Color change of composite resins subjected to accelerated artificial aging.

AIM: The aim of this study was to evaluate the influence of accelerated artificial aging (AAA) on the color change of composite resins used in dentistry. MATERIALS AND METHODS: Three composite resins were evaluated: Two microhybrids and one hybrid of higher viscosity, with different amounts and sizes of filler particles, shades C2 and B2. A total of 54 specimens were obtained (18 for each composite resin), made of a Teflon matrix (15 mm in diameter and 2 mm in height). The color measurements were obtained with a Spectrophotometer, (PCB 6807 BYK Gardner) before and after AAA. Data were submitted to the Kolmogorov-Smirnov test (α >0.05), ANOVA and Tukey test (α <0.05). After statistical analysis, the color difference among composite resins with the same shades was analyzed. RESULTS: All composite resins showed unacceptable color changes after AAA (ΔE > 3). Considering the variable ∆E, it was observed that the color tone C2 was already statistically different for the microhybrid composite resin prior to AAA (P < 0.05) and in shade B2 for hybrid of higher viscosity and microhybrid with barium glass fluoride aluminum and silica dioxide (P < 0.01). After this process, a statistically significant difference was observed only for shade B2 between microhybrid composite resins (P < 0.01) and for hybrid of higher viscosity and microhybrid with barium glass fluoride aluminum and silica dioxide (P < 0.05). Regarding the color difference within a same composite resin group, before aging the composite resin hybrid of higher viscosity B2 showed the highest color variation rate and microhybrid with zirconium/silica C2 showed the lowest. CONCLUSIONS: All composite resins presented unacceptable color changes after 382 h of aging and different composite resins with same hue, presented different colors before being subjected to the aging process (B2 and C2) and after (B2). It was also observed color difference within a group of the same composite resin and same hue.

Conhecimento de profissionais de Odontologia sobre violência doméstica / Knowledge of dentistry's professionals on domestic violence

Introdução e objetivo: Avaliar o conhecimento de cirurgiões-dentistas graduados entre os anos 1998 e 2009 pela Faculdade de Odontologia de Ribeirão Preto da Universidade de São Paulo (Forp-USP) ante o tema violência doméstica contra crianças, mulheres e idosos. Material e métodos: Foram aplicados questionários objetivos a 180 sujeitos da pesquisa com posterior análise estatística dos dados. Resultados: A maioria dos entrevistados nunca atendeu algum paciente vítima de violência doméstica ou suspeitou de alguém e não se sente apta a fazer diagnóstico de maus-tratos. Em contrapartida, 45% denunciariam maus-tratos contra criança às autoridades competentes e nos casos de violência contra mulher e idoso, nesta ordem, 69% e 40% conversariam com a vítima. Os desvios entre as respostas obtidas nos diferentes anos de conclusão do curso não foram estatisticamente significantes. Conclusão: Apesar dos avanços observados nessa área do ensino de graduação, o cirurgião-dentista ainda necessita desenvolver competências e habilidades no que se refere ao tema violência doméstica, tanto no diagnóstico quanto nas condutas a serem seguidas.

Introduction and objective: To evaluate the knowledge of dentists graduated from the School of Dentistry of RibeirÒo Preto, University of SÒo Paulo (FORP-USP) between 1998 and 2009 about domestic violence against children, women and elderly. Material and methods: A questionnaire with multiple-choice questions was applied to 180 subjects and the collected data were subjected to statistical analysis. Results: The majority of respondents never treated or suspected that a patient had been a victim of domestic violence, and affirmed not being able to identify cases of physical abuse. Forty-five percent, however, would report child abuse to the legal authorities; in cases of violence against women and elderly people, 69% and 40%, respectively, would talk to the victim. The differences between the responses obtained at the different senior years were not statistically significant. Conclusion: Despite the advances made in this area of undergraduate education, the dentist still needs to develop competencies and skills for dealing with domestic violence regarding its identification and approaches to be followed.

Avaliação da resistência à fratura de resinas compostas submetidas ao envelhecimento artificial acelerado / Evaluation of composite resin fracture strength submitted to the artificial aging

Objetivo: O objetivo deste trabalho foi avaliar a influência do envelhecimento artificial acelerado na resistência à compressão de resinas compostas. Metodologia: Foram avaliadas cinco marcas comerciais de resinas compostas: Z250®, 4Seasons®, P60®, Z100® e Charisma®. Para cada resina foram obtidos 16 corpos de prova, divididos em dois grupos de oito, sendo um grupo submetido ao sistema envelhecimento acelerado para não metálicos CUV e o outro, à análise de resistência à compressão 24 horas após sua obtenção. Posteriormente, os corpos de prova envelhecidos foram submetidos ao ensaio de compressão. As médias das leituras de resistência à compressão de cada corpo de prova foram submetidas ao teste Kolmogorov-Smirnov (p > 0,05), Anova e teste de Tukey (p < 0,05). Resultados: A análise dos fatores apresentou diferenças significantes entre as marcas de resina composta quanto à resistência à compressão (F = 40,31, p < 0,0001). Com relação ao mesmo material antes e depois do envelhecimento, nota-se que esse processo não influenciou na resistência a compressão de nenhuma das resinas compostas (F = 2,82, p = 0,09). Nota-se que houve interação entre os fatores marca da resina composta e envelhecimento (F = 3,20, p < 0,004). Conclusão: Independentemente do tipo de resina, o envelhecimento artificial acelerado não influenciou na resistência à compressão. No entanto, houve diferença significante entre as marcas de resina quanto a essa propriedade.