whereas it displays a modest effect on gelatin swelling, release in solution, thermal stability and molecular structure. Both glutaraldehyde and genipin enhance the mechanical properties and stability in solution of the gelatin films. In particular, the values of Young modulus increase as a function of crosslinker concentration up to about 10 and 18 MPa for genipin and glutaraldehyde treated samples respectively. The results of in vitro study demonstrate that the films crosslinked with genipin do not display any cytotoxic reaction, whereas glutaraldehyde crosslinking provokes an acute and dose dependent cytotoxic effect.
Assuntos
Reagentes de Ligações Cruzadas/química , Gelatina/química , Glutaral/química , Iridoides/química , Membranas Artificiais , Esterilização/métodos , Reagentes de Ligações Cruzadas/efeitos da radiação , Módulo de Elasticidade/efeitos da radiação , Raios gama , Gelatina/efeitos da radiação , Glutaral/efeitos da radiação , Iridoides/efeitos da radiação , Teste de Materiais , Doses de Radiação , Estresse Mecânico , Resistência à Tração/efeitos da radiaçãoRESUMO
Gelatin films are very versatile materials whose properties can be tuned through functionalization with different systems. This work investigates the influence of WO3 nanoparticles on the swelling, barrier, mechanical, and photochromic properties of gelatin films. To this purpose, polyvinylpirrolidone (PVP)-stabilized WO3 nanoparticles were loaded on gelatin films at two different pH values, namely, 4 and 7. The values of swelling and solubility of functionalized films displayed a reduction of around 50% in comparison to those of pristine, unloaded films. In agreement, WO3 nanoparticles provoked a significant decrease in water vapor permeability, whereas the decrease in the values of elastic modulus (from about 2.0 to 0.7 MPa) and stress at break (from about 2.5 to 1.4 MPa) can be ascribed to the discontinuity created by the nanoparticles inside the films. The results of differential scanning calorimetry and X-ray diffraction analysis suggest that interaction of PVP with gelatin reduce gelatin renaturation. No significant differences were found between the samples prepared at pH 4 and 7, whereas crosslinking with glutaraldehyde greatly influenced the properties of gelatin films. Moreover, the incorporation of WO3 nanoparticles in gelatin films, especially in the absence of glutaraldehyde, conferred excellent photochromic properties, inducing the appearance of an intense blue color after a few seconds of light irradiation and providing good resistance to several irradiation cycles.
RESUMO
This work investigated the range of substitution of two biologically relevant ions, namely Mn2+ and Co2+, into the structure of ß-tricalcium phosphate, as well as their influence on bone cells response. To this aim, ß-TCP was synthesized by solid state reaction in the presence of increasing amount of the substituent ions. The results of the X-ray diffraction analysis reveal that just limited amounts of these ions can enter into the ß-TCP structure: 15â¯at% and 20â¯at% for cobalt and manganese, respectively. Substitution provokes aggregation of the micrometric particles and reduction of the lattice constants. In particular, the dimension of the c-parameter exhibits a discontinuity at about 10â¯at% for both cations, although with different trend. Moreover, Rietveld refinement demonstrates a clear preference of both manganese and cobalt for the octahedral site (V). The influence of these ions on cell response was tested on osteoblast, osteoclast and endothelial cells. The results indicate that the presence of manganese promotes a good osteoblast viability, significantly enhances the expression of osteoblast key genes and the angiogenic process of endothelial cells, while inhibiting osteoclast resorption. At variance, osteoblast viability appears reduced in the presence of Co samples, on which osteoblast genes reach higher expression than on ß-TCP just in a few cases. On the other hand, the results clearly show that cobalt significantly stimulates the angiogenic process and inhibits osteoclast resorption.
