RESUMO
OBJECTIVES: The study aimed to assess the impact of diphenyliodonium hexafluorophosphate (DPI) on the physicochemical properties of experimental resin composites (ECRs) featuring reduced concentrations of camphorquinone (CQ)/amine. METHODS: Five concentrations of CQ (0.125, 0.25, 0.5, 0.75, and 1 mol%) with dimethylaminoethyl amine benzoate (EDAB) in a 1:2 mol% ratio (CQ:EDAB) were incorporated into a 50:50 mass% monomer blend of bisphenol glycidyl methacrylate (BisGMA) and triethyleneglycol dimethacrylate (TEGDMA). An additional 5 groups with the same CQ:EDAB concentrations had 0.5 mol% DPI added. Each resin group contained 60 wt% of 0.7 µm barium-alumino-silicate glass. Light transmission (n = 3), real-time degree of polymerization (n = 3), temperature change during polymerization (n = 5), polymerization shrinkage strain (n = 3), flexural strength, and modulus (n = 12), as well as water sorption and solubility (n = 5), were evaluated. Data were analyzed using two-way ANOVA and Tukey's post-hoc test (α = 0.05). RESULTS: Light transmission was reduced in groups containing 0.125 and 0.25 mol% of CQ without DPI. DPI increased temperature, degree and rate of polymerization, despite the reduction in CQ/amine concentration. Additionally, there was an increase in polymerization shrinkage strain, flexural strength and modulus, and a reduction in water sorption and solubility in ECRs with DPI, even with lower concentrations of CQ/EDAB. SIGNIFICANCE: DPI improved the assessed properties of composites across various concentrations of CQ/EDAB, showing the benefit of reducing the quantity of CQ used without compromising the properties and curing of the resin composites.
Assuntos
Resinas Compostas , Teste de Materiais , Polietilenoglicóis , Polimerização , Ácidos Polimetacrílicos , Terpenos , Resinas Compostas/química , Terpenos/química , Polietilenoglicóis/química , Ácidos Polimetacrílicos/química , Bis-Fenol A-Glicidil Metacrilato/química , Propriedades de Superfície , Oniocompostos/química , Poliuretanos/química , Resinas Acrílicas , Compostos de Bifenilo , Cânfora/análogos & derivadosRESUMO
OBJECTIVES: To analyze the influence of different concentrations of 10-MDP and GPDM used, combined or not, on the bonding to zirconia. METHODS: Specimens of zirconia and a resin-composite (7 mm length, 1 mm width, and 1 mm thick) were obtained. The experimental groups were obtained according to the functional monomer (10-MDP and GPDM) and the concentrations (3 %, 5 %, and 8 %). For the groups with combined 10-MDP and GPDM, the agents were used with a proportion of 50 %/50 % wt until reaching the 3 %, 5 % and 8 % concentrations. All monomers were diluted in ethanol to obtain the primers. Two control groups were established: ethanol (negative control) and a commercial reference Monobond N (positive control). The zirconia surface treatment was performed with the primer application followed by the bonding to a resin-composite sample with a light-curing resin cement. Twenty-four hours after the adhesive procedure, a microtensile test was performed and the failure pattern of each sample was analysed with a stereoscopic magnifying glass. Data were analysed by a two-way ANOVA and Dunnet test. RESULTS: All experimental primers presented a higher bond strength than the negative control (ethanol). Excepting the 8 % GPDM primer, all groups presented statistically similar bond strength compared to the positive control, with a predominance of adhesive failure. SIGNIFICANCE: 10-MDP, GPDM, and the combination of both for the concentrations tested promote an effective chemical bonding to zirconia. However, using 10-MDP and GPDM in the same primer has no synergistic effect.
Assuntos
Colagem Dentária , Cimentos Dentários , Cimentos Dentários/química , Colagem Dentária/métodos , Cimentos de Resina/química , Zircônio/química , Metacrilatos/química , Resinas Compostas , Teste de Materiais , Propriedades de Superfície , Resistência ao Cisalhamento , Análise do Estresse DentárioRESUMO
To evaluate the effects of Type I and Type II photoinitiator systems on curing efficiency, degree of conversion (DC) and chemico-physical properties of resin based materials. A comonomer base containing 50%wt 2.2-bis[4-(2-hydroxy-3-methacryloxypropoxy)phenyl]propane (bis-GMA) and 50%wt triethyleneglycol dimethacrylate (TEGDMA) was formulated with either 0.5 or 1mol% of Type II camphoroquinone (CQ), Type I monoacylphosphine oxide (MAPO) or bis-acylphosphine oxide (BAPO) photoinitiators. The Type II system was either a binary (1: 2 CQ:amine) or ternary system (1: 2 CQ:amine + 0.5 mol% DPI). Degree and rate of polymerization was measured by Fourier Transform Infrared Spectroscopy (FTIR). Knoop micro-hardness prior to and following ethanol immersion was assessed. Flexural strength and modulus was measured under three-point bend test. Water sorption and solubility was also evaluated. The photoinitiator absorption spectra and the total absorbed energy per unit volume (Eabs) for 0.5mol% photoinitiator in each material was calculated. Despite the reduced total absorbed energy per unit volume for CQ based systems, ternary Type II system significantly improved curing efficiency (Pâ¯<â¯0.05) compared to both Type I photoinitiators and degree of conversion compared to MAPO only, whilst exhibiting comparable mechanical and physical properties compared to both Type I based materials at equivalent molar concentrations of photoinitiator (Pâ¯>â¯0.05). Ternary Type II systems is an efficient alternative to improve the polymerization of resin materials, promoting similar or even better properties than Type I initiators. DPI can increase the reactivity of CQ systems and promote polymerization rates superior than Type I photoinitiators.