Revealing the Effect of Anion Regulation in NiCo2X4 (X = O, S, Se, Te) on Photoassisted Methanol Electrocatalytic Oxidation.

Designing nonprecious metal anode catalysts for photoassisted direct methanol fuel cells (PDMFCs) remains a challenge. As a semiconductor catalyst with a spinel structure, NiCo2O4 has good methanol catalytic oxidation activity and photocatalytic activity, making it a highly promising anode non-noble metal catalyst for PDMFCs. However, compared with the noble metal catalyst, the photoelectrocatalytic activity remained to be improved. In this report, an anion regulation strategy was adopted to improve the photoassisted methanol electrocatalytic activity. Using a CoNi-Aspartic (CoNi-Asp) nanorod as the precursor, the anion-regulated NiCo2X4 (X = O, S, Se, Te) was prepared by oxidation, sulfuration, selenization, and telluridation reactions. The regulation of anions and their effects on the electronic structure, intermediate product, and photoelectric catalytic performance of NiCo2X4 (X= O, S, Se, Te) was systematically discussed. Photoelectrochemical characterization and adsorption energy of •OH revealing the volcano-like correlation between the anion in NiCo2X4 (X = O, S, Se, Te) and their photoelectrocatalytic performance. The narrowest band gap (2.239 eV), the highest •OH adsorption energy (-3.32 eV), and the highest ratio of Co3+/Co2+ (2.19) ensure the best photoelectric catalytic performance of NiCo2S4, under the visible light irradiation, the photoresponse current density was 1.9 A g-1, the current density at 0.6 V was up to 21.9 A g-1. After 9 h of stability testing, the current retention rate was 80%. This report sheds an idea for the rational design of non-noble anode catalysts for PDMFCs.

Boosting the Capacitor Performance of the Metal Organic Frameworks Derived V2O5 Nanoflower by Cu Doping.

Due to its ultrahigh theoretical capacitance, vanadium pentoxide (V2O5) is considered to be a valid candidate for advanced supercapacitors. However, because of the low electron/electrolyte transfer rate, the capacitive performance still remains to be improved. In this report, Cu doping is adopted to improve the capacitive performance by a two-steps strategy consisting of microwave-assisted solvothermal and postannealing treatments. The electrochemical results indicate that the Cu doping was beneficial for improving the specific capacitance, extending the potential window, and improving the rate ability and long-term stability of V2O5. Furthermore, the mechanism for the performance improvement is explained in detail by combining theoretical calculation and experiments. The results indicated that, compared with that of undoped V2O5, the larger interplanar spacing, better electrical conductivity, a larger proportion of V3+/V4+, and more abundant oxygen vacancies result in an improved capacitive performance. Our proposed Cu-doped V2O5 (Cu-V2O5) can be used as both a positive electrode and a negative electrode for the assembly of the symmetric supercapacitor, which can be used as an energy storage device for light emitting diode lamps.