RESUMO
In this paper the osteobiography of an elderly woman recovered from a cemetery tomb where she was buried in 1850, affected by hip fracture and osteoporosis, is described. The overall anthropological characteristics of the individual have been investigated. Macroscopic, radiographic, tomographic, microscopic, and chemical and structural examinations have been performed to give a detailed account of the condition of the skeleton. A non-union pertrochanteric fracture not surgically treated and probably due to senile osteoporosis was diagnosed. The consequences of the fracture to the bones show that this individual likely survived several years following the injury. The osseous features we describe (remodelled bone at the fracture site, asymmetry of entheseal changes likely related to the particular walking pattern of the individual) may be useful in personal identification of skeletons of legal interest. Regarding the recognition of osteoporosis in unearthed skeletons, our study underlines that the cortical thickness, microscopic features, degree of crystallinity and Ca/P ratio represent more useful elements than the mean bone density, mineral/matrix ratio and mineral maturity, which are more sensitive to diagenetic changes that affect the mineral phase post-mortem.
Assuntos
Antropologia Física/métodos , Fraturas do Quadril/diagnóstico , Osteoporose/diagnóstico , Acetábulo/diagnóstico por imagem , Acetábulo/lesões , Idoso de 80 Anos ou mais , Feminino , Fraturas do Quadril/história , História do Século XIX , Humanos , Comunicação Interdisciplinar , Osteoporose/história , RadiografiaRESUMO
Calcium phosphate-based coatings are widely studied in orthopedics and dentistry for their similarity to the mineral component of bone and their capability to promote osseointegration. Different calcium phosphates have tunable properties that result in different behaviors in vitro, but the majority of studies focus only on hydroxyapatite. Here, different calcium phosphate-based nanostructured coatings are obtained by ionized jet deposition, starting with hydroxyapatite, brushite and beta-tricalcium phosphate targets. The properties of the coatings obtained from different precursors are systematically compared by assessing their composition, morphology, physical and mechanical properties, dissolution, and in vitro behavior. In addition, for the first time, depositions at high temperature are investigated for the further tuning of the coatings mechanical properties and stability. Results show that different phosphates can be deposited with good composition fidelity even if not in a crystalline phase. All coatings are nanostructured and non-cytotoxic and display variable surface roughness and wettability. Upon heating, higher adhesion and hydrophilicity are obtained as well as higher stability, resulting in better cell viability. Interestingly, different phosphates show very different in vitro behavior, with brushite being the most suitable for promoting cell viability and beta-tricalcium phosphate having a higher impact on cell morphology at the early timepoints.
RESUMO
Reproducing in vitro a model of the bone microenvironment is a current need. Preclinical in vitro screening, drug discovery, as well as pathophysiology studies may benefit from in vitro three-dimensional (3D) bone models, which permit high-throughput screening, low costs, and high reproducibility, overcoming the limitations of the conventional two-dimensional cell cultures. In order to obtain these models, 3D bioprinting offers new perspectives by allowing a combination of advanced techniques and inks. In this context, we propose the use of hydroxyapatite nanoparticles, assimilated to the mineral component of bone, as a route to tune the printability and the characteristics of the scaffold and to guide cell behavior. To this aim, both stoichiometric and Sr-substituted hydroxyapatite nanocrystals are used, so as to obtain different particle shapes and solubility. Our findings show that the nanoparticles have the desired shape and composition and that they can be embedded in the inks without loss of cell viability. Both Sr-containing and stoichiometric hydroxyapatite crystals permit enhancing the printing fidelity of the scaffolds in a particle-dependent fashion and control the swelling behavior and ion release of the scaffolds. Once Saos-2 cells are encapsulated in the scaffolds, high cell viability is detected until late time points, with a good cellular distribution throughout the material. We also show that even minor modifications in the hydroxyapatite particle characteristics result in a significantly different behavior of the scaffolds. This indicates that the use of calcium phosphate nanocrystals and structural ion-substitution is a promising approach to tune the behavior of 3D bioprinted constructs.
