RESUMO
Smart wearable electronic accessories (e.g., watches) have found wide adoption; conversely, progress in electronic textiles has been slow due to the difficulty of embedding rigid electronic materials into flexible fabrics. Electronic clothing requires fibers that are conductive, robust, biocompatible, and can be produced on a large scale. Here, we create sewable electrodes and signal transmission wires from neat carbon nanotube threads (CNTT). These threads are soft like standard sewing thread, but they have metal-level conductivity and low interfacial impedance with skin. Electrocardiograms (EKGs) obtained by CNTT electrodes were comparable (P > 0.05) to signals obtained with commercial electrodes. CNTT can also be used as transmission wires to carry signals to other parts of a garment. Finally, the textiles can be machine-washed and stretched repeatedly without signal degradation. These results demonstrate promise for textile sensors and electronic fabric with the feel of standard clothing that can be incorporated with traditional clothing manufacturing techniques.
Assuntos
Dispositivos Eletrônicos Vestíveis , Vestuário , Eletrodos , Eletrônica , TêxteisRESUMO
Active fibers with electro-optic functionalities are promising building blocks for the emerging and rapidly growing field of fiber and textile electronics. Yet, there remains significant challenges that require improved understanding of the principles of active fiber assembly to enable the development of fiber-shaped devices characterized by having a small diameter, being lightweight, and having high mechanical strength. To this end, the current frameworks are insufficient, and new designs and fabrication approaches are essential to accommodate this unconventional form factor. Here, we present a first demonstration of a pathway that effectively integrates the foundational components meeting such requirements, with the use of a flexible and robust conductive core carbon nanotube fiber and an organic-inorganic emissive composite layer as the two critical elements. We introduce an active fiber design that can be realized through an all solution-processed approach. We have implemented this technique to demonstrate a three-layered light-emitting fiber with a coaxially coated design.
RESUMO
A monofilament fiber spun from individual carbon nanotubes is an arbitrarily long ensemble of weakly interacting, aligned, discrete nanoparticles. Despite the structural resemblance of carbon nanotube monofilament fibers to crystalline polymeric fibers, very little is known about their dynamic collective mechanics, which arise from van der Waals interactions among the individual carbon nanotubes. Using ultrafast stroboscopic microscopy, we study the collective dynamics of carbon nanotube fibers and compare them directly with nylon, Kevlar, and aluminum monofilament fibers under the same supersonic impact conditions. The in situ dynamics and kinetic parameters of the fibers show that the kinetic energy absorption characteristics of the carbon nanotube fibers surpass all other fibers. This study provides insight into the strain-rate-dependent strengthening mechanics of an ensemble of nanomaterials for the development of high-performance fibers used in body armor and other protective nanomaterials possessing exceptional stability in various harsh environments.
RESUMO
Carbon nanotube (CNT) fibers are a promising material for wearable electronics and biomedical applications due to their combined flexibility and electrical conductivity. To engineer the bending properties for such applications requires understanding how the bending stiffness of CNT fibers scales with CNT length and fiber diameter. We measure bending stiffness with a cantilever setup interpreted within Euler Elastica theory. We find that the bending stiffness scales with a power law of 1.9 for the fiber diameter and 1.6 for the CNT length. The diameter scaling exponent for fiber diameter agrees with results from earlier experiments and theory for microscopic CNT bundles. We develop a simple model which predicts the experimentally observed scaling exponents within statistical significance.
RESUMO
The synthesis of colloidal nanocrystals (NCs) of lithiated groupâ 14 elements (Z=Si, Ge, and Sn) is reported, which are Li4.4 Si, Li3.75 Si, Li4.4 Ge, and Li4.4 Sn. Lix Z compounds are highly reactive and cannot be synthesized by existing methods. The success relied on separating the surface protection from the crystal formation and using a unique passivating ligand. Bare Lix Z crystals were first produced by milling elemental Li and Z in an argon-filled jar. Then, under the assistance of additional milling, hexyllithium was added to passivate the freshly generated Lix Z NCs. This ball-milling-assisted surface protection method may be generalized to similar systems, such as Nax Z and Kx Z. Moreover, Li4.4 Si and Li4.4 Ge NCs were conformally encapsulated in carbon fibers, providing great opportunities for studying the potential of using Lix Z to mitigate the volume-fluctuation-induced poor cyclability problem confronted by Zâ anodes in lithium-ion batteries.
