RESUMO
For inorganic luminescent materials with activators, the energy yield is usually observed to decrease with an increase in activator concentration, which is known as the concentration quenching effect. To inhibit this phenomenon, a common strategy is to increase the distance between activators. Most previous reports have focused on the three-dimensional crystal lattice, and there have been few reports about two-dimensional layered structure. Herein, we synthesized a novel Cr3+-activated near-infrared (NIR) phosphor Li2Sr2Al(PO4)3 (LSAPO) with layered structure, and in such a two-dimensional structure, we proved experimentally that the concentration quenching was suppressed. Under 460 nm excitation, LSAPO:Cr3+ gave a broad NIR emission band (700-1200 nm) centered at 823 nm with a full width at half-maximum (fwhm) of 178 nm and a broad absorption band, indicating its potential application in NIR spectroscopy. Moreover, by codoping Cr3+ and Yb3+ ions, we further widened the emission bandwidth to â¼230 nm of fwhm, the internal quantum efficiency increased from 54% to 61%, and the thermal stability was improved. The fabricated NIR device with a LSAPO:Cr3+,Yb3+ phosphor coupled with blue chips can be applied in night-vision technologies and medical fields.
RESUMO
There is strong demand for ultraefficient near-infrared (NIR) phosphors with adjustable emission properties for next-generation intelligent NIR light sources. Designing phosphors with large full-width at half-maximum (FWHM) variations is challenging. In this study, novel near-ultraviolet light-emitting diode (LED)-excited NIR phosphors, MgAlGa0.7 B0.3 O4 :Cr3+ (MAGBO:Cr3+ ), with three emission centers achieve ultra-narrowband (FWHM = 29 nm) to ultra-broadband (FWHM = 260 nm) emission with increasing Cr3+ concentration. Gaussian fitting and decay time analysis reveal the alteration in the FWHM, which is attributed to the energy transfer occurring between the three emission centers. The distinct thermal quenching behaviors of the three emission centers are revealed through the temperature-dependent decay times. The ultra-broadband NIR phosphor MAGBO:0.05Cr3+ exhibits high thermal stability (85%, 425 K) and exceptional external quantum efficiency of 68.5%. An NIR phosphor-converted LED (pc-LED) is fabricated using MAGBO:0.05Cr3+ phosphor, exhibiting a remarkable NIR output power of 136 mW at 600 mA in ultra-broadband NIR pc-LEDs. This study describes the preparation of highly efficient phosphors and provides a further understanding of the tunable FWHM, which is vital for high-performance NIR phosphors with versatile applications.
RESUMO
A highly efficient phosphor with exceptional luminescence properties is crucial for achieving high-quality solid-state white-light illumination. Here, this paper presents a groundbreaking discovery, an innovative blue-violet emitting Ba1.31Sr3.69(BO3)3Cl:Ce3+ (BSBCl:Ce3+) phosphor designed with remarkable thermal stability and quantum efficiency for full spectrum white light-emitting diodes (WLEDs). By employing a high-temperature solid-phase method, we synthesized various BSBCl:xCe3+ phosphors with different Ce3+ doping concentrations. Remarkably, BSBCl:0.03Ce3+ displays a broad excitation band from 250 nm to 400 nm, rendering it compatible with commercial near-ultraviolet (UV) LED chips. Under 330 nm excitation, this phosphor emits blue light with an astonishing 88.2% internal quantum efficiency (IQE) and an impressive 60.9% external quantum efficiency (EQE). Notably, when employed in the temperature range of 298-473 K, the synthesized BSBCl:0.03Ce3+ phosphor exhibits exceptional color stability and thermal stability (I423 K/I298 K = 83%). Utilizing BSBCl:0.03Ce3+ as the blue-violet emitting component in the fabrication of WLED devices has demonstrated significant advancements in the color rendering index. These findings underscore the potential of BSBCl:Ce3+ phosphors for a wide range of applications in health-oriented indoor illumination.