RESUMO
Monetite and brushite are regarded with increasing interest for the preparation of biomaterials for applications in the musculoskeletal system. Herein, we investigated the influence of strontium substitution in the structures of these two phosphates on bone cell response. To achieve this aim, co-cultures of human primary osteoclasts and human osteoblast-like MG63 cells were tested on strontium-substituted monetite and strontium-substituted brushite, as well as on monetite and brushite, as controls. In both structures, strontium substitution for calcium amounted to about 6 at% and provoked enlargement of the cell parameters and morphologic variations. Cumulative release in physiological solution increased linearly over time and was greater from brushite (up to about 160 and 560 mg/L at 14 days for Sr and Ca, respectively) than from monetite (up to about 90 and 250 mg/L at 14 days for Sr and Ca, respectively). The increasing viability of osteoblast-like cells over time, with the different expression level of some typical bone markers, indicates a more pronounced trigger toward osteoblast differentiation and osteoclast inhibition by brushite materials. In particular, the inhibition of cathepsin K and tartrate-resistant acid phosphatase at the gene and morphological levels suggests strontium-substituted brushite can be applied in diseases characterized by excessive bone resorption.
RESUMO
The availability of biomaterials able to counteract bacterial colonization is one of the main requirements of functional implants and medical devices. Herein, we functionalized hydroxyapatite (HA) with tungsten oxide (WO3) nanoparticles in the aim to obtain composite materials with improved biological performance. To this purpose, we used HA, as well as HA functionalized with polyacrilic acid (HAPAA) or poly(ethylenimine) (HAPEI), as supports and polyvinylpyrrolidone (PVP) as stabilizing agent for WO3 nanoparticles. The number of nanoparticles loaded on the substrates was determined through Molecular Plasma-Atomic Emission Spectroscopy and is quite small, so it cannot be detected through X-ray diffraction analysis. It increases from HAPAA, to HA, to HAPEI, in agreement with the different values of zeta potential of the different substrates. HRTEM and STEM images show the dimensions of the nanoparticles are very small, less than 1 nm. In physiological solution HA support displays a greater tungsten cumulative release than HAPEI, despite its smaller loaded amount. Indeed, WO3 nanoparticles-functionalized HA exhibits a remarkable antibacterial activity against the Gram-positive Staphylococcus aureus in absence of cytotoxicity, which could be usefully exploited in the biomedical field.
RESUMO
In this paper we used curcumin as a functionalizing agent of gelatin films with the aim to get antioxidant materials with modulated physico-chemical properties. To this aim, we prepared gelatin films at different contents of curcumin up to about 1.2 wt%. The as-prepared films, as well as glutaraldehyde crosslinked films, were submitted to several tests: swelling, water solubility, differential scanning calorimetry, X-ray diffraction, mechanical tests and curcumin release. The radical scavenging activity of the as-prepared films is similar to that of free curcumin, indicating remarkable antioxidant properties. All the other tested properties vary as a function of curcumin content and/or the presence of the crosslinking agent. In particular, the films exhibit sustained curcumin release in different solvents. Thanks to its biocompatibility, biodegradability and lack of antigenicity, gelatin uses span from food processing to packaging and biomaterials. It follows that the modulated properties exhibited by the functionalized materials developed in this work can be usefully employed in different application fields.
RESUMO
Multi-functionalization of calcium phosphates to get delivery systems of therapeutic agents is gaining increasing relevance for the development of functional biomaterials aimed to solve problems related to disorders of the muscolo-skeletal system. In this regard, we functionalized Strontium substituted hydroxyapatite (SrHA) with some ß-lactam integrin agonists to develop materials with enhanced properties in promoting cell adhesion and activation of intracellular signaling as well as in counteracting abnormal bone resorption. For this purpose, we selected two monocyclic ß-lactams on the basis of their activities towards specific integrins on promoting cell adhesion and signalling. The amount of ß-lactams loaded on SrHA could be modulated on changing the polarity of the loading solution, from 3.5-24 wt% for compound 1 and from 3.2-8.4 wt% for compound 2. Studies on the release of the ß-lactams from the functionalized SrHA in aqueous medium showed an initial burst followed by a steady-release that ensures a small but constant amount of the compounds over time. The new composites were fully characterized. Co-culture of human primary mesenchymal stem cells (hMSC) and human primary osteoclast (OC) demonstrated that the presence of ß-lactams on SrHA favors hMSC adhesion and viability, as well as differentiation towards osteoblastic lineage. Moreover, the ß-lactams were found to enhance the inhibitory role of Strontium on osteoclast viability and differentiation.
