Self-consolidation mechanism of nanostructured Ti5Si3 compact induced by electrical discharge.

Electrical discharge using a capacitance of 450 µF at 7.0 and 8.0 kJ input energies was applied to mechanical alloyed Ti5Si3 powder without applying any external pressure. A solid bulk of nanostructured Ti5Si3 with no compositional deviation was obtained in times as short as 159 µsec by the discharge. During an electrical discharge, the heat generated is the required parameter possibly to melt the Ti5Si3 particles and the pinch force can pressurize the melted powder without allowing the formation of pores. Followed rapid cooling preserved the nanostructure of consolidated Ti5Si3 compact. Three stepped processes during an electrical discharge for the formation of nanostructured Ti5Si3 compact are proposed: (a) a physical breakdown of the surface oxide of Ti5Si3 powder particles, (b) melting and condensation of Ti5Si3 powder by the heat and pinch pressure, respectively, and (c) rapid cooling for the preservation of nanostructure. Complete conversion yielding a single phase Ti5Si3 is primarily dominated by the solid-liquid mechanism.

Tuning microcavities in thermally rearranged polymer membranes for CO2 capture.

Microporous materials have a great importance in catalysis, delivery, storage and separation in terms of their performance and efficiency. Most microporous materials are comprised of inorganic frameworks, while thermally rearranged (TR) polymers are a microporous organic polymer which is tuned to optimize the cavity sizes and distribution for difficult separation applications. The sub-nano sized microcavities are controlled by in situ thermal treatment conditions which have been investigated by positron annihilation lifetime spectroscopy (PALS). The size and relative number of cavities increased from room temperature to 230 °C resulting in improvements in both permeabilities and selectivities for H(2)/CO(2) separation due to the significant increase of gas diffusion and decrease of CO(2) solubility. The highest performance of the well-tuned TR-polymer membrane was 206 Barrer for H(2) permeability and 6.2 of H(2)/CO(2) selectivity, exceeding the polymeric upper bound for gas separation membranes.

Microporous Ti implant compact coated with hydroxyapatite produced by electro-discharge-sintering and electrostatic-spray-deposition.

A single pulse of 1.5 kJ/0.7 g of atomized spherical Ti powder from 300 µF capacitor was applied to produce the porous-surfaced Ti implant compact by electro-discharge-sintering (EDS). A solid core surrounded by porous layer was self-consolidated by a discharge in the middle of the compact in 122 µsec. Average pore size, porosity, and compressive yield strength of EDS Ti compact were estimated to be about 68.2 µm, 25.5%, and 266.4 MPa, respectively. Coatings with hydroxyapatite (HAp) on the Ti compact were conducted by electrostatic-spray-deposition (ESD) method. As-deposited HAp coating was in the form of porous structure and consisted of HAp particles which were uniformly distributed on the Ti porous structure. By heat-treatment at 700 degrees C, HAp particles were agglomerated each other and melted to form a highly smooth and homogeneous HAp thin film consisted of equiaxed nano-scaled grains. Porous-surfaced Ti implant compacts coated with highly crystalline apatite phase were successfully obtained by using the EDS and ESD techniques.