RESUMO
Chlorosulfonic acid and oleum are ideal solvents for enabling the transformation of disordered carbon nanotubes (CNTs) into precise and highly functional morphologies. Currently, processing these solvents using extrusion techniques presents complications due to chemical compatibility, which constrain equipment and substrate material options. Here, we present a novel acid solvent system based on methanesulfonic or p-toluenesulfonic acids with low corrosivity, which form true solutions of CNTs at concentrations as high as 10 g/liter (≈0.7 volume %). The versatility of this solvent system is demonstrated by drop-in application to conventional manufacturing processes such as slot die coating, solution spinning continuous fibers, and 3D printing aerogels. Through continuous slot coating, we achieve state-of-the-art optoelectronic performance (83.6 %T and 14 ohm/sq) at industrially relevant production speeds. This work establishes practical and efficient means for scalable processing of CNT into advanced materials with properties suitable for a wide range of applications.
RESUMO
Covalent modification of the surface of carbon nanotube fibres (CNTFs) through electrochemical reduction of para-substituted phenyldiazonium salts and electrochemical oxidation of an aliphatic diamine is described. Following these strategies, diverse surface functionalities have been introduced while preserving the fibre bulk properties. The corresponding modified CNTFs were fully characterised by Raman spectroscopy, X-ray photoelectron spectroscopy, energy dispersive X-Ray, scanning electron microscopy and electrochemical impedance spectroscopy, exhibiting different surface properties from those of the unmodified CNTFs.
RESUMO
Theoretical considerations suggest that the strength of carbon nanotube (CNT) fibers be exceptional; however, their mechanical performance values are much lower than the theoretical values. To achieve macroscopic fibers with ultrahigh performance, we developed a method to form multidimensional nanostructures by coalescence of individual nanotubes. The highly aligned wet-spun fibers of single- or double-walled nanotube bundles were graphitized to induce nanotube collapse and multi-inner walled structures. These advanced nanostructures formed a network of interconnected, close-packed graphitic domains. Their near-perfect alignment and high longitudinal crystallinity that increased the shear strength between CNTs while retaining notable flexibility. The resulting fibers have an exceptional combination of high tensile strength (6.57 GPa), modulus (629 GPa), thermal conductivity (482 W/m·K), and electrical conductivity (2.2 MS/m), thereby overcoming the limits associated with conventional synthetic fibers.
RESUMO
Low-dimensional materials have recently attracted much interest as thermoelectric materials because of their charge carrier confinement leading to thermoelectric performance enhancement. Carbon nanotubes are promising candidates because of their one-dimensionality in addition to their unique advantages such as flexibility and light weight. However, preserving the large power factor of individual carbon nanotubes in macroscopic assemblies has been challenging, primarily due to poor sample morphology and a lack of proper Fermi energy tuning. Here, we report an ultrahigh value of power factor (14 ± 5 mW m-1 K-2) for macroscopic weavable fibers of aligned carbon nanotubes with ultrahigh electrical and thermal conductivity. The observed giant power factor originates from the ultrahigh electrical conductivity achieved through excellent sample morphology, combined with an enhanced Seebeck coefficient through Fermi energy tuning. We fabricate a textile thermoelectric generator based on these carbon nanotube fibers, which demonstrates high thermoelectric performance, weavability, and scalability. The giant power factor we observe make these fibers strong candidates for the emerging field of thermoelectric active cooling, which requires a large thermoelectric power factor and a large thermal conductivity at the same time.