Assuntos
Durapatita , beta-Lactamas , Regeneração Óssea , Adesão Celular , Diferenciação Celular , Humanos , Hidroxiapatitas , Integrinas , Estrôncio/farmacologiaRESUMO
A copper-based metal-organic framework (MOF) was prepared using a new linker, a 5-substituted isophthalic acid bearing a propargyl carbamate group, intended to provide a terminal alkyne function protruding from the material surface to generate supported gold species for potential catalytic applications. The novel material was fully characterized by spectroscopic analyses of different kinds: FTIR, Raman, EDX, and XPS, as well as by thermal and surface area measurements. Synchrotron X-ray diffraction data analysis, in particular, revealed that this MOF, labelled [Cu(1,3-YBDC)]·xH2O (x â¼ 2), where Y stands for the pendant alkYne and BDC for benzene dicarboxylate, contains a complex network of 5-substituted isophthalate anions bound to Cu(ii) centers, arranged in pairs within paddlewheel (or "Chinese lantern") fragments of Cu2(µ-COO)4(D)2 formulation (D being a neutral Lewis base), with a short Cuâ¯Cu distance of 2.633(4) Å. Quite unexpectedly, the apical atom in the paddlewheel structure belongs to the carbamate carbonyl oxygen atom. Such extra coordination by the propargyl carbamate groups drastically reduces the MOF porosity, a feature that was also confirmed by BET measurements. However, the MOF functionality is retained at the external crystal surface where 2% of active terminal alkynes is located.
RESUMO
Para-methyl benzyl alcohol (p-MeBA II) and para-chloro benzyl alcohol (p-ClBA) are quasi-isostructural and share the same hydrogen-bond patterns, but their crystals are not isomorphous. No new polymorphs could be obtained by conventional polymorph screening based on different solvents and different crystallization conditions. Formation of a new polymorph of p-MeBA named p-MeBA I, isomorphous with the crystal of p-ClBA, was induced by hetero-seeding with a small quantity of powdered p-ClBA added to a supersaturated solution of p-MeBA in hexane, while seeding of p-ClBA with p-MeBA II failed to give a new phase of p-ClBA isomorphous with known crystalline p-MeBA II. Mixed crystals of p-MeBA and p-ClBA were also prepared with different p-MeBA/p-ClBA ratios to understand the role of the different functional groups in the crystal structure. Crystal phases were characterized by combined use of single-crystal and powder X-ray diffraction, differential scanning calorimetry, and solid-state NMR spectroscopy.
RESUMO
Dicalcium phosphate dihydrate (DCPD) is one of the mineral phases indicated as possible precursors of biological apatites and it is widely employed in the preparation of calcium phosphate bone cements. Herein, we investigated the possibility to functionalize DCPD with aspartic acid (ASP) and poly-aspartic acid (PASP), as models of the acidic macromolecules of biomineralized tissues, and studied their influence on DCPD hydrolysis. To this aim, the synthesis of DCPD was performed in aqueous solution in the presence of increasing concentrations of PASP and ASP, whereas the hydrolysis reaction was carried out in physiological solution up to three days. The results indicate that it is possible to prepare DCPD functionalized with PASP up to a polyelectrolyte content of about 2.3 wt%. The increase of PASP content induces crystal aggregation, reduction of the yield of the reaction and of the thermal stability of the synthesized DCPD. Moreover, DCPD samples functionalized with PASP display a slower hydrolysis than pure DCPD. On the other hand, in the explored range of concentrations (up to 10 mM) ASP is not incorporated into DCPD and does not influence its crystallization nor its hydrolysis. At variance, when present in the hydrolysis solution, ASP, and even more PASP, delays the conversion into the more stable phases, octacalcium phosphate and/or hydroxyapatite. The greater influence of PASP on the synthesis and hydrolysis of DCPD can be ascribed to the cooperative action of the carboxylate groups and to its good fit with DCPD structure.
