Investigating the mechanism of Zn cross-linking of chitin in a mycelium-based leather substitute and its performance evaluation.

Mycelium-based leather substitutes with a three-dimensional reticulated structure have attracted attention owing to the negative environmental impacts of natural and synthetic leather. This study utilised Ganoderma lucidum mycelium to prepare a mycelium-based leather substitute with zinc cross-linking (MF-Zn) and evaluated its physicochemical properties and sensory performance; the conventional Cr3+ tanning method was used as reference. Results demonstrated that Zn2+ and Cr3+ formed cross-links with the -OH and -NHOCH3 groups in the polysaccharides of chitin, while Zn2+ selectively bonded to a fraction of -NH2 groups in cystine and phenylalanine. The mycelium-based leather substitute with Zn cross-linking exhibited impressive tensile strength and tear strength of 7.0 MPa and 16.4 kN/m, respectively, while demonstrating desirable organoleptic properties. The free radical-scavenging capacity of MF-Zn was assessed, revealing a DPPH radical and hydroxyl radical scavenging rates of 39.4% and 52.7%, respectively. By successfully investigating the cross-linking mechanism of mycelial fibres with Zn2+ and obtaining the stabilised mycelium-based leather substitute, this study establishes a fundamental basis for the development of sustainable leather substitutes, meeting the requirements and facilitating significant advancements in low-carbon leather substitute production.

Mechanically Tough and Conductive Hydrogels Based on Gelatin and Z-Gln-Gly Generated by Microbial Transglutaminase.

Gelatin-based hydrogels with excellent mechanical properties and conductivities are desirable, but their fabrication is challenging. In this work, an innovative approach for the preparation of gelatin-based conductive hydrogels is presented that improves the mechanical and conductive properties of hydrogels by integrating Z-Gln-Gly into gelatin polymers via enzymatic crosslinking. In these hydrogels (Gel-TG-ZQG), dynamic π-π stacking interactions are created by the introduction of carbobenzoxy groups, which can increase the elasticity and toughness of the hydrogel and improve the conductivity sensitivity by forming effective electronic pathways. Moreover, the mechanical properties and conductivity of the obtained hydrogel can be controlled by tuning the molar ratio of Z-Gln-Gly to the primary amino groups in gelatin. The hydrogel with the optimal mechanical properties (Gel-TG-ZQG (0.25)) exhibits a high storage modulus, compressive strength, tensile strength, and elongation at break of 7.8 MPa at 10 °C, 0.15 MPa at 80% strain, 0.343 MPa, and 218.30%, respectively. The obtained Gel-TG-ZQG (0.25) strain sensor exhibits a short response/recovery time (260.37 ms/130.02 ms) and high sensitivity (0.138 kPa-1) in small pressure ranges (0-2.3 kPa). The Gel-TG-ZQG (0.25) hydrogel-based sensors can detect full-range human activities, such as swallowing, fist clenching, knee bending and finger pressing, with high sensitivity and stability, yielding highly reproducible and repeatable sensor responses. Additionally, the Gel-TG-ZQG hydrogels are noncytotoxic. All the results demonstrate that the Gel-TG-ZQG hydrogel has potential as a biosensor for wearable devices and health-monitoring systems.

Magnetic multi-template molecularly imprinted polymers for selective simultaneous extraction of chlorophenols followed by determination using HPLC.

Magnetic multi-template molecularly imprinted polymers (M-mt-MIPs) were successfully synthesized by surface imprinting and multi-template imprinting strategy, using polydopamine coated magnetic multi-walled carbon nanotubes as supporting materials, five typical chlorophenols (CPs) as templates, methacrylic acid as functional monomer and ethylene glycol dimethacrylate as cross-linker. Compared to non-imprinted polymers (NIPs), the as-prepared M-mt-MIPs showed high adsorption capacity (32.58‒80.63 mg g-1), rapid mass transfer and specific selectivity for the five targeted CPs, which were applied as magnetic solid-phase extraction (MSPE) adsorbents. Parameters affecting MSPE efficiency were detailed investigated, such as adsorbents dosage, sample pH, extraction time, type and volume of desorption solvent and salt effect. Combined with HPLC-DAD, a simple, rapid and sensitive method was established, showing good linearity (2‒200 µg L-1), low limits of detection (0.32‒0.49 µg L-1), and high enrichment factors (35.2‒108). The developed M-mt-MIPs-MSPE-HPLC method was applied to enrich and determine CPs in tannery wastewater, wet-blue and crust leather, and satisfactory spiking recoveries were attained in the range of 73.95‒109.7% with relative standard deviations (RSDs) of 2.13-8.48%. This study provided a new alternative material and method to rapid simultaneously extract and analyze low concentration of typical CPs in complicated matrices.