RESUMO
ß-tricalcium phosphate (ß-TCP) is one of the most common bioceramics, widely applied in bone cements and implants. Herein we synthesized ß-TCP by solid state reaction in the presence of increasing amounts of two biologically active ions, namely strontium and zinc, in order to clarify the structural modifications induced by ionic substitution. The results of X-ray diffraction analysis indicate that zinc can substitute for calcium into a ß-TCP structure up to about 10 at% inducing a reduction of the cell parameters, whereas the substitution occurs up to about 80 at% in the case of strontium, which provokes a linear increase of the lattice constants, and a slight modification into a more symmetric structure. Rietveld refinements and solid-state 31P NMR spectra demonstrate that the octahedral Ca(5) is the site of ß-TCP preferred by the small zinc ion. ATR-FTIR results indicate that zinc substitution provokes a disorder of ß-TCP structure. At variance with the behavior of zinc, strontium completely avoids Ca(5) site even at high concentration, whereas it exhibits a clear preference for Ca(4) site. The infrared absorption bands of ß-TCP show a general shift towards lower wavenumbers on increasing strontium content. Particularly significant is the shift of the infrared symmetric stretching band at 943 cm-1 due to P(1), that is the phosphate more involved in Ca(4) coordination, which further supports the occupancy preference of strontium.
RESUMO
Three crystal forms of the co-crystal 4,4'-bipy/pimelic acid (bipy: bipyridine), [NH(4)C(5)-C(5)H(4)N][HOOC(CH(2))(5)COOH], have been prepared and their relationship investigated by single-crystal X-ray diffraction, variable-temperature X-ray powder diffraction, differential scanning calorimetry and solid-state NMR spectroscopy. Both X-ray and NMR spectroscopic results indicate that no proton transfer takes place, that is, the three crystal forms are true co-crystals of neutral molecules. Forms I and II both convert into Form III at high temperature, Forms II and III being the thermodynamically stable forms at room and high temperature, respectively.
RESUMO
Functionalization of calcium phosphates for biomedical applications has been proposed as a strategy to enrich the good osteoinductive properties of these materials with specific therapeutic characteristics. Herein, we prepared and characterized hydroxyapatite nanocrystals functionalized with an anticancer agent, (9R)-9-hydroxystearate (HSA), and loaded with an antimicrobial agent, namely silver nanoparticles (AgNPs). Nanocrystals at two different contents of HSA, about 4 and 9 wt %, were prepared via direct synthesis in aqueous solution. Loading with the antibacterial agent was achieved through interaction with different volumes of AgNPs suspensions. The amount of loaded nanoparticles increases with the volume of the AgNPs suspension and with the hydroxystearate content of the nanocrystals, up to about 3.3 wt %. The structural, morphological, and hydrophobic properties of the composite materials depend on hydroxystearate content, whereas they are not affected by AgNPs loading. At variance, the values of zeta potential slightly increase with the content of AgNPs, which exhibit a sustained release in cell culture medium.
RESUMO
On heating the hydrated complexes 18-Crown[6].M[H(2)PO(4)].xH(2)O (x= 2 for M = K, Rb; x= 1.5 for M = Cs), quantitatively prepared by mechanical mixing of crystalline 18-Crown[6] and M[H(2)PO(4)], to ca. 60 degrees C, water loss takes place, accompanied by the extrusion of the crown ether from the crystalline complex and followed by reconstruction of the inorganic phase M[H(2)PO(4)](M = K, Rb, Cs); the resulting solid mixture reverts to 18-Crown[6].M[H(2)PO(4)].xH(2)O (x= 2 for M = K, Rb; x= 1.5 for M = Cs) upon grinding in air.
RESUMO
In spite of its remarkable anti-oxidant, anti-inflammatory, anti-cancer properties and its possible inhibition activity towards bone resorption, quercetin therapeutic use is limited by its poor bioavailability. Herein we developed a new multifunctionalized system for the local administration of quercetin and alendronate, one of the most potent anti-osteoporotic drugs, with the aim to get a material with enhanced properties. To this purpose we loaded quercetin on hydroxyapatite functionalized with alendronate, as well as on hydroxyapatite. Characterization was performed by means of X-ray diffraction, FT-IR and Raman spectroscopies, thermogravimetric and spectrophotometric analyses. Loading of quercetin from hydro-alcoholic solution increased with time and reached a constant value of about 5 weight% on both substrates, without causing significant structural and morphological modifications. Quercetin functionalized materials exhibit relevant anti-oxidant properties, in agreement with their high radical scavenging activity, and a quercetin sustained release in phosphate buffer. In vitro osteoblast and osteoclast co-culture in a microenvironment altered by oxidative stress shows that both alendronate and quercetin significantly reduce osteoclast viability, whereas they are able to counteract the negative effect of oxidative stress on osteoblast viability and differentiation, suggesting that their relative amount in the functionalized materials can be utilized to tailor bone cells response. © 2017 Wiley Periodicals, Inc. J Biomed Mater Res Part A: 105A: 3293-3303, 2017.
Assuntos
Alendronato/farmacologia , Antioxidantes/farmacologia , Conservadores da Densidade Óssea/farmacologia , Estresse Oxidativo/efeitos dos fármacos , Quercetina/farmacologia , Alendronato/administração & dosagem , Antioxidantes/administração & dosagem , Materiais Biocompatíveis/química , Conservadores da Densidade Óssea/administração & dosagem , Linhagem Celular , Técnicas de Cocultura , Sistemas de Liberação de Medicamentos/métodos , Durapatita/química , Humanos , Osteoblastos/citologia , Osteoblastos/efeitos dos fármacos , Osteoclastos/citologia , Osteoclastos/efeitos dos fármacos , Quercetina/administração & dosagem , Difração de Raios XRESUMO
The development of biomaterials able to act against a wide range of bacteria, including antibiotic resistant bacteria, is of great importance since bacterial colonization is one of the main causes of implant failure. In this work, we explored the possibility to functionalize hydroxyapatite (HA) nanocrystals with some monocyclic N-thio-substituted ß-lactams. To this aim, a series of non-polar azetidinones have been synthesized and characterized. The amount of azetidinones loaded on HA could be properly controlled on changing the polarity of the loading solution and it can reach values up to 17 wt%. Data on cumulative release in aqueous solution show different trends which can be related to the lipophilicity of the molecules and can be modulated by suitable groups on the azetidinone. The examined ß-lactams-HA composites display good antibacterial activity against reference Gram-positive and Gram-negative bacteria. However, the results of citotoxicity and antibacterial tests indicate that HA loaded with 4-acetoxy-1-(methylthio)-azetidin-2-one displays the best performance. In fact, this material strongly inhibited the bacterial growth of both methicillin resistant and methicillin susceptible clinical isolates of S. aureus from surgical bone biopsies, showing to be a very good candidate as a new functional biomaterial with enhanced antibacterial activity.
Assuntos
Antibacterianos/química , Antibacterianos/farmacologia , Materiais Biocompatíveis/química , Durapatita/química , Monobactamas/química , Monobactamas/farmacologia , Antibacterianos/síntese química , Azetidinas/química , Azetidinas/farmacologia , Bactérias/efeitos dos fármacos , Portadores de Fármacos , Liberação Controlada de Fármacos , Humanos , Testes de Sensibilidade Microbiana , Estrutura Molecular , Monobactamas/síntese química , Espectroscopia de Infravermelho com Transformada de FourierRESUMO
In this work we synthesized mesoporous bioactive glass nanospheres (nMBG) with the aim to utilize them as substrates for loading one of the most potent amino-bisphosphonates, alendronate (AL). The results of the chemical and structural characterization show that the nMBG display a relatively high surface area (528 m²/g) and a mean pore volume of 0.63 cm³/g, both of which decrease on increasing alendronate content. It is possible to modulate the amount of AL loaded into the nanospheres up to a maximum value of about 17 wt %. In vitro tests were performed using a human osteosarcoma cell line (MG63) and a murine monocyte/macrophage cell line as osteoclast model (RAW 264.7). The results indicate that even the lower concentration of alendronate provokes decreased tumor cell viability, and that osteoclast activity exhibits an alendronate dose-dependent inhibition. The data suggest that nMBG can act as a suitable support for the local delivery of alendronate, and that the antiresorptive and antitumor properties of the functionalized mesoporous nanospheres can be modulated by varying the amount of alendronate loading.